CN102212318A - 新型抗冻耐湿胶粘剂 - Google Patents
新型抗冻耐湿胶粘剂 Download PDFInfo
- Publication number
- CN102212318A CN102212318A CN2010101393033A CN201010139303A CN102212318A CN 102212318 A CN102212318 A CN 102212318A CN 2010101393033 A CN2010101393033 A CN 2010101393033A CN 201010139303 A CN201010139303 A CN 201010139303A CN 102212318 A CN102212318 A CN 102212318A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive agent
- novel anti
- moisture resistant
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水溶性胶粘剂，尤其是涉及一种新型抗冻耐湿胶粘剂。是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝15～25∶40～60∶22～35∶55～75∶5～10∶3～10。本发明配方科学、工艺简单，以性能优异的高分子材料及其它几种易购化工原料配制而成，彻底改变了传统白乳胶的用料，且耐水性、耐湿性和抗冻融性能较好，本发明耐冻融，耐老化，粘接强度优良，储存期长，且成本低廉，应用范围广泛。
Description
技术领域
本发明涉及一种水溶性胶粘剂，尤其是涉及一种新型抗冻耐湿胶粘剂。
背景技术
水溶性胶粘剂又称为白乳胶是目前用途最广，用量最大的粘合剂品种之一。传统白乳胶大多以醋酸乙烯，聚乙烯醇为主要原料，聚合工艺复杂，生产周期长(8-10小时)，产品造价成本高。耐水性和耐湿性差，易在潮湿空气中吸湿，在高温下使用会产生蠕变现象，使胶接强度下降；在-5℃以下储存易冻结，使乳液受到破坏。尤其在冬季低温条件下，常因粘度增高而导致胶凝，需加热之后才能使用，不仅给冬季施工带来许多不便。
发明内容
本发明针对上述现有技术中存在的问题，经优化配方设计，精心制造，提供了新型抗冻耐湿胶粘剂，解决了现有技术中耐水性和耐湿性差，易在潮湿空气中吸湿的问题，而且成本低，使用范围广泛，适合多种领域应用。
本发明的技术方案是：
新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝15～25∶40～60∶22～35∶55～75∶5～10∶3～10。
所述的新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝17～23∶45～55∶25～36∶63～70∶6～8∶5～9。
所述的新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝20∶50∶30∶65∶7∶6。
所述的新型抗冻耐湿胶粘剂的制备方法可采用常规的搅拌均匀、充分混合的生产方法即可。
本发明与现有技术相比具有如下的优点效果：
本发明配方科学、工艺简单，以性能优异的高分子材料及其它几种易购化工原料配制而成，彻底改变了传统白乳胶的用料，且耐水性、耐湿性和抗冻融性能较好，本发明耐冻融，耐老化，粘接强度优良，储存期长，且成本低廉，应用范围广泛。
具体实施方式
实施例1
新型抗冻耐湿胶粘剂，由下述原料按重量份数比制备而成：丁二苯乙烯乳液：乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝20∶50∶30∶65∶7∶6。
所述的新型抗冻耐湿胶粘剂的制备方法可采用常规的搅拌均匀、充分混合的生产方法即可。
实施例2
新型抗冻耐湿胶粘剂，由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝15∶60∶35∶75∶10∶10。其它同实施例1。
实施例3
新型抗冻耐湿胶粘剂，由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝25∶40∶22∶55∶5∶3。其它同实施例1。
实施例4
新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝17∶55∶36∶70∶8∶9。其它同实施例1。
实施例5
新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝23∶45∶25∶63∶6∶5。其它同实施例1。
Claims (3)
1.一种新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝15～25∶40～60∶22～35∶55～75∶5～10∶3～10。
2.根据权利要求1所述的新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝17～23∶45～55∶25～36∶63～70∶6～8∶5～9。
3.根据权利要求1所述的新型抗冻耐湿胶粘剂，其特征在于是由下述原料按重量份数比制备而成：丁二苯乙烯乳液∶乙酸乙烯酯∶萜烯树脂∶氯丁橡胶乳液∶水玻璃∶氧化锌＝20∶50∶30∶65∶7∶6。