CN102212913A - 涤、天丝、苎麻混纺纱及其生产方法 - Google Patents
涤、天丝、苎麻混纺纱及其生产方法 Download PDFInfo
- Publication number
- CN102212913A CN102212913A CN2010101469117A CN201010146911A CN102212913A CN 102212913 A CN102212913 A CN 102212913A CN 2010101469117 A CN2010101469117 A CN 2010101469117A CN 201010146911 A CN201010146911 A CN 201010146911A CN 102212913 A CN102212913 A CN 102212913A
- Authority
- CN
- China
- Prior art keywords
- ramie
- terylene
- tencel
- fibers
- blended yarns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
涤、天丝、苎麻混纺纱,是涤纶、天丝和苎麻三种纤维混纺而成的纱线,细度60-80公支,颜色白色,其中涤纶、天丝、苎麻三者的重量比为35-45∶20-30∶30-40,单纱强力为180-210厘牛,捻度为700-800捻/米。这种涤、天丝、苎麻混纺纱的生产方法,先将涤纶、天丝和苎麻三种纤维分别预并→2-4次混并→粗纱→细纱→络筒。在本发明的产品中,苎麻纤维,挺括,刚性高,吸湿性好;天丝纤维柔软、色泽亮丽、吸湿性好,有丝的感觉,涤纶,吸湿性差,但是耐磨。本发明的涤、天丝、苎麻混纺纱利用了三种纤维各自的理化特点,使之条干均匀、色泽亮丽、柔软、耐磨。可生产高档面料,其服用性能比其它涤麻产品得以大大提高。
Description
【技术领域】本发明涉及纺织产品,即一种涤、天丝、苎麻混纺纱及其生产方法。
【背景技术】在纺织行业中,涤纶是经常使用的,苎麻也是经常使用的,而天丝是一种近年来新开发的纺织纤维,它是由一些天然的废弃物如木屑、甘蔗屑、麻杆、棉杆等加工再生而成,目前市场上还没有涤纶、天丝、苎麻这三种纤维混纺的纱,主要是天丝这种原料才刚刚问世,其可纺性较差。
【发明内容】为了充分利用天丝这种纤维的某些优点,生产高档面料,本发明提出了涤、天丝、苎麻混纺纱及其生产方法。
这种涤、天丝、苎麻混纺纱,是涤纶、天丝和苎麻三种纤维混纺而成的纱线,其特征在于,细度60-80公支,颜色白色,其中涤纶、天丝、苎麻三者的重量比为35-45∶20-30∶30-40,单纱强力为180-210厘牛,捻度为700-800捻/米。
这种涤、天丝、苎麻混纺纱的生产方法,其特征在于,工艺流程是:先将涤纶、天丝和苎麻三种纤维分别预并→2-4次混并→粗纱→细纱→络筒。
在本发明的产品中,苎麻纤维,挺括,刚性高,吸湿性好;天丝纤维柔软、色泽亮丽、吸湿性好,有丝的感觉,涤纶,吸湿性差,但是耐磨。本发明的涤、天丝、苎麻混纺纱利用了三种纤维各自的理化特点,相互取长补短,使之条干均匀、色泽亮丽、柔软、耐磨。可生产高档面料,其服用性能比其它涤麻产品得以大大提高。本发明的工艺简单,生产条件要求不高。
【具体实施方式】
下面举一实施例对本发明详细说明如下:
本实施例的涤、天丝、苎麻混纺纱,细度68公支,颜色白色,其中涤纶、天丝和苎麻的干重量比为40∶25∶35,单纱强力为190厘牛,捻度为760捻/米。
上述涤、天丝、苎麻混纺纱的生产方法,原料是2D×88涤纶、3D×88天丝和03号苎麻球。
Claims (2)
1.涤、天丝、苎麻混纺纱,是涤纶、天丝和苎麻三种纤维混纺而成的纱线,其特征在于,细度60-80公支,颜色白色,其中涤纶、天丝、苎麻三者的重量比为35-45∶20-30∶30-40,单纱强力为180-210厘牛,捻度为700-800捻/米。
2.涤、天丝、苎麻混纺纱的生产方法,其特征在于,工艺流程是:先将涤纶、天丝和苎麻三种纤维分别预并→2-4次混并→粗纱→细纱→络筒。