CN102352157A - 一种耐化学品的塑胶涂料及其使用方法和应用 - Google Patents
一种耐化学品的塑胶涂料及其使用方法和应用 Download PDFInfo
- Publication number
- CN102352157A CN102352157A CN2011102734896A CN201110273489A CN102352157A CN 102352157 A CN102352157 A CN 102352157A CN 2011102734896 A CN2011102734896 A CN 2011102734896A CN 201110273489 A CN201110273489 A CN 201110273489A CN 102352157 A CN102352157 A CN 102352157A
- Authority
- CN
- China
- Prior art keywords
- plastic coating
- chemicals
- resistant plastic
- percent
- coating according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种耐化学品塑胶涂料及其使用方法和应用,所述耐化学品塑胶涂料,按重量百分比计,主要由以下组分组成:热塑性丙烯酸树脂10-30%,改性丙烯酸树脂35-65%,三元氯醋树脂0-10%,有机溶剂8-20%,附着促进剂1-3%,流平剂0.1-0.5%,手感剂1-5%。所述耐化学品塑胶涂料,是一种单组份塑胶涂料,面漆静电喷涂效果好,表面平滑,颜色均匀。干燥后的漆膜耐化学品优异,同时兼顾耐乙醇擦拭。
Description
技术领域
本发明涉及塑胶涂料领域,尤其涉及一种耐化学品塑胶涂料及其使用方法和应用,所述耐化学品塑胶涂料特别适用于静电喷涂。
背景技术
目前,塑胶制品由于导电性差,在静电喷涂中需要在整个塑胶表面涂敷一层导电底漆才能喷涂面漆。同时由于静电喷涂的工艺,很多具有耐化学品(洗手液、洗洁精、洗面奶等日化品)要求的塑胶涂料在静电喷涂时漆膜表面粗糙,颜色不均匀,效果差达不到客户要求。而一些耐化学品较好的涂料,却不耐乙醇擦拭。市场上提出的解决方案有三种:喷一层普通的色漆,表面罩双组份聚氨酯清漆;直接喷涂双组份聚氨酯色漆;喷一层底色漆,表面罩紫外光固化清漆。这三种方案都会增加工厂的设备和用料成本。
因此,现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足,本发明的目的在于提供一种耐化学品塑胶涂料及其使用方法和应用,旨在解决现有耐化学品的塑胶涂料在静电喷涂时漆膜表面粗糙、颜色不均匀、效果不好的问题。
本发明的技术方案如下:
一种耐化学品塑胶涂料,其中,所述耐化学品塑胶涂料,按重量百分比计,主要由以下组分组成:
热塑性丙烯酸树脂10-30%,改性丙烯酸树脂35-65%,三元氯醋树脂0-10%,有机溶剂8-20%,附着促进剂1-3%,流平剂0.1-0.5%,手感剂1-5%。
所述的耐化学品塑胶涂料,其中,所述有机溶剂包含丁酮,甲基异丁基酮和乙二醇丁醚,丙二醇丁醚的一种或几种。
所述的耐化学品塑胶涂料,其中,所述有机溶剂的成分为丁酮3-10%,丙二醇单丁醚5-10%。
上述耐化学品塑胶涂料的使用方法,其中,所述耐化学品塑胶涂料的使用方法为,使用前,用稀释剂进行稀释,将稀释后的耐化学品塑胶涂料喷涂于基材表面;
所述稀释后的耐化学品塑胶涂料岩田2#杯粘度为10-11秒25℃。
所述的耐化学品塑胶涂料的使用方法,其中,所述稀释剂,按重量百分比计,由以下组分组成:
白电油5-20%,异丙醇10-30%,异丁醇5-20%,乙酸乙酯10-30%,甲基异丁基酮5-25%,乙酸正丁酯5-15%,二丙酮醇10-20%,丙二醇丁醚5-20%,不饱和酸式羧酸酯的烷醇基铵盐溶液0.2-3%。
所述的耐化学品塑胶涂料的使用方法,其中,在稀释后的耐化学品塑胶涂料喷涂于基材表面前,所述基材表面喷涂有一层导电底漆。
所述的耐化学品塑胶涂料的使用方法,其中,所述导电底漆,按重量百分比计,由以下组分组成:
无水乙醇30-50%,异丙醇30-50%,异丁醇5-20%,二丙酮醇1-5%,助剂0.1-0.5,不饱和酸式羧酸酯的烷醇基铵盐溶液0.5-3%;
所述助剂为流平剂、润湿剂或消泡剂中的一种或多种。
所述的耐化学品塑胶涂料的使用方法,其中,所述喷涂的方式为手工喷涂、机械喷涂或静电喷涂。
上述的耐化学品塑胶涂料的使用方法,其中,将所述的耐化学品塑胶涂料喷涂于聚苯乙烯、聚碳酸酯、聚丙烯或丙烯睛-丁二烯-苯乙烯的基材上。
所述的耐化学品塑胶涂料的使用方法,其中,将所述的耐化学品塑胶涂料静电喷涂于聚苯乙烯、聚氯丁烯聚丙烯或丙烯睛-丁二烯-苯乙烯的基材上。
有益效果:本发明所提供的耐化学品塑胶涂料,是一种单组份塑胶涂料,面漆静电喷涂效果好,表面平滑,颜色均匀。干燥后的漆膜耐化学品优异,同时兼顾耐乙醇擦拭。
具体实施方式
本发明提供一种耐化学品塑胶涂料及其使用方法和应用,为使本发明的目的、技术方案及效果更加清楚、明确,以下对本发明进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
本发明所提供的耐化学品塑胶涂料,是一种单组份塑胶涂料,不仅耐化学品性能优秀,而且耐乙醇擦拭,同时非常适合静电喷涂。
所述耐化学品塑胶涂料,按重量百分比计,由以下组分制成:
热塑性丙烯酸树脂(10-30%),改性丙烯酸树脂(35-65%),三元氯醋树脂(0-10%),有机溶剂(8-20%),附着促进剂(1-3%),流平剂(0.1-0.5%),手感剂(1-5%)。
所述热塑性丙烯酸树脂提供耐化性及施工性;所述改性丙烯酸树脂提供耐醇性及耐化性。
所述三元氯醋树脂的作用是增加涂料的耐化学品性、耐醇性和附着力。
所述附着促进剂为聚酯树脂类,可增加对基材的附着力。
所述流平剂为聚硅氧烷类,让涂层表面平滑均匀。
所述手感剂为有机硅油类,增加表面滑爽手感。
所述有机溶剂包含丁酮,甲基异丁基酮和乙二醇丁醚,丙二醇丁醚的一种或几种,优选为含有丁酮(3-10%),丙二醇单丁醚(5-10%)。
所述耐化学品塑胶涂料的制备方法为将热塑性丙烯酸树脂、改性丙烯酸树脂、三元氯醋树脂、有机溶剂、附着促进剂、流平剂和手感剂依次加入,搅拌均匀,成耐化学品塑胶涂料。
本发明还提供所述耐化学品塑胶涂料的稀释剂,用于稀释所述耐化学品塑胶涂料。所述耐化学品塑胶涂料的稀释剂是由有机溶剂和增加涂料导电性的助剂组成。所述有机溶剂优选为包含乙二醇丁醚。
所述耐化学品塑胶涂料的稀释剂,按重量百分比计,由以下组分组成:
白电油(5-20%),异丙醇(10-30%),异丁醇(5-20%),乙酸乙酯(10-30%),甲基异丁基酮(5-25%),乙酸正丁酯(5-15%),二丙酮醇(10-20%),丙二醇丁醚(5-20%),不饱和酸式羧酸酯的烷醇基铵盐溶液(0.2-3%)。所述耐化学品塑胶涂料的稀释剂的电阻为15-25KΩ。
所述不饱和酸式羧酸酯的烷醇基铵盐溶液是增加静电喷涂涂料导电性的助剂。
所述耐化学品塑胶涂料的稀释剂的制备方法为,将白电油、异丙醇、异丁醇、乙酸乙酯、甲基异丁基酮、乙酸正丁酯、二丙酮醇、丙二醇丁醚和不饱和酸式羧酸酯的烷醇基铵盐溶液依次加入反应釜中,混合均匀。
本发明还提供所述耐化学品塑胶涂料的使用方法,在使用前,将所述耐化学品塑料涂料的稀释剂与所述耐化学品塑胶涂料混合后,岩田2#杯粘度为10-11秒25℃,电阻为50-80KΩ,喷涂于基材的表面。所述喷涂的方式可以为手工喷涂、机械喷涂或静电喷涂,本发明所提供的塑胶涂料尤其适用于静电喷涂。所述的耐化学品塑胶涂料适用于聚苯乙烯、聚碳酸酯、聚丙烯或丙烯睛-丁二烯-苯乙烯等基材。所述的耐化学品塑胶涂料适用于静电喷涂于聚苯乙烯、聚碳酸酯、聚丙烯或丙烯睛-丁二烯-苯乙烯的基材上。
在所述耐化学品塑胶涂料喷涂于基材表面前,优选在基材表面先均匀喷涂一层导电底漆。
所述导电底漆主要由醇类溶剂和增加涂料导电性的助剂组成。所述导电底漆,按重量百分比计,由以下组分组成:无水乙醇(30-50%),异丙醇(30-50%),异丁醇(5-20%),二丙酮醇(1-5%),助剂(0.1-0.5),不饱和酸式羧酸酯的烷醇基铵盐溶液(0.5-3%)。
所述助剂包含流平剂、润湿剂或消泡剂中的一种或多种。
所述流平剂为聚醚改性聚二甲基硅氧烷类。所述润湿剂为聚醚改性聚二甲基硅氧烷类或含氟表面活性剂聚合物。所述消泡剂为破泡聚硅氧烷类。
所述导电底漆的制备方法为依次将上述组分加入,并搅拌均匀。所述导电底漆的电阻为2-5 KΩ。
实施例的实施例步骤:
1、按表1实施例1将各组分依次加入并搅拌均匀成混合涂料。
2、按表2实施例4将各组分依次加入并搅拌均匀成导电底漆,测电阻2-5 KΩ。
3、按表3实施例7将各组分依次加入并搅拌均匀成面漆稀释剂,测电阻15-25 KΩ.
4、将实施例4的导电底漆均匀喷涂在塑胶件上,闪干1分钟左右。
5、将实施例1和实施例7混合,岩田2#杯粘度为10-11秒25℃,电阻为50-80 KΩ.静电喷涂,闪干2-5分钟,60-70℃烤15-20分钟。放置24小时后测试,
6、按表1表2表3实施例交叉重复1-5步骤,性能测试条件见表4.测试结果良好,见表5
表1:面漆涂料实施例
表2:导电底漆实施例
表3:面漆稀释剂实施例
表4:性能测试指标
表5:测试结果
备注:比较例为中华制漆机壳WK类涂料。
应当理解的是,本发明的应用不限于上述的举例,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (10)
1.一种耐化学品塑胶涂料,其特征在于,所述耐化学品塑胶涂料,按重量百分比计,主要由以下组分组成:
热塑性丙烯酸树脂10-30%,改性丙烯酸树脂35-65%,三元氯醋树脂0-10%,有机溶剂8-20%,附着促进剂1-3%,流平剂0.1-0.5%,手感剂1-5%。
2.根据权利要求1所述的耐化学品塑胶涂料,其特征在于,所述有机溶剂包含丁酮,甲基异丁基酮和乙二醇丁醚,丙二醇丁醚的一种或几种。
3.根据权利要求1所述的耐化学品塑胶涂料,其特征在于,所述有机溶剂的成分为丁酮3-10%,丙二醇单丁醚5-10%。
4.一种如权利要求1所述耐化学品塑胶涂料的使用方法,其特征在于,所述耐化学品塑胶涂料的使用方法为,使用前,用稀释剂进行稀释,将稀释后的耐化学品塑胶涂料喷涂于基材表面;
所述稀释后的耐化学品塑胶涂料涂岩田2#杯粘度为10-11秒25℃。
5.根据权利要求4所述的耐化学品塑胶涂料的使用方法,其特征在于,所述稀释剂,按重量百分比计,由以下组分组成:
白电油5-20%,异丙醇10-30%,异丁醇5-20%,乙酸乙酯10-30%,甲基异丁基酮5-25%,乙酸正丁酯5-15%,二丙酮醇10-20%,丙二醇丁醚5-20%,不饱和酸式羧酸酯的烷醇基铵盐溶液0.2-3%。
6.根据权利要求5所述的耐化学品塑胶涂料的使用方法,其特征在于,在稀释后的耐化学品塑胶涂料喷涂于基材表面前,所述基材表面喷涂有一层导电底漆。
7.根据权利要求6所述的耐化学品塑胶涂料的使用方法,其特征在于,所述导电底漆,按重量百分比计,由以下组分组成:
无水乙醇30-50%,异丙醇30-50%,异丁醇5-20%,二丙酮醇1-5%,助剂0.1-0.5,不饱和酸式羧酸酯的烷醇基铵盐溶液0.5-3%;
所述助剂为流平剂、润湿剂或消泡剂中的一种或多种。
8.根据权利要求4所述的耐化学品塑胶涂料的使用方法,其特征在于,所述喷涂的方式为手工喷涂、机械喷涂或静电喷涂。
9.一种如权利要求1所述的耐化学品塑胶涂料的应用,其特征在于,将所述的耐化学品塑胶涂料喷涂于聚苯乙烯、聚碳酸酯、聚丙烯或丙烯睛-丁二烯-苯乙烯的基材上。
10.根据权利要求9所述的耐化学品塑胶涂料的应用,其特征在于,将所述的耐化学品塑胶涂料静电喷涂于聚苯乙烯、聚碳酸酯、聚丙烯或丙烯睛-丁二烯-苯乙烯的基材上。