CN102191531B - 一种不锈钢发黑剂 - Google Patents

一种不锈钢发黑剂 Download PDF

Info

Publication number
CN102191531B
CN102191531B CN 201110163150 CN201110163150A CN102191531B CN 102191531 B CN102191531 B CN 102191531B CN 201110163150 CN201110163150 CN 201110163150 CN 201110163150 A CN201110163150 A CN 201110163150A CN 102191531 B CN102191531 B CN 102191531B
Authority
CN
China
Prior art keywords
stainless steel
blackening agent
content
steel blackening
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110163150
Other languages
English (en)
Other versions
CN102191531A (zh
Inventor
郑崇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG BAIHE MEDICAL TECHNOLOGY CO., LTD.
Original Assignee
Foshan Aidi Medical Devices Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Aidi Medical Devices Co Ltd filed Critical Foshan Aidi Medical Devices Co Ltd
Priority to CN 201110163150 priority Critical patent/CN102191531B/zh
Publication of CN102191531A publication Critical patent/CN102191531A/zh
Application granted granted Critical
Publication of CN102191531B publication Critical patent/CN102191531B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种不锈钢发黑剂，包括硫酸钠、硝酸钠、草酸钠和稀土盐溶于去离子水形成的水溶液，其特征要于：所述硫酸钠的含量为20～40g/L，所述硝酸钠的含量为8～20g/L，所述草酸钠的含量为3～8g/L，所述稀土盐的含量为1～5g/L。具有发黑时间短，作用温度在常温下就能进行发黑；不含强酸、强碱等腐蚀性物质，PH中性，操作过程中对人体无任何不良影响。

Description

一种不锈钢发黑剂
技术领域
本发明涉及一种不锈钢发黑剂。
背景技术
随着人们需求的不断提高，其表面经氧化发黑后的不锈钢被广泛应用于电子工业、建筑装饰、厨房用具、仪器仪表、汽车工业、化工设备、标牌印刷及宇航军工等众多领域。不锈钢氧化发黑作为一种不锈钢着色技术开始受到人们的重视。
现有技术常用重铬酸钾和硫酸作为不锈钢的发黑剂，该发黑剂含有重铬酸钾，污染环境，而且需要加热，发黑时间要几分钟到十几分钟，用时较长。
发明内容
本发明要解决的技术问题是，提供一种对环境无污染、常温发黑和发黑时间较短的不锈钢发黑剂。
为解决上述问题，本发明的一种不锈钢发黑剂，包括硫酸钠、硝酸钠、草酸钠和稀土盐溶于去离子水形成的水溶液，所述硫酸钠的含量为20～40g/L，所述硝酸钠的含量为8～2g/L，所述草酸钠的含量为3～8g/L，所述稀土盐的含量为1～5g/L。
所述稀土盐为硫酸镧或硫酸铈。
本发明的使用方法是在常温条件下，将不锈钢工件与阳极相连，置于本发明的不锈钢发黑剂中，工作电压为10V，该不锈钢发黑剂在低电流和低电压(小于10V)的作用下，通过电化学反应，不锈钢表面发生氧化还原反应，在8～20秒钟之内在不锈钢表面形成一层很薄且牢固耐磨的发黑膜。且整个发黑过程不会对环境造成污染，符合环保要求。
本发明的技术原理是：其中硫酸钠主要起导电盐和提供阴阳离子，有利于整个发黑剂发黑的分散能力；硝酸钠主要起氧化和辅助成膜作用；草酸钠起络合剂作用，并起缓冲作用；硫酸镧起提高电流效率、降低电位和分散能力。
采用本发明的不锈钢发黑剂，发黑时间短，一般8-20秒就可以达到较好的效果；作用温度在常温下就能进行发黑；不含强酸、强碱等腐蚀性物质，PH中性，操作过程中对人体无任何不良影响。
具体实施方式
实施例1
1.发黑剂制备
分别称取硫酸钠20g，硝酸钠10g，草酸钠5g，硫酸镧3g溶于800mL去离子水中，并搅拌，待完全溶解后再加去离子水至1L，即得到本实施例的发黑剂。
2.发黑方法
将不锈钢工件除油并于超声波清洗烘干后，然后将其与阳极相连，置于上述制备好的发黑剂中，工作电压为10V，发黑时间为20秒，最后将工件进行超声波水洗并烘干得到发黑后的不锈钢工件，发黑效果好。
实施例2
1.发黑剂制备
分别称取硫酸钠25g，硝酸钠8g，草酸钠5g，硫酸铈2g溶于800mL去离子水中，并搅拌，待完全溶解后再加去离子水至1L，即得到本实施例的发黑剂。
2.发黑方法
将不锈钢工件除油并于超声波清洗烘干后，然后将其与阳极相连，置于上述制备好的发黑剂中，工作电压为8V，发黑时间为20秒，最后将工件进行超声波水洗并烘干得到发黑后的不锈钢工件，发黑效果好。
实施例3
1.发黑剂制备
分别称取硫酸钠40g，硝酸钠8g，草酸钠3g，硫酸镧5g溶于800mL去离子水中，并搅拌，待完全溶解后再加去离子水至1L，即得到本实施例的发黑剂。
2.发黑方法
将不锈钢工件除油并于超声波清洗烘干后，然后将其与阳极相连，置于上述制备好的发黑剂中，工作电压为7V，发黑时间为8秒，最后将工件进行超声波水洗并烘干得到发黑后的不锈钢工件，发黑效果较好。
实施例4
1.发黑剂制备
分别称取硫酸钠30g，硝酸钠15g，草酸钠5g，硫酸镧3g溶于800mL去离子水中，并搅拌，待完全溶解后再加去离子水至1L，即得到本实施例的发黑剂。
2.发黑方法
将不锈钢工件除油并于超声波清洗烘干后，然后将其与阳极相连，置于上述制备好的发黑剂中，工作电压为7V，发黑时间为15秒，最后将工件进行超声波水洗并烘干得到发黑后的不锈钢工件，发黑效果好。
实施例5
1.发黑剂制备
分别称取硫酸钠20g，硝酸钠20g，草酸钠8g，硫酸镧1g溶于800mL去离子水中，并搅拌，待完全溶解后再加去离子水至1L，即得到本实施例的发黑剂。
2.发黑方法
将不锈钢工件除油并于超声波清洗烘干后，然后将其与阳极相连，置于上述制备好的发黑剂中，工作电压为5V，发黑时间为18秒，最后将工件进行超声波水洗并烘干得到发黑后的不锈钢工件，发黑效果较好。

Claims (1)

1.一种不锈钢发黑剂，包括硫酸钠、硝酸钠、草酸钠和稀土盐溶于去离子水形成的水溶液，其特征在于：所述硫酸钠的含量为20~40g/L，所述硝酸钠的含量为8~20g/L，所述草酸钠的含量为3~8g/L，所述稀土盐的含量为1~5g/L，所述稀土盐为硫酸镧或硫酸铈。
CN 201110163150 2011-06-17 2011-06-17 一种不锈钢发黑剂 Active CN102191531B (zh)