CN102352080A - 一种高抗冲pvc管材配方 - Google Patents

一种高抗冲pvc管材配方 Download PDF

Info

Publication number
CN102352080A
CN102352080A CN2011103589476A CN201110358947A CN102352080A CN 102352080 A CN102352080 A CN 102352080A CN 2011103589476 A CN2011103589476 A CN 2011103589476A CN 201110358947 A CN201110358947 A CN 201110358947A CN 102352080 A CN102352080 A CN 102352080A
Authority
CN
China
Prior art keywords
impact
pipe material
pvc pipe
pvc
polyvinyl chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103589476A
Other languages
English (en)
Inventor
徐风飞
邓碧霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Heshan Liansu Industrial Development Co Ltd
Original Assignee
Heshan Liansu Industrial Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heshan Liansu Industrial Development Co Ltd filed Critical Heshan Liansu Industrial Development Co Ltd
Priority to CN2011103589476A priority Critical patent/CN102352080A/zh
Publication of CN102352080A publication Critical patent/CN102352080A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种高抗冲PVC管材配方，其组分包括PVC树脂粉、有机重钙、有机锡稳定剂、硬脂酸钙、PE蜡、抗冲剂、钛白粉、环氧大豆油和加工助剂。与现有技术相比，本发明配方制得的PVC管材具有高强度和高韧性并重的特点，抗冲击能力强，且产品组分价格低廉，市场竞争力大。

Description

一种高抗冲PVC管材配方
技术领域
本发明涉及塑胶管道技术领域，尤其涉及一种高抗冲PVC管材配方。
背景技术
PVC管材的主要成分是聚氯乙烯，另外加入其它成分来增强其耐热性、韧性、延展性等。PVC在当今世界上深受喜爱，是颇为流行并广泛应用的一种合成材料。PVC管材是一种成熟的管材，主要应用于给排水工程。PVC管材具有耐酸、耐碱、耐腐蚀、强度高等优点，但抗冲性能比较差。
发明内容
本发明克服了现有技术中的不足，提供了一种强度与抗冲性能并重的高抗冲PVC管材配方。
为了实现上述的目的，采用如下的技术方案：一种高抗冲PVC管材配方，包括以下重量份数的组分：
PVC树脂粉        100
有机重钙          3-10
有机锡稳定剂      1-3
硬脂酸钙          0.5-1
PE蜡             0.5-3
抗冲剂            1-5
钛白粉            1-5
环氧大豆油        1-5
加工助剂          1-5。
抗冲剂即为抗冲击改性剂，主要作用是改善高分子材料的低温脆化，在PVC管材中加入适量的抗冲剂，可有效提高PVC管材的抗冲击性能，赋予管材更高的韧性。
上述方案中，所述抗冲剂采用MBS类的抗冲剂。MBS树脂的溶度参数与PVC相近，故两者的热力学相容性好，表现为在室温或低温下具有很高的抗冲击强度。并且由于两者的折光指数相近，故当两者共混熔融以后，容易达到均一的折射率,因此用MBS做PVC的抗冲剂，不会影响其透明性。
上述方案中，所述PVC树脂粉采用SG-5型。PVC树脂SG-5型材料的强度、刚度、韧性、耐热及耐低温性适中，而成型加工性能也适中，适合作为本PVC-U配方的材料。
上述方案中，所述有机重钙采用纳米级的有机重钙，所述有机锡稳定剂采用甲基型的有机锡稳定剂，所述钛白粉采用金红石型钛白粉。
与现有技术相比，本发明配方制得的PVC管材具有高强度和高韧性并重的特点，抗冲击能力强，且产品组分价格低廉，市场竞争力大。
具体实施方式
下面结合实施例对本发明作进一步的描述。
采用本发明提供的配方生产管材包括以下步骤：
1、配好各组分的剂量；
2、将配好的各组分在高速混和机中搅拌均匀，当混合料温度达到120℃时，放入低速冷混搅拌机中冷混搅拌，当混合料温度达到40℃时，卸料待用。
3、将混合好的物料投入锥形双螺杆挤出机中进行挤出加工成型，设定机筒加热温度120-200℃，口模温度120-200℃，螺杆转速10-50rpm，加料转速在5-50rpm。
具体实施例的组分、重量份及加工参数如表1所示，
  实施例一 实施例二 实施例三
PVC 100 100 100
有机重钙 8.0 5.0 3.0
有机锡稳定剂 1.6 1.6 1.6
硬脂酸钙 0.5 0.5 0.5
PE蜡(YL-100) 1.8 1.0 0.6
抗冲剂 2 1.5 1.2
钛白粉 1.5 1.5 1.5
环氧大豆油 1 1.5 1
机筒、模头温度 130-160℃ 120-170℃ 130-200℃
主机螺杆转速 30rpm 40rpm 40rpm
加料转速 25rpm 30rpm 40rpm
表1
物料从口模挤出后经过水槽冷却，根据所需长度切断，即可得到高抗冲PVC管材。
各实施例制得的PVC管材的性能参数如表2所示，
性能 实施例一 实施例二 实施例三
拉伸强度（MPa） 39.54 41.48 49.57
伸长率（%） 121.9 75.6 178.4
冲击强度（KJ/m2） 5.11 8.75 7.84
弯曲强度（MPa） 64.55 61.3 77.03
弯曲模量（MPa） 2484 2328 2613
表2
从表2中各参数可以看出，由本发明配方制得的PVC管材，性能好，强度高，实现了PVC管材的强度与韧性并重。

Claims (6)

1.一种高抗冲PVC管材配方，其特征在于，包括以下重量份数的组分：
PVC树脂粉        100
有机重钙          3-10
有机锡稳定剂      1-3
硬脂酸钙          0.5-1
PE蜡             0.5-3
抗冲剂            1-5
钛白粉            1-5
环氧大豆油        1-5
加工助剂          1-5。
2.根据权利要求1所述的PVC管材配方，其特征在于，所述抗冲剂采用MBS类的抗冲剂。
3.根据权利要求1所述的PVC管材配方，其特征在于，所述PVC树脂粉采用SG-5型。
4.根据权利要求1所述的PVC管材配方，其特征在于，所述有机重钙采用纳米级的有机重钙。
5.根据权利要求1所述的PVC管材配方，其特征在于，所述有机锡稳定剂采用甲基型的有机锡稳定剂。
6.根据权利要求1所述的PVC管材配方，其特征在于，所述钛白粉采用金红石型钛白粉。
CN2011103589476A 2011-11-14 2011-11-14 一种高抗冲pvc管材配方 Pending CN102352080A (zh)