CN102179983A - Bope蒸煮膜 - Google Patents
Bope蒸煮膜 Download PDFInfo
- Publication number
- CN102179983A CN102179983A CN2011100272977A CN201110027297A CN102179983A CN 102179983 A CN102179983 A CN 102179983A CN 2011100272977 A CN2011100272977 A CN 2011100272977A CN 201110027297 A CN201110027297 A CN 201110027297A CN 102179983 A CN102179983 A CN 102179983A
- Authority
- CN
- China
- Prior art keywords
- layer
- bope
- polyethylene
- hot sealing
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种蒸煮膜,用于熟食品的包装。BOPE蒸煮膜,其特征在于由防粘层、芯层、热封层热合成一体;芯层位于防粘层与热封层之间,防粘层、芯层、热封层的质量比为2∶3∶2;所述的防粘层1由聚乙烯和防粘剂混合后挤出而成,各原料所占质量百分数为:聚乙烯98%、防粘剂2%;所述的芯层2由聚乙烯和成核剂混合后挤出而成,各原料所占质量百分数为:聚乙烯99.9%、成核剂0.01%;所述的热封层3的材料为茂金属PE。该BOPE蒸煮膜适用蒸煮,无毒性、经济实用。
Description
技术领域
本发明涉及一种蒸煮膜,用于熟食品的包装。
背景技术
现有蒸煮膜由几种膜复合而成(如,CPP和PET由胶复合成蒸煮膜),复合过程中有残留的苯,有毒性。
发明内容
本发明的目的在于提供一种适用蒸煮的BOPE蒸煮膜。
为了实现上述目的,本发明所采用技术方案是:BOPE蒸煮膜,其特征在于它由防粘层、芯层、热封层热合成一体(热合温度160~220℃);芯层位于防粘层与热封层之间,防粘层、芯层、热封层的质量比为2∶3∶2;
所述的防粘层由聚乙烯(PE)和防粘剂混合后挤出而成,各原料所占质量百分数为:聚乙烯(PE)98%、防粘剂2%;所述的芯层由聚乙烯(PE)和成核剂混合后挤出而成,各原料所占质量百分数为:聚乙烯(PE)99.9%、成核剂0.01%;所述的热封层的材料为茂金属PE(茂金属聚乙烯)。
所述防粘剂为SiO2。成核剂为现有产品(如深圳市骏德化工有限公司的PE成核剂),现有产品均可使用。
上述BOPE蒸煮膜的制备:1)防粘层:按上述防粘层的配比选取原料,混合得到混合料,混合料送入双螺杆挤出机挤出(挤出温度为160~220℃),得到防粘层;2)芯层:按上述芯层的配比选取原料,混合得到混合料,混合料送入双螺杆挤出机挤出(挤出温度为160~220℃),得到芯层;3)热封层:茂金属PE送入双螺杆挤出机挤出(挤出温度为160~220℃),得到热封层;4)将防粘层、芯层、热封层送入挤出复合机挤出热合成一体(热合温度160~220℃),得到BOPE蒸煮膜。
本发明的有益效果是:该BOPE蒸煮膜适用蒸煮,无毒性、经济实用。
附图说明
图1为本发明的结构示意图。
图中:1-防粘层,2-芯层,3-热封层。
具体实施方式
为了更好地理解本发明,下面结合实施例进一步阐明本发明的内容,但本发明的内容不仅仅局限于下面的实施例。
实施例1:
如图1所示,BOPE蒸煮膜,它由防粘层1、芯层2、热封层3热合成一体(热合温度160~220℃);芯层2位于防粘层1与热封层3之间,防粘层1、芯层2、热封层3的质量比为2∶3∶2;
所述的防粘层1由聚乙烯(PE)和防粘剂混合后挤出而成,各原料所占质量百分数为:聚乙烯(PE)98%、防粘剂2%;所述的芯层2由聚乙烯(PE)和成核剂混合后挤出而成,各原料所占质量百分数为:聚乙烯(PE)99.9%、成核剂0.01%;所述的热封层3的材料为茂金属PE(茂金属聚乙烯)。
所述防粘剂为SiO2。成核剂为现有产品(如深圳市骏德化工有限公司的PE成核剂),现有产品均可使用。
上述BOPE蒸煮膜的制备:1)防粘层:按上述防粘层的配比选取原料,混合得到混合料,混合料送入双螺杆挤出机挤出(挤出温度为160~220℃),得到防粘层;2)芯层:按上述芯层的配比选取原料,混合得到混合料,混合料送入双螺杆挤出机挤出(挤出温度为160~220℃),得到芯层;3)热封层:茂金属PE送入双螺杆挤出机挤出(挤出温度为160~220℃),得到热封层;4)将防粘层1、芯层2、热封层3送入挤出复合机挤出热合成一体(热合温度160~220℃),得到BOPE蒸煮膜。
用BOPE蒸煮膜装熟食品蒸煮10分钟,四周密封不脱层,不散开,说明适用蒸煮。BOPE蒸煮膜无毒性、经济实用。
Claims (2)
1.BOPE蒸煮膜,其特征在于由防粘层、芯层、热封层热合成一体;芯层位于防粘层与热封层之间,防粘层、芯层、热封层的质量比为2∶3∶2;
所述的防粘层1由聚乙烯和防粘剂混合后挤出而成,各原料所占质量百分数为:聚乙烯98%、防粘剂2%;所述的芯层2由聚乙烯和成核剂混合后挤出而成,各原料所占质量百分数为:聚乙烯99.9%、成核剂0.01%;所述的热封层3的材料为茂金属PE。
2.根据权利要求1所述的BOPE蒸煮膜,其特征在于:所述防粘剂为SiO2。