CN102213066A - 一种高阻燃木质防火门及其制备方法 - Google Patents
一种高阻燃木质防火门及其制备方法 Download PDFInfo
- Publication number
- CN102213066A CN102213066A CN2011100955076A CN201110095507A CN102213066A CN 102213066 A CN102213066 A CN 102213066A CN 2011100955076 A CN2011100955076 A CN 2011100955076A CN 201110095507 A CN201110095507 A CN 201110095507A CN 102213066 A CN102213066 A CN 102213066A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- wood
- flame
- door
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种高阻燃木质防火门及其制备方法，是将木质门置于微波加热的真空软化木材装置罐中，用高阻燃均三嗪磷酸酯阻燃剂真空浸渍，使阻燃剂充分浸渍入木质门的木质空隙中，其制成品大于国家甲级木质防火门的耐火极限标准，并且有低烟、无毒的功效，使用的阻燃剂可使防火门含有的高阻燃剂的高聚物受热时，表面能够生成一层均匀的阻燃层，起到隔热、隔氧、抑烟的作用，并具有良好的阻燃性能，能有效降低生产成本，改善木质防火门整体的阻燃防火功能，符合当今要求防火门低烟、无毒的发展趋势。
Description
技术领域
本发明涉及防火门的技术领域，尤指一种高阻燃木质防火门及其制备方法。
背景技术
防火门是指在一定时间内能满足耐火稳定性、完整性和隔热性要求的门。木质防火门是指木材或木材制品经阻燃处理制作门框，门扇骨架，门扇面板，是建筑物防火分隔的设施之一。通常用在室内外门洞、防火墙上、楼梯间出入口或管道井开口部位，火灾发生时可起到阻止火焰蔓延和防止燃烧烟气流动，对于减少火灾损失起着重要的作用，同时保证火灾发生时人员的安全撤离。随着现代高新科学技术的应用，防火门要求尽量减少材料热分解或燃烧时放出的烟和有毒气体，传统阻燃处理的木质防火门已经远远不能满足市场对其性能的需求了，如含卤系阻燃剂处理的木材在材料燃烧时放出大量的卤化氢气体，进而吸水形成具有强腐蚀性的氢卤酸而造成二次公害。现今木质防火门无卤呼声日益高涨，含卤系阻燃剂的传统防火门很难在21世纪得到较大发展。
目前，全球各发达国家都对高阻燃、低烟、低毒的木质防火门给予极大的重视，而国内市场上装修用防火门多数阻燃性能低，在阻燃防火时存在着高烟和排放有毒气体的缺陷，为此市场上急需一种高阻燃、低烟、低毒的防火门产品。
发明内容
本发明一种高阻燃木质防火门及其制备方法，其特征是将木质门置于微波加热的真空软化木材装置罐中，用高阻燃均三嗪磷酸酯阻燃剂真空加压浸渍，可使高阻燃均三嗪磷酸酯阻燃剂充分浸渍入木质门的木质空隙中，使木质门产生高效高阻燃、低烟、无毒功能，并具有良好的阻燃性能和受热稳定性，能有效降低生产成本，改善木质防火门整体的阻燃防火功能。
为了实现上述目的，本发明的技术解决方案为：三聚氯氰与双羟乙基胺反应，引入水溶性羟乙基氨基基团，其反应生成的含多羟乙基氨基化合物与硼酸进行酯化反应，再加入双羟乙基胺进行酯化反应并引入水溶性羟基，具体包含以下步骤：
第一步，在反应釜中以乙醇为溶剂，三聚氯氰(I)和双羟乙基胺在碱催化剂碳酸钠作用下于60℃～90℃下反应5～7h，生成化合物三(N，N-二羟乙基氨基)-均三嗪(II)：
其化学反应为：
三聚氯氰和双羟乙基胺的摩尔比为1∶3～3.2。
第二步，化合物(II)与含五氧化二磷、焦磷酸或多聚磷酸的其中的一种或多种在80℃～110℃温度下加热反应4～6h，生成三(N，N-二羟乙基氨基)-均三嗪磷酸酯阻燃剂化合物；
第三步，将合成的均三嗪磷酸酯阻燃剂化合物在搅拌槽中加入2倍纯水稀释搅拌30min，再置入微波加热真空软化木材罐中，将制作的木质防火门叠加摆放在微波加热真空软化木材罐中密封真空加压，微波加热升温至80～℃90℃，保温浸渍3h；
第四步，将木质防火门出罐控液，进入干燥窑中定形，在窑温60～℃80℃定型烘干24h，自然冷却常温出窑，粘贴阻燃外板、整形，使用均三嗪磷酸酯阻燃剂涂刷二遍，干燥后涂表漆即为成品。
本发明制作的防火门具有受热稳定性高和高阻燃性强的特点，其制成品大于国家甲级木质防火门的耐火极限标准，并且有低烟、无毒的功效，使用均三嗪磷酸酯阻燃剂可使防火门含有的高阻燃剂的高聚物受热时，表面能够生成一层均匀的阻燃层，起到隔热、隔氧、抑烟的作用，并具有良好的阻燃性能，能有效降低生产成本，改善木质防火门整体的阻燃防火功能，符合当今要求防火门低烟、无毒的发展趋势。
具体实施方法
a、在反应釜中以乙醇为溶剂，三聚氯氰(I)和双羟乙基胺在碱催化剂碳酸钠作用下于60℃～90℃下反应5～7h，生成化合物三(N，N-二羟乙基氨基)-均三嗪；
b、将化合物三(N，N-二羟乙基氨基)-均三嗪与含五氧化二磷、焦磷酸或多聚磷酸的其中的一种或多种在80℃～110℃温度下加热反应4～6h，生成三(N，N-二羟乙基氨基)-均三嗪磷酸酯阻燃剂化合物；
C、将合成的均三嗪磷酸酯阻燃剂化合物在搅拌槽中加入2倍纯水稀释搅拌30min，再置入微波加热真空软化木材罐中，将制作的木质防火门叠加摆放在微波加热真空软化木材罐中密封真空加压，微波加热升温至80～℃90℃，保温浸渍3h；
d、将木质防火门提出控液，进入干燥窑中定形，在窑温60～℃80℃定型烘干24h，出窑粘贴阻燃外板、整形，使用均三嗪磷酸酯阻燃剂涂刷二遍，干燥后涂覆表漆即为成品。
以上所述，实施方式仅仅是对本发明的优选实施方式进行描述，并非对本发明的范围进行限定，在不脱离本发明技术的精神的前提下，本领域工程技术人员对本发明的技术方案作出的各种变形和改进，均应落入本发明的权利要求书确定的保护范围内。
Claims (2)
1.一种高阻燃木质防火门及其制备方法，其特征是木质门置于微波加热的真空软化木材装置罐中，加入均三嗪磷酸酯阻燃剂真空加压升温至80～℃90℃，保温浸渍3h，在干燥窑温60～℃80℃定型烘干24h，出窑粘贴阻燃外板、整形，使用均三嗪磷酸酯阻燃剂涂刷二遍，干燥后涂覆表漆即为成品。
2.根据权利要求1所述的一种高阻燃木质防火门及其制备方法，其特征是均三嗪磷酸酯阻燃剂化合物在搅拌槽中加入2倍纯水稀释搅拌30min。