CN102702651A - 一种纳米级增韧增强的pvc-m管材 - Google Patents

一种纳米级增韧增强的pvc-m管材 Download PDF

Info

Publication number
CN102702651A
CN102702651A CN2012102208062A CN201210220806A CN102702651A CN 102702651 A CN102702651 A CN 102702651A CN 2012102208062 A CN2012102208062 A CN 2012102208062A CN 201210220806 A CN201210220806 A CN 201210220806A CN 102702651 A CN102702651 A CN 102702651A
Authority
CN
China
Prior art keywords
pvc
tubing
nano level
toughness reinforcing
tubular product
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102208062A
Other languages
English (en)
Inventor
鲁忠瑛
范永兵
李永峰
李晓轩
鱼江涛
张红梅
明瑞军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGXIA QINGLONG PIPES INDUSTRY Co Ltd
Original Assignee
NINGXIA QINGLONG PIPES INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGXIA QINGLONG PIPES INDUSTRY Co Ltd filed Critical NINGXIA QINGLONG PIPES INDUSTRY Co Ltd
Priority to CN2012102208062A priority Critical patent/CN102702651A/zh
Publication of CN102702651A publication Critical patent/CN102702651A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纳米级增强增韧的PVC-M管材。所述PVC-M管材中含有一种纳米增强材料。本发明充分利用了纳米级增强材料在塑料中应用具有优异的增韧补强作用，可显著改善塑料的流变均匀性，提高其成型性，可显著提升塑料的拉伸强度和弹性模量的优点，在PVC-M管材中应用后，可显著改善其加工流动性，产品韧性与强度刚性有大幅度提高，从而有效降低抗冲改性剂和加工助剂的用量，从而解决了管材拉伸强度降低、管材塑化度不均匀等质量缺陷。由于减少了增韧剂的用量，并加入了廉价的纳米级增强材料，管材的生产成本有较大幅度降低。

Description

一种纳米级增韧增强的PVC-M管材
技术领域
本发明涉及一种PVC管材的生产技术，特别是一种纳米级增韧增强的PVC-M管材。
背景技术
给水用抗冲改性聚氯乙烯(PVC-M)管材其优良的耐低温脆性以及耐环境应力开裂性和拉伸屈服强度，被认为是替代传统给水用聚氯乙烯(PVC-U)管材首选产品，普遍用于建筑给水、排水、建筑采暖、城镇给排水以及农业节水灌溉等领域。为满足PVC-M管材的上述优点，在加工配方中需要添加一些抗冲改性剂、增韧剂等，但在实际加工过程中，少量的抗冲改性剂和增韧剂的添加会造成管材韧性不足，达不到抗冲改性目的，而过量的添加又会导致韧性有余而强度刚性不足，管材拉伸屈服强度大幅度下降，管材承压能力达不到标准要求。并且配方体系中因有大量抗冲改性剂的存在，在加工生产中，往往管材二氯甲烷浸渍试验(塑化度)很难达标，传统工艺生产出的管材内外壁外观质量较差，且生产成本较高。
目前，公知的专利技术中，只是部分解决了刚、韧平衡的缺点，但均未解决刚、韧平衡后，管材整体拉伸屈服强度下降，外观质量差、二氯甲烷浸渍试验(塑化度)不合格、生产成本高等缺陷。
发明内容
本发明的目的是克服现有技术缺陷，提供一种纳米级增韧增强的PVC-M管材。
本发明的技术方案为：
一种纳米级增韧增强的PVC-M管材，所述PVC-M管材中含有一种纳米增强材料。
所述管材的原料组成以重量份计为：
Figure BDA00001831497600021
上述所述的聚氯乙烯树脂为SG-5型树脂；
上述所述的的润滑剂为石蜡、硬脂酸或聚乙烯蜡、氧化聚乙烯蜡中任意两种或两种以上的组合；
上述所述的热稳定剂为有机锡稳定剂；
上述所述加工助剂为丙烯酸酯类聚合物(ACR)加工助剂；
上述所述的抗冲改性剂为甲基丙烯酸甲酯、丁二烯、苯乙烯共聚物(MBS)、氯化聚乙烯(CPE)、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、苯乙烯共聚物(ACR401)中任意两种或两种以上组合；
上述填充剂为轻质碳酸钙；
上述所述纳米增强材料为粒径30～70纳米的超微细碳酸钙或纳米级滑石粉中的一种或两种任意组合；
上述所述的偶联剂为钛酸酯类、铝酸酯类偶联剂中一种或两种任意组合。
本发明充分利用了纳米级增强材料在塑料中应用具有优异的增韧补强作用，可显著改善塑料的流变均匀性，提高其成型性，可显著提升塑料的拉伸强度和弹性模量的优点，在PVC-M管材中应用后，可显著改善其加工流动性，产品韧性与强度刚性有大幅度提高，从而有效降低抗冲改性剂和加工助剂的用量，从而解决了管材拉伸强度降低、管材塑化度不均匀等质量缺陷。由于减少了增韧剂的用量，并加入了廉价的纳米级增强材料，管材的生产成本有较大幅度降低。
普通抗冲改性聚氯乙烯(PVC-M)管材与纳米增强增韧聚氯乙烯(PVC-M)管材物理性能对比见下表。
Figure BDA00001831497600041
具体实施方式：
实施例1
按照下列配比准备原料：
聚氯乙烯树脂(SG-5)80份，有机锡0．4份，石蜡0．8份，聚乙烯蜡0．4份，ACR(201)0．8份，CPE2份，ACR(401)3份，轻质碳酸钙3份，纳米级滑石粉5份，钛酸酯偶联剂0．4份，着色剂炭黑0．05份。
将上述配料进行热混、冷混后再通过挤出成型制成管材。
实施例2
按照下列配比准备原料：
聚氯乙烯树脂(SG-5)100份，有机锡0．5份，石蜡0．9份，聚乙烯蜡0．5份，ACR(201)0．5份，CPE2份，MBS5份，轻质碳酸钙4份，纳米级超细碳酸钙6份，铝酸酯偶联剂0．3份，着色剂炭黑0．05份。
将上述配料进行热混、冷混后再通过挤出成型制成管材
实施例3
按照下列配比准备原料：
聚氯乙烯树脂(SG-5)85份，有机锡0．5份，石蜡0．9份，聚乙烯蜡0．5份，CPE2份，ACR(401)4份，轻质碳酸钙4份，纳米级超细碳酸钙3份，纳米级滑石粉3份，钛酸酯偶联剂0．3份，着色剂炭黑0．05份。
将上述配料进行热混、冷混后再通过挤出成型制成管材本发明的具体实施方式不限于上述实施案例所提供的方式。

Claims (10)

1.一种纳米级增韧增强的PVC-M管材，其特征在于所述PVC-M管材中含有一种纳米增强材料。
2.按照权利要求1所述的纳米级增韧增强的PVC-M管材，其特征在于所述管材的原料组成以重量份计为：
聚氯乙烯树脂（PVC） 80～100份
润滑剂   0.6～1.6
热稳定剂  0.4～1.0
加工助剂 0.5～2
抗冲改性剂 0～5
填充剂  0～5
纳米增强材料 1～10
偶联剂     0.1～1份
着色剂  0.01～0.05。
3.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述纳米增强材料为粒径30～70纳米的超微细碳酸钙或纳米级滑石粉中的一种或两种任意组合。
4.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述的聚氯乙烯树脂为SG-5型树脂。
5.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述的的润滑剂为石蜡、硬脂酸或聚乙烯蜡、氧化聚乙烯蜡中任意两种或两种以上的组合。
6.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述的热稳定剂为有机锡稳定剂。
7.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述加工助剂为丙烯酸酯类聚合物（ACR）加工助剂。
8.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述的抗冲改性剂为甲基丙烯酸甲酯、丁二烯、苯乙烯共聚物（MBS）、氯化聚乙烯（CPE）、甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸丁酯、苯乙烯共聚物（ACR401）中任意两种或两种以上组合。
9.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述填充剂为轻质碳酸钙。
10.按照权利要求2中所述的纳米级增韧增强的PVC-M管材，其特征是：上述所述的偶联剂为钛酸酯类、铝酸酯类偶联剂中一种或两种任意组合。
CN2012102208062A 2012-06-29 2012-06-29 一种纳米级增韧增强的pvc-m管材 Pending CN102702651A (zh)