CN102271841B - 一种金属零件的制造方法 - Google Patents
一种金属零件的制造方法 Download PDFInfo
- Publication number
- CN102271841B CN102271841B CN2010800039904A CN201080003990A CN102271841B CN 102271841 B CN102271841 B CN 102271841B CN 2010800039904 A CN2010800039904 A CN 2010800039904A CN 201080003990 A CN201080003990 A CN 201080003990A CN 102271841 B CN102271841 B CN 102271841B
- Authority
- CN
- China
- Prior art keywords
- density
- temperature
- compacting
- steel
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (11)