CN102190959A - 一种释放远红外的内墙乳胶漆 - Google Patents
一种释放远红外的内墙乳胶漆 Download PDFInfo
- Publication number
- CN102190959A CN102190959A CN2011100547630A CN201110054763A CN102190959A CN 102190959 A CN102190959 A CN 102190959A CN 2011100547630 A CN2011100547630 A CN 2011100547630A CN 201110054763 A CN201110054763 A CN 201110054763A CN 102190959 A CN102190959 A CN 102190959A
- Authority
- CN
- China
- Prior art keywords
- agent
- far
- stirring
- speed
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保涂料，特别涉及可用于室内墙面、天花板及石膏板等表面装饰用，具有释放远红外线对人体具有一定保健作用、并且能净化室内空气的环保内墙涂料，其制备工艺如下：先在低速下依次加入分散剂、润湿剂、消泡剂、增稠剂、防霉防藻剂；在中速下依次加入钛白粉、PH调节剂、重钙、煅烧高岭土、远红外粉，麦饭石，玉石粉、负离子素；高速分散至细度小于50Ｕ；在低速下依次加入乳液、成膜助剂、防冻剂、防腐剂、消泡剂、流平剂及H2O,检测合格后过滤包装，制得具有释放红外线对人体具有一定保健作用、并且能净化空气的环保内墙涂料。
Description
技术领域
本发明涉及一种内墙涂料，特别涉及一种可广泛应用于室内墙壁、天花板、石膏板等表面装饰用，具有释放远红外线对人体具有一定保健作用、并且能净化空气的环保型内墙涂料。
背景技术
远红外线有较强的渗透力和辐射力，具有显著的温控效应和共振效应，它易被物体吸收并转化为物体的内能。远红外线被人体吸收后，可使体内水分子产生共振，使水分子活化，增强其分子间的结合力，从而活化蛋白质等生物大分子，使生物体细胞处于最高振动能级。由于生物细胞产生共振效应，可将远红外热能传递到人体皮下较深的部分，以下深层温度上升，产生的温热由内向外散发。这种作用强度，使毛细血管扩张，促进血液循环，强化各组织之间的新陈代谢，增加组织的再生能力，提高机体的免疫能力，调节精神的异常兴奋状态，从而起到医疗保健的作用。
发明内容
本发明的目的是提供一种具有释放远红外线、对人体具有一定保健作用并且净化室内空气的环保型内墙涂料。
本发明是采用如下的技术配方和工艺来实现上述目的，其使用的原材料及具体配比（按重量计%）如下：
H2O 10-35
分散剂 0.4-0.8
润湿剂 0.1-0.2
消泡剂 0.2-0.5
防霉防藻剂 0.2-1.0
增稠剂 0.3-0.6
钛白粉 8-30
PH调节剂 0.05-0.15
800目重钙 5-30
煅烧高岭土或水洗高岭土 5-15
远红外粉 0.5-2.5
麦饭石 3-5
玉石粉 2-10
负离子素 0.5-2.0
乳液 10-35
成膜助剂 0.5-2.5
防冻剂 0.5-2.5
防腐剂 0.1-0.4
流平剂 0.1-1.5。
所述的环保型涂料其特征在于该涂料的制备工艺如下：
(1)在小于500r/min的速度下，依次加入10-35％的H2O的全部总量的90％、0.4-0.8％的分散剂、0.1-0.2％的润湿剂、0.2-0.5％消泡剂全部总量的50％、0.2-1.0％的防霉防藻剂、0.3-0.6％的增稠剂混合搅拌均匀；
(2)在500r/min-1000r/min的速度下依次加入8-30％钛白粉、0.05-0.15％的PH调节剂、5-30％的800目重钙、5-15％煅烧高岭土或水洗高岭土、0.5-2.5％的远红外粉、0.5-2.0％负离子素、 3-5％麦饭石、2-10的玉石粉；
(3)在大于1000r/min的速度下，分散或砂磨至细度＜50μm；
(4)在小于500r/min的速度下，依次加入10-35％乳液、0.5-2.5％成膜助剂、0.5-2.5％防冻剂、0.1-0.4％防腐剂、0.1-1.5％的流平剂、0.2-0.5％的消泡剂的总量中剩余的50％、10-35％的水的总量中剩余的10％混合搅拌均匀。
采用上述配方与现有技术相比，有如下优点：
1)本发明所制涂料具有释放远红外线对人体具有一定保健作用并且净化室内空气等功能;
2)本发明所制涂料气味低，基本无味;
3)本发明所制涂料具有很好的物料性能，能满足室内装饰要求。
具体实施方式
本发明是采用合成树脂乳液为基料添加能释放远红外的远红外粉，麦饭石，及玉石粉，释放负离子、净化空气的负离子素，再精选其它环保助剂及颜填料配制而成的。该环保型内墙涂料具有释放远红外有一定保健作用，释放负离子、净化室内空气的作用，其配方组成（按重量计%）如下：
H2O 10-35
分散剂 0.4-0.8
润湿剂 0.1-0.2
消泡剂 0.2-0.5
防霉防藻剂 0.2-1.0
增稠剂 0.3-0.6
钛白粉 8-30
PH调节剂 0.05-0.15
800目重钙 5-30
煅烧高岭土或水洗高岭土 5-15
远红外粉 0.5-2.5
麦饭石 3-5
玉石粉 2-10
负离子素 0.5-2.0
乳液 10-35
成膜助剂 0.5-2.5
防冻剂 0.5-2.5
防腐剂 0.1-0.4
流平剂 0.1-1.5。
所述的环保型涂料其特征在于该涂料的制备工艺如下：
1) 在小于500r/min的速度下，依次加入10-35％的H2O的全部总量的90％、0.4-0.8％的分散剂、0.1-0.2％的润湿剂、0.2-0.5％消泡剂全部总量的50％、0.2-1.0％的防霉防藻剂、0.3-0.6％的增稠剂混合搅拌均匀；
2) 在500r/min-1000r/min的速度下依次加入8-30％钛白粉、0.05-0.15％的PH调节剂、5-30％的800目重钙、5-15％煅烧高岭土或水洗高岭土、0.5-2.5％的远红外粉、0.5-2.0％负离子素、 3-5％麦饭石、2-10的玉石粉；
3) 在大于1000r/min的速度下，分散或砂磨至细度＜50μm；
4) 在小于500r/min的速度下，依次加入10-35％乳液、0.5-2.5％成膜助剂、0.5-2.5％防冻剂、0.1-0.4％防腐剂、0.1-1.5％的流平剂、0.2-0.5％的消泡剂的总量中剩余的50％、10-35％的水的总量中剩余的10％混合搅拌均匀。
其中，实施例一的具体配比如下：
1) H2O 10
2) 分散剂 0.4
3) 润湿剂 0.1
4) 消泡剂 0.2
5) 防霉防藻剂 0.2
6) 增稠剂 0.3
7) 钛白粉 8
8) PH调节剂 0.15
9) 800目重钙 22.25
10) 煅烧高岭土或水洗高岭土 5
11) 远红外粉 2.5
12) 麦饭石 5
13) 玉石粉 2
14) 负离子素 2
15) 乳液 35
16) 成膜助剂 2.5
17) 防冻剂 2.5
18) 防腐剂 0.4
19) 流平剂 1.5。
实施例二的具体配比如下：
1) H2O 35
2) 分散剂 0.8
3) 润湿剂 0.2
4) 消泡剂 0.5
5) 防霉防藻剂 1
6) 增稠剂 0.6
7) 钛白粉 16.65
8) PH调节剂 0.05
9) 800目重钙 5
10) 煅烧高岭土或水洗高岭土 15
11) 远红外粉 0.5
12) 麦饭石 3
13) 玉石粉 10
14) 负离子素 0.5
15) 乳液 10
16) 成膜助剂 0.5
17) 防冻剂 0.5
18) 防腐剂 0.1
19) 流平剂 0.1。
实施例三的具体配比如下：
1) H2O 12
2) 分散剂 0.5
3) 润湿剂 0.15
4) 消泡剂 0.3
5) 防霉防藻剂 0.3
6) 增稠剂 0.5
7) 钛白粉 30
8) PH调节剂 0.1
9) 800目重钙 30
10) 煅烧高岭土或水洗高岭土 6
11) 远红外粉 0.6
12) 麦饭石 3.05
13) 玉石粉 3
14) 负离子素 0.6
15) 乳液 11
16) 成膜助剂 0.6
17) 防冻剂 0.7
18) 防腐剂 0.2
19) 流平剂 0.4。
其中，本发明的一个较佳实施例的配方如下（按重量计％）：
1) H2O 24.2
2) 分散剂 0.5
3) 润湿剂 0.1
4) 消泡剂 0.4
5) 防霉防藻剂 0.5
6) 增稠剂 0.4
7) 钛白粉 15
8) PH调节剂 0.1
9) 800目重钙 10
10) 煅烧高岭土或水洗高岭土 9
11) 远红外粉 2
12) 麦饭石 5
13) 玉石粉 8
14) 负离子素 1.0
15) 乳液 20
16) 成膜助剂 1.5
17) 防冻剂 2.0
18) 防腐剂 0.2
19) 流平剂 0.1。
Claims (2)
1.一种释放远红外的内墙乳胶漆，其特征在于：其使用的原材料及具体配方按重量百分比计如下：
H2O 10-35
分散剂 0.4-0.8
润湿剂 0.1-0.2
消泡剂 0.2-0.5
防霉防藻剂 0.2-1.0
增稠剂 0.3-0.6
钛白粉 8-30
PH调节剂 0.05-0.15
800目重钙 5-30
煅烧高岭土或水洗高岭土 5-15
远红外粉 0.5-2.5
麦饭石 3-5
玉石粉 2-10
负离子素 0.5-2.0
乳液 10-35
成膜助剂 0.5-2.5
防冻剂 0.5-2.5
防腐剂 0.1-0.4
流平剂 0.1-1.5。
2.根据权利要求1所述的一种释放远红外的内墙乳胶漆，其特征在于：该涂料的制备工艺如下：
1)在小于500r/min的速度下，依次加入10-35％的H2O的全部总量的90％、0.4-0.8％的分散剂、0.1-0.2％的润湿剂、0.2-0.5％消泡剂全部总量的50％、0.2-1.0％的防霉防藻剂、0.3-0.6％的增稠剂混合搅拌均匀；
2)在500r/min-1000r/min的速度下依次加入8-30％钛白粉、0.05-0.15％的PH调节剂、5-30％的800目重钙、5-15％煅烧高岭土或水洗高岭土、0.5-2.5％的远红外粉、0.5-2.0％负离子素、 3-5％麦饭石、2-10的玉石粉；
3)在大于1000r/min的速度下，分散或砂磨至细度＜50μm；
4)在小于500r/min的速度下，依次加入10-35％乳液、0.5-2.5％成膜助剂、0.5-2.5％防冻剂、0.1-0.4％防腐剂、0.1-1.5％的流平剂、0.2-0.5％的消泡剂的总量中剩余的50％、10-35％的水的总量中剩余的10％混合搅拌均匀。