CN103952098A - 一种抗冻乳胶 - Google Patents

一种抗冻乳胶 Download PDF

Info

Publication number
CN103952098A
CN103952098A CN201410212335.XA CN201410212335A CN103952098A CN 103952098 A CN103952098 A CN 103952098A CN 201410212335 A CN201410212335 A CN 201410212335A CN 103952098 A CN103952098 A CN 103952098A
Authority
CN
China
Prior art keywords
parts
water
polyvinyl alcohol
diatomite
formaldehyde
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410212335.XA
Other languages
English (en)
Inventor
刘晓萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410212335.XA priority Critical patent/CN103952098A/zh
Publication of CN103952098A publication Critical patent/CN103952098A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇80～100份、乙二醇5～8份、甲基纤维素8～10份、玉米淀粉20～50份、轻质碳酸钙5～10份、纳米防霉剂1～2份、甲醛1～3份、硅藻土4～6份、饮白粉5～8份、膨润土4～8份、尿素0.1～0.2份和水40～5份。本发明的抗水乳胶黏结强度高、成本低和抗冻效果好，且生产设备简单，工艺简易，生产周期短，干燥时间短，生产中无有害气体的排放。，原材料廉价易得，成本低。

Description

一种抗冻乳胶
技术领域
本发明涉及一种木材及建筑材料用的粘合剂，具体地涉及一种抗冻乳胶。
背景技术
目前广泛使用的木材及建筑材料粘合剂有两大类：一类是成本较低，但理化性能较差，产品粘度在3000CP以下，初粘时间长达10个小时至48小时，压缩剪切强3.9MPa以下，主要技术指标连国家二级标准也达不到。另一类是成本高，质量相对较好，最常见的为聚醋酸乙烯乳胶。由于此种白乳胶主要利用醋酸乙烯作为单体，以聚乙烯醇作保护胶体，通过一定的条件聚合制得，主要性能得到提高，所以质量有所提高。但醋酸乙烯单体、聚乙烯醇等原料较紧缺，价格不断高涨，引起成本过高，一般使用单位难以接受。而且生产工艺复杂，设备投资大，生产周期长，低温抗冻性差，给产品的应用带来不便。如何在降低成本的基础上提高粘合剂的抗冻性能成为研究热点。
发明内容
发明目的：为解决现有技术中存在的技术问题，本发明提出一种抗冻乳胶，具有低成本和抗冻效果好的特点。
技术内容：为实现上述技术目的，本发明提出一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇80～100份、乙二醇5～8份、甲基纤维素8～10份、玉米淀粉20～50份、轻质碳酸钙5～10份、纳米防霉剂1～2份、甲醛1～3份、硅藻土4～6份、饮白粉5～8份、膨润土4～8份、尿素0.1～0.2份和水40～50份。
优选地，所述抗冻乳胶包括如下重量份数的组分：聚乙烯醇90份、乙二醇7份、甲基纤维素9份、玉米淀粉40份、轻质碳酸钙8份、纳米防霉剂1.5份、甲醛2份、硅藻土5份、饮白粉7份、膨润土6份、尿素0.15份和水45份。
本发明还提出上述的抗冻乳胶的制备方法，包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，低速搅拌均匀，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续加速搅拌即得。
其中，低速搅拌的条件为：搅拌速度800～1000r/min，搅拌时间20～30min。
高速搅拌的条件为：搅拌速度2500～2800r/min，搅拌时间15～20min。。
有益效果：与现有技术相比，本发明的抗水乳胶黏结强度高、成本低和抗冻效果好，且生产设备简单，工艺简易，生产周期短，干燥时间短，生产中无有害气体的排放。，原材料廉价易得，成本低。
具体实施方式
实施例1
一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇90份、乙二醇7份、甲基纤维素9份、玉米淀粉40份、轻质碳酸钙8份、纳米防霉剂1.5份、甲醛2份、硅藻土5份、饮白粉7份、膨润土6份、尿素0.15份和水45份。
其制备方法包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，1000r/min下搅拌20min，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续2500r/min下搅拌20min即得。
实施例2
一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇80份、乙二醇8份、甲基纤维素8份、玉米淀粉50份、轻质碳酸钙5份、纳米防霉剂2份、甲醛1份、硅藻土6份、饮白粉5份、膨润土8份、尿素0.1份和水50份。
其制备方法包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，800r/min下搅拌30min，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续2800r/min下搅拌15min即得。
实施例3
一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇00份、乙二醇份、甲基纤维素10份、玉米淀粉20份、轻质碳酸钙10份、纳米防霉剂1份、甲醛3伤、硅藻土4份、饮白粉8份、膨润土4份、尿素0.2份和水40份。
其制备方法包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，900r/min下搅拌25min，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、铁白粉、膨润土和尿素，继续2600r/min下搅拌20min即得。
实施例4
一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇90份、乙二醇6份、甲基纤维素9份、玉米淀粉40份、轻质碳酸钙7份、纳米防霉剂1.6份、甲醛2.5份、硅藻土5.5份、饮白粉6份、膨润土7份、尿素0.18份和水48份。
其制备方法包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，800r/min下搅拌30min，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续2500r/min下搅拌15～20min即得。
实施例5
一种抗冻乳胶，包括如下重量份数的组分：聚乙烯醇85份、乙二醇7份、甲基纤维素8.5份、玉米淀粉45份、轻质碳酸钙9份、纳米防霉剂1.6份、甲醛2.4份、硅藻土4.5份、饮白粉6份、膨润土6份、尿素0.16份和水40份。
其制备方法包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，1000r/min下搅拌20，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续2800r/min下搅拌15min即得。

Claims (5)

1.一种抗冻乳胶，其特征在于，包括如下重量份数的组分：聚乙烯醇80～100份、乙二醇5～8份、甲基纤维素8～10份、玉米淀粉20～50份、轻质碳酸钙5～10份、纳米防霉剂1～2份、甲醛1～3份、硅藻土4～6份、饮白粉5～8份、膨润土4～8份、尿素0.1～0.2份和水40～50份。
2.根据权利要求1所述的抗冻乳胶，其特征在于，包括如下重量份数的组分：聚乙烯醇90份、乙二醇7份、甲基纤维素9份、玉米淀粉40份、轻质碳酸钙8份、纳米防霉剂1.5份、甲醛2份、硅藻土5份、饮白粉7份、膨润土6份、尿素0.15份和水45份。
3.权利要求1所述的抗冻乳胶的制备方法，其特征在于，包括如下步骤：
(1)称取配方量的聚乙烯醇、乙二醇、甲基纤维素、玉米淀粉和水，低速搅拌均匀，然后加入配方量的轻质碳酸钙、纳米防霉剂、甲醛、硅藻土、饮白粉、膨润土和尿素，继续加速搅拌即得。
4.根据权利要求3所述的方法，其特征在于，低速搅拌的条件为：搅拌速度800～1000r/min，搅拌时间20～30min。
5.根据权利要求3所述的方法，其特征在于，高速搅拌的条件为：搅拌速度2500～2800r/min，搅拌时间15～20min。
CN201410212335.XA 2014-05-19 2014-05-19 一种抗冻乳胶 Pending CN103952098A (zh)