CN103537612A - 一种含有镁矿石尾渣的铸造型砂 - Google Patents

一种含有镁矿石尾渣的铸造型砂 Download PDF

Info

Publication number
CN103537612A
CN103537612A CN201310524419.2A CN201310524419A CN103537612A CN 103537612 A CN103537612 A CN 103537612A CN 201310524419 A CN201310524419 A CN 201310524419A CN 103537612 A CN103537612 A CN 103537612A
Authority
CN
China
Prior art keywords
magnesium ore
parts
molding sand
ore tailing
casting molding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310524419.2A
Other languages
English (en)
Inventor
黄俞丰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310524419.2A priority Critical patent/CN103537612A/zh
Publication of CN103537612A publication Critical patent/CN103537612A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种含有镁矿石尾渣的铸造型砂，由以重量份计的下述组分组成：石英颗粒40-55份，木质纤维素3-5份，硅藻土7-9份，钠基膨润土6-8份，可再分散性乳胶粉2-5份，粉状镁矿石尾渣4-6份，水8-12份，具体制备方法是，1)按配比称量粉状镁矿石尾渣、可再分散性乳胶粉、钠基膨润土，加入总量35-40％的水，浸泡3-4小时并保持温度在100-150℃，该型砂不添加煤粉、主要以秸秆粉末、草木灰为防粘助剂，以期降低成本，并改善铸件表面光洁度。

Description

一种含有镁矿石尾渣的铸造型砂
技术领域
本发明涉及铸造领域，特别涉及砂型铸造领域。
背景技术
目前，用砂型铸造生产的铸件占总铸件的80％。砂型铸造的造型材料在铸造生产中占有重要的地位，它直接影响铸造生产的能源消耗、环境污染，以及铸件的质量、生产效率和成本。国内外广泛使用的煤粉粘土湿型砂，一般由原砂、粘结剂、煤粉添加物等与水混制而成，具有一定的防粘砂效果和材料成本低、生产效率高的优点，但其消耗量大、排放严重、在铸造过程煤粉燃烧分解产生有毒气体污染。
由上可见，煤粉粘土湿型砂已经不适应铸造工业科学发展的需要和当前降耗减排的环境保护政策。所以，近些年，为了减少煤粉粘土砂对环境的污染，铸造工作者一直设法寻找合适的代用品。
发明内容
针对现有技术的不足，本发明的目的之一在于提供一种含有镁矿石尾渣的铸造型砂，该型砂不添加煤粉、主要以秸秆粉末、草木灰为防粘助剂，以期降低成本，并改善铸件表面光洁度。
为实现上述目的，本发明采用的技术方案为：
一种含有镁矿石尾渣的铸造型砂，由以重量份计的下述组分组成：石英颗粒40-55份，木质纤维素3-5份，硅藻土7-9份，钠基膨润土6-8份，可再分散性乳胶粉2-5份，粉状镁矿石尾渣4-6份，水8-12份，具体制备方法是，1)按配比称量粉状镁矿石尾渣、可再分散性乳胶粉、钠基膨润土，加入总量35-40％的水，浸泡3-4小时并保持温度在100-150℃，得浆料；2)按配比称量石英颗粒，木质纤维素，硅藻土，一起放入混砂机中干混，混合2-3小时；3)再在混砂机中加入步骤1)的浆料和剩余的水，混合2-4小时后，出砂。
所述粉状镁矿石尾渣粒度为80-100目。
本发明的含有镁矿石尾渣的铸造型砂的有益效果为：
(1)本发明的型砂不含煤粉；
(2)采用粉状镁矿石尾渣和硅藻土为防粘助剂，成本低，节约资源；
(3)在铸造过程中，不产生有毒、有污染的有害气体，绿色环保；
(4)通过各成分合理的配比，使得制备的型砂质量优异，采用该型砂生产的铸件表面光洁度高。
具体实施方式
一种含有镁矿石尾渣的铸造型砂，由以重量份计的下述组分组成：石英颗粒40-55份，木质纤维素3-5份，硅藻土7-9份，钠基膨润土6-8份，可再分散性乳胶粉2-5份，粉状镁矿石尾渣4-6份，水8-12份，具体制备方法是，1)按配比称量粉状镁矿石尾渣、可再分散性乳胶粉、钠基膨润土，加入总量35-40％的水，浸泡3-4小时并保持温度在100-150℃，得浆料；2)按配比称量石英颗粒，木质纤维素，硅藻土，一起放入混砂机中干混，混合2-3小时；3)再在混砂机中加入步骤1)的浆料和剩余的水，混合2-4小时后，出砂。
通过本发明含有镁矿石尾渣的铸造型砂的工艺性能为：
湿压强度(MPa)0.082-0.095
透气性102
热湿拉强度(KPa)312-320
破碎指数(j：)80-83％。

Claims (2)

1.一种含有镁矿石尾渣的铸造型砂，其特征在于，由以重量份计的下述组分组成：石英颗粒40-55份，木质纤维素3-5份，硅藻土7-9份，钠基膨润土6-8份，可再分散性乳胶粉2-5份，粉状镁矿石尾渣4-6份，水8-12份，具体制备方法是，1)按配比称量粉状镁矿石尾渣、可再分散性乳胶粉、钠基膨润土，加入总量35-40％的水，浸泡3-4小时并保持温度在100-150℃，得浆料；2)按配比称量石英颗粒，木质纤维素，硅藻土，一起放入混砂机中干混，混合2-3小时；3)再在混砂机中加入步骤1)的浆料和剩余的水，混合2-4小时后，出砂。
2.权利要求1所述的含有镁矿石尾渣的铸造型砂，其特征在于，所述粉状镁矿石尾渣粒度为80-100目。
CN201310524419.2A 2013-10-28 2013-10-28 一种含有镁矿石尾渣的铸造型砂 Pending CN103537612A (zh)