CN102277074A - 一种高遮盖力水性汽车修补漆及其制备方法 - Google Patents

一种高遮盖力水性汽车修补漆及其制备方法 Download PDF

Info

Publication number
CN102277074A
CN102277074A CN2011102096217A CN201110209621A CN102277074A CN 102277074 A CN102277074 A CN 102277074A CN 2011102096217 A CN2011102096217 A CN 2011102096217A CN 201110209621 A CN201110209621 A CN 201110209621A CN 102277074 A CN102277074 A CN 102277074A
Authority
CN
China
Prior art keywords
water
covering power
high covering
aqueous automobile
paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102096217A
Other languages
English (en)
Inventor
朱忠敏
赵瑛琛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Eastern Paint Technology (shanghai) Co Ltd
Original Assignee
Eastern Paint Technology (shanghai) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Eastern Paint Technology (shanghai) Co Ltd filed Critical Eastern Paint Technology (shanghai) Co Ltd
Priority to CN2011102096217A priority Critical patent/CN102277074A/zh
Publication of CN102277074A publication Critical patent/CN102277074A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高遮盖力水性汽车修补漆及其制备方法，该金属效果漆包括以下组分和重量份含量：水性树脂50～55，消泡剂0.01～0.1，分散剂2.5～6，助溶剂1～8，底材润湿剂0.1～0.3，杀菌防霉剂0.2，增稠剂0.22～0.32，有机颜料5～8，钛白粉0.8～2.0，去离子水25～40。与现有技术相比，本发明具有环保、遮盖力强、成本低等优点。

Description

一种高遮盖力水性汽车修补漆及其制备方法
技术领域
本发明涉及一种涂料，尤其是涉及一种高遮盖力水性汽车修补漆及其制备方法。
背景技术
目前汽车修补用水性漆在国内汽车修补领域刚刚起步。有效降低环境排放、符合VOC法规是水性修补漆的基本要求。而传统油性汽车修补漆对环境造成的要重污染主要来源于两个方面，其一是有毒气体VOC的排放，其二是含铅、铬等重金属污染物的有毒颜料的使用。一直以来，黄色颜料铅铬黄以其优秀的着色力、彩度和遮盖力被汽车修补漆行业所广泛采用，同时此种颜料也带来了严重的环境危害。因此应环境保护的需要，采用低公害的有机黄色颜料取代无机铅铬黄是各大厂商研究机构的必选方案。但有机黄颜料有着自身无法解决的性能问题，这主要反映在颜料遮盖力上。较差的遮盖力无法适应行业施工习惯，而且通过增加涂层厚度来改善遮盖力会大幅提高油漆成本，造成不必要的浪费。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种环保、遮盖力强、成本低的高遮盖力水性汽车修补漆及其制备方法。
本发明的目的可以通过以下技术方案来实现：一种高遮盖力水性汽车修补漆，其特征在于，该金属效果漆包括以下配方：
组分          重量份
水性树脂      50～55，
消泡剂        0.01～0.1，
分散剂        2.5～6，
助溶剂        1～8，
底材润湿剂    0.1～0.3，
杀菌防霉剂    0.2，
增稠剂        0.22～0.32，
有机颜料      5～8，
钛白粉        0.8～2.0，
去离子水      25～40。
所述的水性树脂包括水性聚氨酯树脂或水性丙烯酸树脂。
所述的消泡剂包括BYK-021，BYK024，Defom W-082或TEGO Airex931。
所述的分散剂包括TEGO Dispers 715W，TEGO Dispers 740W，NUOSPERSEFN 265或NUOSPERSE W-22。
所述的助溶剂包括正丁醇，仲丁醇，异丙醇，乙醇，丙二醇单甲醚或二丙二醇单甲醚。
所述的底材润湿剂包括BYK-348，TEGO Wet 500或TEGO Wet 250。
所述的杀菌防霉剂为杂环化合物杀菌防霉剂，包括苯并咪唑、1，2-苯并异噻唑啉酮、8-羟基喹啉。
所述的增稠剂为聚丙烯酸类水性增稠剂，包括Viscalex HV 30，Rheolate 212，Rheolate FX1070；所述的有机颜料包括PV FAST YELLOW H3G；所述的钛白粉为金红石型钛白粉，包括KRONOS 2190或GA-120。
一种高遮盖力水性汽车修补漆的制备方法，其特征在于，该方法包括以下步骤：
(1)将有机颜料，钛白粉，分散剂，消泡剂及去离子水按照配方顺序加入容器，在800～1200转/分钟的搅拌速度下，搅拌20～30分钟得到混合物，制备成组分a；
(2)将组分a通过砂磨机充分研磨至细度不超过5μm；
(3)将水性树脂，底材润湿剂，去离子水，杀菌防霉剂，增稠剂，助溶剂依次加入，在200-400转/分钟的搅拌速度下并搅拌均匀，制备成组份b；
(4)在200-400转/分钟的搅拌速度下将组份a加入b中，搅拌均匀。
与现有技术相比，本发明具有以下优点：
(1)环保对环境无公害；
(2)具有较高遮盖力；
(3)节省油漆用量，有效降低成本。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
实施例1
一种高遮盖力水性汽车修补漆的制备方法，该方法包括以下工艺步骤：
Figure BDA0000078372640000031
将去离子水和分散剂混合均匀，加入余下组分，在800～1200转/分钟的搅拌速度下，搅拌20～30分钟得到混合物，制备成组分a。经砂磨机充分研磨至细度小于5μm。
Figure BDA0000078372640000032
按照配方将前5种组分在200-400转/分钟的搅拌速度下并搅拌均匀，在搅拌状态加入Viscalex HV 30制备成组份b。
取28.5克组分a在200-400转/分钟的搅拌速度下加入b中，搅拌均匀。
实施例2
一种高遮盖力水性汽车修补漆的制备方法，该方法包括以下工艺步骤：
Figure BDA0000078372640000033
将去离子水和分散剂混合均匀，加入余下组分，在800～1200转/分钟的搅拌速度下，搅拌20～30分钟得到混合物，制备成组分a。经砂磨机充分研磨至细度小于5μm。
Figure BDA0000078372640000042
按照配方将前5种组分在200-400转/分钟的搅拌速度下并搅拌均匀，在搅拌状态加入Rheolate 212制备成组份b。
取28.5克组分a在200-400转/分钟的搅拌速度下加入b中，搅拌均匀。
实施例3
一种高遮盖力水性汽车修补漆的制备方法，该方法包括以下工艺步骤：
Figure BDA0000078372640000043
将去离子水和分散剂混合均匀，加入余下组分，在800～1200转/分钟的搅拌速度下，搅拌20～30分钟得到混合物，制备成组分a。经砂磨机充分研磨至细度小于5μm。
Figure BDA0000078372640000051
按照配方将前5种组分在200-400转/分钟的搅拌速度下并搅拌均匀，在搅拌状态加入Viscalex HV 30制备成组份b。
取28.5克组分a在200-400转/分钟的搅拌速度下加入b中，搅拌均匀。
实施例4
一种高遮盖力水性汽车修补漆的制备方法，该方法包括以下步骤：
(1)将5kg有机颜料PV FAST YELLOW H3G，2.0kg金红石型钛白粉KRONOS2190，2.5kg分散剂TEGO Dispers 715W，0.1kg消泡剂Defom W-082及去离子水按照配方顺序加入容器，在800转/分钟的搅拌速度下，搅拌20分钟得到混合物，制备成组分a；
(2)将组分a通过砂磨机充分研磨至细度不超过5μm；
(3)将55kg水性聚氨酯树脂，0.1kg底材润湿剂TEGO Wet 500，去离子水，0.2kg杂环化合物杀菌防霉剂苯并咪唑，0.22kg聚丙烯酸类水性增稠剂Rheolate212，1kg助溶剂正丁醇依次加入，在200转/分钟的搅拌速度下并搅拌均匀，制备成组份b；
(4)在200转/分钟的搅拌速度下将组份a加入b中，搅拌均匀。
实施例5
一种高遮盖力水性汽车修补漆的制备方法，该方法包括以下步骤：
(1)将8kg有机颜料PV FAST YELLOW H3G，0.8kg金红石型钛白粉GA-120，6kg分散剂NUOSPERSE FN 265，0.01kg消泡剂TEGO Airex931及去离子水按照配方顺序加入容器，在1200转/分钟的搅拌速度下，搅拌30分钟得到混合物，制备成组分a；
(2)将组分a通过砂磨机充分研磨至细度不超过5μm；
(3)将50kg水性丙烯酸树脂，0.3kg底材润湿剂BYK-348，去离子水，0.2kg杂环化合物杀菌防霉剂1，2-苯并异噻唑啉酮，0.32kg聚丙烯酸类水性增稠剂Viscalex HV 30，8kg助溶剂丙二醇单甲醚依次加入，在400转/分钟的搅拌速度下并搅拌均匀，制备成组份b；
(4)在400转/分钟的搅拌速度下将组份a加入b中，搅拌均匀。

Claims (9)

1.一种高遮盖力水性汽车修补漆，其特征在于，该金属效果漆包括以下配方：
组分          重量份
水性树脂      50～55，
消泡剂        0.01～0.1，
分散剂        2.5～6，
助溶剂        1～8，
底材润湿剂    0.1～0.3，
杀菌防霉剂    0.2，
增稠剂        0.22～0.32，
有机颜料      5～8，
钛白粉        0.8～2.0，
去离子水      25～40。
2.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的水性树脂包括水性聚氨酯树脂或水性丙烯酸树脂。
3.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的消泡剂包括BYK-021，BYK024，Defom W-082或TEGO Airex931。
4.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的分散剂包括TEGO Dispers 715W，TEGO Dispers 740W，NUOSPERSE FN 265或NUOSPERSE W-22。
5.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的助溶剂包括正丁醇，仲丁醇，异丙醇，乙醇，丙二醇单甲醚或二丙二醇单甲醚。
6.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的底材润湿剂包括BYK-348，TEGO Wet 500或TEGO Wet 250。
7.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的杀菌防霉剂为杂环化合物杀菌防霉剂，包括苯并咪唑、1，2-苯并异噻唑啉酮、8-羟基喹啉。
8.根据权利要求1所述的一种高遮盖力水性汽车修补漆，其特征在于，所述的增稠剂为聚丙烯酸类水性增稠剂，包括Viscalex HV 30，Rheolate 212，RheolateFX1070；所述的有机颜料包括PV FAST YELLOW H3G；所述的钛白粉为金红石型钛白粉，包括KRONOS 2190或GA-120。
9.一种如权利要求1所述的高遮盖力水性汽车修补漆的制备方法，其特征在于，该方法包括以下步骤：
(1)将有机颜料，钛白粉，分散剂，消泡剂及去离子水按照配方顺序加入容器，在800～1200转/分钟的搅拌速度下，搅拌20～30分钟得到混合物，制备成组分a；
(2)将组分a通过砂磨机充分研磨至细度不超过5μm；
(3)将水性树脂，底材润湿剂，去离子水，杀菌防霉剂，增稠剂，助溶剂依次加入，在200-400转/分钟的搅拌速度下并搅拌均匀，制备成组份b；
(4)在200-400转/分钟的搅拌速度下将组份a加入b中，搅拌均匀。
CN2011102096217A 2011-07-25 2011-07-25 一种高遮盖力水性汽车修补漆及其制备方法 Pending CN102277074A (zh)