CN102219528A - 碳化硼陶瓷冷压成型用结合剂 - Google Patents
碳化硼陶瓷冷压成型用结合剂 Download PDFInfo
- Publication number
- CN102219528A CN102219528A CN2011101052781A CN201110105278A CN102219528A CN 102219528 A CN102219528 A CN 102219528A CN 2011101052781 A CN2011101052781 A CN 2011101052781A CN 201110105278 A CN201110105278 A CN 201110105278A CN 102219528 A CN102219528 A CN 102219528A
- Authority
- CN
- China
- Prior art keywords
- boron carbide
- binding agent
- cellulose
- water
- wedding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种碳化硼陶瓷冷压成型用结合剂，所述结合剂的组成和质量比是纤维素：水=0.03~0.09。纤维素是粉末状纤维素，易于溶解。所述结合剂中纤维素和水的质量比是纤维素：水=0.08。本发明采用无污染、低成本的纤维素和水为原料，经简单的混料就能制成效果良好的碳化硼陶瓷冷压成型用结合剂，这大大降低了生产成本，而且降低污染，有利于环境保护。
Description
技术领域
本发明涉及一种陶瓷成型用的结合剂，具体是一种碳化硼陶瓷冷压成型用结合剂。
背景技术
碳化硼陶瓷制品在我国生产已有50多年的历史，传统的生产工艺所使用的冷压成型结合剂为汽油橡胶，主要成分溶剂是航空汽油，结合剂是丁苯胶，这种结合剂的成本高、气味大、易燃易爆，危险性大，而且污染较严重。
发明内容
为了克服现有技术中存在的缺陷，本发明提供了一种低成本、无污染的碳化硼陶瓷冷压成型用结合剂。
本发明的技术方案是这样实现的：碳化硼陶瓷冷压成型用结合剂，所述结合剂的组成和质量比是纤维素：水=0.03~0.09。
所述纤维素是粉末状纤维素，粉末状易于溶解，丝状、颗粒状的纤维素溶解效果不好，在陶瓷制品成型过程中容易出现裂纹和起层现象。
所述结合剂中纤维素和水的质量比是纤维素：水=0.08。
本发明的有益效果是：本发明采用无污染、低成本的纤维素和水为原料，经简单的混料就能制成效果良好的碳化硼陶瓷冷压成型用结合剂，这大大降低了生产成本，而且降低污染，有利于环境保护。
具体实施方式
实施例1
碳化硼陶瓷冷压成型用结合剂的组成：粉末状纤维素50g和水（溶剂）2000g。
实施例2
碳化硼陶瓷冷压成型用结合剂的组成：粉末状纤维素80g和水（溶剂）1000g。
实施例3
碳化硼陶瓷冷压成型用结合剂的组成：粉末状纤维素30g和水（溶剂）1000g。
将上述原料混合搅拌，与碳化硼粉末混合经造粒、成型、干燥工艺得到碳化硼陶瓷产品。对上述结合剂进行碳化硼制品毛坯成型实验，得到的结果是：毛坯易于压制成型，质量好，毛坯没有裂纹和起层现象。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (3)
1. 碳化硼陶瓷冷压成型用结合剂，其特征在于，所述结合剂的组成和质量比是纤维素：水=0.03~0.09。
2.根据权利要求1所述的碳化硼陶瓷冷压成型用结合剂，其特征在于，所述纤维素是粉末状纤维素。
3. 根据权利要求1或2所述的碳化硼陶瓷冷压成型用结合剂，其特征在于，所述结合剂中纤维素和水的质量比是纤维素：水=0.08。