CN102277583B - 制备生物转化膜金属板的前处理方法 - Google Patents
制备生物转化膜金属板的前处理方法 Download PDFInfo
- Publication number
- CN102277583B CN102277583B CN 201110240803 CN201110240803A CN102277583B CN 102277583 B CN102277583 B CN 102277583B CN 201110240803 CN201110240803 CN 201110240803 CN 201110240803 A CN201110240803 A CN 201110240803A CN 102277583 B CN102277583 B CN 102277583B
- Authority
- CN
- China
- Prior art keywords
- clean
- out system
- time
- rinsing
- metal sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种制备生物转化膜金属板的前处理方法,取金属板;在常温条件下,将金属板放入清洗剂中浸泡3-10min,所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成;将金属板从清洗剂中取出,用自来水进行第一次漂洗,第一次漂洗的时间为3-5min,自来水的温度≥45℃;第一次漂洗之后,再在常温状态下用自来水对金属板进行第二次漂洗,第二次漂洗时间为1-3min。本发明具有生产工艺简单、清洗效果好、安全环保的优点。
Description
技术领域
本发明涉及一种制备生物转化膜金属板的前处理方法。
背景技术
目前,金属板清洗的过程是将原金属板表面进行除油、除锈,清洗的过程是将金属板浸入盐酸或硫酸等清洗介质中,其目的是为了去除粘附在金属板基质表面的油垢、污垢,一般的表面处理工艺为:脱脂;两次水洗;除锈;再次水洗;表面调整;又一次水洗;磷化处理;最后一次水洗;晾干;这一整套处理工艺不仅清洗过程慢,而且存在很严重的排放问题,同时清洗时使用的盐酸或硫酸等清洗介质对人体有危害,对环境也会造成很大的污染。
发明内容
本发明的目的是为了克服以上的不足,提供一种生产工艺简单、清洗效果好、安全环保的制备生物转化膜金属板的前处理方法。
本发明是通过以下技术方案来实现:一种制备生物转化膜金属板的前处理方法,包括以下步骤:
A、取金属板;
B、在常温条件下,将金属板放入清洗剂中浸泡3-10min,所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成;
C、将金属板从清洗剂中取出,用自来水进行第一次漂洗,第一次漂洗的时间为3-5min,自来水的温度≥45℃;
D、第一次漂洗之后,再在常温状态下用自来水对金属板进行第二次漂洗,第二次漂洗时间为1-3min。
本发明的进一步改进在于:清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成。
本发明与现有技术相比具有以下优点:本发明对金属板表面进行清理处理,即将金属板放入含有有机物质的清洗剂中,将除油、除锈工艺合并在同一个工序内完成,清洗的过程是将粘附在金属板基质表面的油垢、污垢经清洗介质润湿渗透,并与金属板基质剥离分散,经中温水漂洗和常温水漂洗,使金属板基质表面被清洁干净,清洗步骤简单,清洗效果好,采用的清洗剂环保无危害。
具体实施方式:
为了加深对本发明的理解,下面将结合实施例对本发明作进一步详述,以下实施例仅用于解释本发明,并不构成对本发明保护范围的限定。
本发明一种制备生物转化膜金属板的前处理方法,取金属板;在常温条件下,将金属板放入清洗剂中浸泡3-10min,所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成;将金属板从清洗剂中取出,用自来水进行第一次漂洗,第一次漂洗的时间为3-5min,自来水的温度≥45℃,最佳温度为45℃;第一次漂洗之后,再在常温状态下用自来水对金属板进行第二次漂洗,第二次漂洗时间为1-3min。
所述清洗剂按质量比包括以下成分:
生物有机酸:0.02-4%;
维生素:0.3~1%;
食用碳酸氢钠:3-5%;
缓蚀剂:2-10%;
表面活性剂:1.01-2.05%;
水:78-86%。
其中,生物有机酸为柠檬酸和乳酸的混合液,柠檬酸占清洗剂总质量的0.01-3%,所述乳酸占清洗剂总质量的0.01-1%,维生素为维生素B,缓蚀剂为酒石酸,表面活性剂为辛基酚聚氧乙烯醚和十二烷基磺酸钠的混合物,辛基酚聚氧乙烯醚占清洗剂总重量的0.01-0.05%,十二烷基磺酸钠占清洗剂总重量的1-2%。
金属板放入清洗剂中,清洗药剂对粘附在金属基质表面的油垢、污垢润湿渗透,清洗药剂中的生物介质及活性剂的游离使金属基质表面的油垢、污垢与金属基质脱离分散,同时可借助一定机械动力加强清洗效果,以防油垢、污垢再次沉积。
本发明对金属板表面进行清理处理,即将金属板放入含有有机物质的清洗剂中,将除油、除锈工艺合并在同一个工序内完成,清洗的过程是将粘附在金属板基质表面的油垢、污垢经清洗介质润湿渗透,并与金属板基质剥离分散,经中温水漂洗和常温水漂洗,使金属板基质表面被清洁干净,清洗步骤简单,清洗效果好,采用的清洗剂环保无危害。
Claims (1)
1.一种制备生物转化膜金属板的前处理方法,其特征在于:
A、取金属板;
B、在常温条件下,将金属板放入清洗剂中浸泡3-10min,所述清洗剂由生物有机酸、维生素、食用碳酸氢钠、缓蚀剂、表面活性剂、水组成;所述清洗剂按质量比包括以下成分:生物有机酸:0.02-4%;维生素:0.3~1%;食用碳酸氢钠:3-5%;缓蚀剂:2-10%;表面活性剂:1.01-2.05%;水:78-86%;其中,生物有机酸为柠檬酸和乳酸的混合液,柠檬酸占清洗剂总质量的0.01-3%,所述乳酸占清洗剂总质量的0.01-1%,维生素为维生素B,缓蚀剂为酒石酸,表面活性剂为辛基酚聚氧乙烯醚和十二烷基磺酸钠的混合物,辛基酚聚氧乙烯醚占清洗剂总重量的0.01-0.05%,十二烷基磺酸钠占清洗剂总重量的1-2%;
C、将金属板从清洗剂中取出,用自来水进行第一次漂洗,第一次漂洗的时间为3-5min,自来水的温度≥45℃;
D、第一次漂洗之后,再在常温状态下用自来水对金属板进行第二次漂洗,第二次漂洗时间为1-3min。