CN102277784A - 纸张耐折增强剂及其制备方法 - Google Patents

纸张耐折增强剂及其制备方法 Download PDF

Info

Publication number
CN102277784A
CN102277784A CN201110166423A CN201110166423A CN102277784A CN 102277784 A CN102277784 A CN 102277784A CN 201110166423 A CN201110166423 A CN 201110166423A CN 201110166423 A CN201110166423 A CN 201110166423A CN 102277784 A CN102277784 A CN 102277784A
Authority
CN
China
Prior art keywords
reinforcing agent
polyvinyl alcohol
carboxymethyl cellulose
aqueous solution
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201110166423A
Other languages
English (en)
Inventor
王林军
钱松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BAOJI DONGSHENG AUXILIARIES MANUFACTURING CO LTD
Original Assignee
BAOJI DONGSHENG AUXILIARIES MANUFACTURING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BAOJI DONGSHENG AUXILIARIES MANUFACTURING CO LTD filed Critical BAOJI DONGSHENG AUXILIARIES MANUFACTURING CO LTD
Priority to CN201110166423A priority Critical patent/CN102277784A/zh
Publication of CN102277784A publication Critical patent/CN102277784A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种纸张耐折增强剂及其制备方法。原料组分的重量份是：聚乙稀醇37.5-38∶羧甲基纤维素40-42∶壳聚糖2.0-2.5∶淀粉10-12∶干强剂4-5∶磷酸5-6；其制备方法如下：1、制取聚乙稀醇水溶液：2、制取羧甲基纤维素水溶液：3、将上述：聚乙稀醇制成的水溶液和羧甲基纤维素制成的水溶液；4、加入壳聚糖和淀粉，搅拌成混合液；5、将干强剂稀释后，加入上述混合液，搅拌；6、补加清水；7、调PH值。本发明之纸张表面增强剂，由多种高分子化合物，按一定的比例和流程复合而成，使用时，稀释之，均匀地涂在纸张的表层。该纤维增强剂，具有优良的亲和力和极强的成膜性，可用于白板纸、牛皮箱板纸、铜版纸等之纸板表面的施胶和涂布。该增强剂较传统工艺可提高纸板表面强20-25％。从而可降低纸张中添加的木浆比例，降低生产成本，有利于保护木材资源。

Description

纸张耐折增强剂及其制备方法
技术领域  本发明涉及造纸技术，具体地说是提高纸板表面强度和纸张耐折强度的技术。 
背景技术  传统牛皮挂面纸的生产方法，是用增加挂面量即增加木浆比例的办法，来提高成纸的表面强度和耐折度，因此需要较高的生产成本，消耗更多的木材资源，且木浆比例的增加又带来生产过程的复杂化。 
发明内容  本发明的目的在于，既保证提高纸板表面强度和纸张耐折强度，又降低浆料中木浆的配比，以降低生产成本和节约木材资源。 
本发明是以下述步骤和方法实现的： 
原料组分主要有：聚乙稀醇、羧甲基纤维素、壳聚糖、淀粉、干强剂、磷酸。其间的重量份是，：聚乙稀醇37.5-38∶羧甲基纤维素40-42∶壳聚糖2.0-2.5∶淀粉10-12∶干强剂4-5∶磷酸5-6。 
该增强剂的制备方法如下： 
1、制取聚乙稀醇水溶液：将聚乙稀醇加入水中，聚乙稀醇与水的比例为100∶500～570； 
2、制取羧甲基纤维素水溶液：将羧甲基纤维素加入水中，羧甲基纤维素与水的比例为100∶1200～1300； 
3、将上述：聚乙稀醇的水溶液和羧甲基纤维素的水溶液，放入反应釜中，充分搅拌均匀； 
4、加入壳聚糖和阳离子淀粉，搅拌3-5分钟，成混合液， 
5、将干强剂稀释18-22倍后，加入上述混合液，搅拌50～70分钟； 
所说干强剂，是一种用于提高成膜性的高分子化合物——分子量为50-80万的聚丙烯酰胺。 
6、补加清水，清水量与上述2的总量比例为1∶12.5-13.5提示； 
7、加入磷酸，调PH值到5-6； 
8、装桶出货。 
施胶和涂布的工艺是 
1.在待加工纸的表面施胶的淀粉糊化罐中，加入一定量的清水，再加入定量的淀粉，使其淀粉浓度为20-25％，开动搅拌，缓慢通汽加温至93-95℃。 
2.淀粉液达到糊化温度时，保温20分钟，然后加入定量的清水，使溶液温度降低至65℃～70℃。 
3.加入定量的本品，搅拌5分钟，上机使用。也可将本品稀释后用计量泵连续添加于施胶机中。 
4.用量视纸钟、原材料及强度要求不同而作相应调节，特殊情况需另做调整，一般吨纸用量在5-7KG即可达到要求。 
本发明之纸张表面增强剂，由多种高分子化合物，按一定的比例和流程，多步复合而成。使用时，稀释之，均匀地涂在纸张的表层。该纤维增强剂，具有优良的亲和力和极强的成膜性，可用于白板纸、牛皮箱板纸、铜版纸等之纸板表面的施胶和涂布。该增强剂较传统工艺可提高纸板表面强20-25％。从而可降低纸张中添加的木浆比例，降低了生产成本，有利于保护木材资源。 
本发明产品的性能指标如下： 
外观：透明胶体状        相对密度：1.00-1.30        固含量：15±1％ 
粘度(25℃)：≥1000CP    PH值：5.5±0.5             离子性：中性 
溶解性：易溶于水、与淀粉相溶性良好 
保质期(4-35℃)：6个月 
具体实施方式
下面叙述两个本发明的实施例，对本发明做进一步说明 
实施例1 
原料组分的重量份是：：聚乙稀醇37.5∶羧甲基纤维素42∶壳聚糖2.0∶淀粉12∶干强剂4∶磷酸6。 
本实施例增强剂的制备方法如下： 
1、制取聚乙稀醇水溶液：将聚乙稀醇加入水中，通入蒸汽化开，聚乙稀醇与水的比例为100∶570； 
2、制取羧甲基纤维素水溶液：将羧甲基纤维素加入水中，羧甲基纤维素与水的比例为100∶1200； 
3、将上述：37.5公斤聚乙稀醇制成的水溶液和40公斤羧甲基纤维素制成的水溶液，放入反应釜中，充分搅拌均匀； 
4、加入壳聚糖2.0公斤和淀粉10公斤，搅拌3分钟，成混合液， 
5、将干强剂稀释18-22倍后，加入上述混合液，搅拌70分钟； 
6、补加清水，清水量与上述2的总量比例为1∶12.5提示； 
7、加入磷酸，将PH值调到6； 
8、装桶出货。 
实施例2 
原料组分的重量份是：：聚乙稀醇38∶羧甲基纤维素40∶壳聚糖2.5∶淀粉10∶干强剂5∶磷酸5。 
本实施例增强剂的制备方法如下： 
1、制取聚乙稀醇水溶液：将聚乙稀醇加入水中，通入蒸汽化开，聚乙稀醇与水的比例为100∶500； 
2、制取羧甲基纤维素水溶液：将羧甲基纤维素加入水中，羧甲基纤维素与水的比例为100∶1300； 
3、将上述：37.5公斤聚乙稀醇制成的水溶液和40公斤羧甲基纤维素制成的水溶液，放入反应釜中，充分搅拌均匀； 
4、加入壳聚糖2.0公斤和阳离子淀粉10公斤，搅拌5分钟，成混合液， 
5、将干强剂稀释18-22倍后，加入上述混合液，搅拌50分钟； 
6、补加清水，清水量与上述2的总量比例为13.5提示； 
7、加入磷酸，将PH值调到5； 
8、装桶出货。 

Claims (2)

1.纸张耐折增强剂，其特征在于：原料组分中含有聚乙稀醇、羧甲基纤维素、壳聚糖、阳离子淀粉、干强剂、磷酸，其间的重量份是，：聚乙稀醇37.5-38∶羧甲基纤维素40-42∶壳聚糖2.0-2.5∶淀粉10-12∶干强剂4-5∶磷酸5-6。
2.纸张耐折增强剂的制备方法，其特征在于依下述步骤进行：
(1)制取聚乙稀醇的水溶液：将聚乙稀醇加入水中，聚乙稀醇与水的比例为100∶500～570；
(2)制取羧甲基纤维素的水溶液：将羧甲基纤维素加入水中，羧甲基纤维素与水的比例为100∶1200～1300
(3)将上述聚乙稀醇制成的水溶液和羧甲基纤维素制成的水溶液，放入反应釜中，充分搅拌均匀；
(4)加入壳聚糖和淀粉，搅拌3-5分钟，成混合液，
(5)将干强剂稀释18-22倍后，加入上述混合液，搅拌50～70分钟；
(6)补加清水，清水量与上述(2)的总量比例为1∶12.5-13.5提示；
(7)加磷酸调PH值至5-6；
(8)装桶出货。
CN201110166423A 2011-06-20 2011-06-20 纸张耐折增强剂及其制备方法 Pending CN102277784A (zh)