CN102173618A - 一种生产白水泥的方法 - Google Patents

一种生产白水泥的方法 Download PDF

Info

Publication number
CN102173618A
CN102173618A CN 201110054811 CN201110054811A CN102173618A CN 102173618 A CN102173618 A CN 102173618A CN 201110054811 CN201110054811 CN 201110054811 CN 201110054811 A CN201110054811 A CN 201110054811A CN 102173618 A CN102173618 A CN 102173618A
Authority
CN
China
Prior art keywords
white cement
kaolin
calcining
preparation
grinding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110054811
Other languages
English (en)
Other versions
CN102173618B (zh
Inventor
王波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yantai University
Original Assignee
Yantai University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yantai University filed Critical Yantai University
Priority to CN 201110054811 priority Critical patent/CN102173618B/zh
Publication of CN102173618A publication Critical patent/CN102173618A/zh
Application granted granted Critical
Publication of CN102173618B publication Critical patent/CN102173618B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用贝壳替代石灰石低温制备白水泥的方法。白水泥配方及重量百分含量是混合材80-90％，熟料10-20％。混合材制备方法是将贝壳、高岭土、天然石膏制备细粉。高温炉分别煅烧，按比例5∶3∶2混合均匀。熟料制备方法是85％贝壳粉与15％高岭土粉均匀混合，在1350℃煅烧，冷水漂白1min。优点：贝壳制备白水泥，煅烧温度低，利废、节能，产品健康、生态，符合建材工业可持续发展原则，具有广阔的市场前景。

Description

一种生产白水泥的方法
技术领域
本发明属于利用废弃物生产建筑材料新技术，具体涉及一种白水泥的配方和制备方法。
背景技术
沿海地区具有丰富的贝壳类资源，贝壳利用率很低，大部分作为垃圾处理或堆积海边，少部分作为饲料或制作装饰品。贝壳属于轻质碳酸钙，含钙量高、易磨性好，以其为原料代替天然石灰石烧制水泥和混合材等方面使用，具有广泛的发展前景。
白色水泥在装饰装修中应用量大，普通白色水泥烧制温度高，成本高。针对目前白水泥生产工艺的不足，本发明提出了一种新的节能白水泥生产工艺。
发明内容
本发明的目的是解决白水泥生产中石灰石原料替代问题，用海洋可再生资源贝壳与高岭土配料低温制备白水泥。
具体实施方式：
1、白水泥配方组成及重量百分含量：
混合材        80-90％
白水泥熟料    10-20％。
强度性能指标：
水泥胶砂强度3d抗压强度33MPa，28d抗压强度53MPa。
2、混合材制备步骤：
步骤1.粉料制备。贝壳清理砂土、杂质，破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％。高岭土、天然石膏分别破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％。
步骤2.高温煅烧。贝壳粉高温炉煅烧950℃，保温时间1h；高岭土粉煅烧850℃，保温时间40min；天然石膏粉煅烧750℃，保温时间1h。
步骤3.配料混合。将煅烧好的物料按配比5∶3∶2比例混合均匀形成混合材。
3、白水泥熟料制备步骤：
步骤1.将去砂贝壳和高岭土分别破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％。
步骤2.将85％贝壳粉与15％高岭土粉混合均匀，添加10％水压成直径10mm、厚度3mm生料饼，105℃下烘干至恒重。干燥后的生料饼在1350℃煅烧，保温40min。
步骤3.取出熟料立即在水里漂白1min，冷却室温。破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％。
4、贝壳原料组成：
可以是扇贝、牡蛎、白蛤蜊壳其中一种或是混合物，都可以作为石灰石替代原料。
本发明的优点：
本发明采用贝壳制备白水泥，煅烧温度低，利废、节能，产品健康、生态，符合建材工业可持续发展原则。

Claims (3)

1.一种生产白水泥的方法，其特征在于配方组成及重量百分含量：
混合材        80-90％
白水泥熟料    10-20％。
2.根据权利要求1所述的生产白水泥方法，其特征在于混合材制备方法为：
步骤1.将贝壳、高岭土、天然石膏分别破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％；
步骤2.贝壳粉在950℃煅烧保温1h；高岭土粉850℃煅烧保温40min；天然石膏粉750℃煅烧保温1h；
步骤3.上述煅烧好的物料按配比5∶3∶2比例混合形成混合材。
3.根据权利要求1所述的生产白水泥方法，其特征在于熟料制备方法为：
步骤1.将贝壳和高岭土分别粉磨，制备细粉，细度控制0.08mm方孔筛筛余＜10％；
步骤2.将85％贝壳粉与15％高岭土混合均匀压制成生料饼烘干，在1350℃煅烧，保温40min；
步骤3.取出熟料迅速在水里漂白1min，冷却室温，破碎、粉磨，细度控制0.08mm方孔筛筛余＜10％。
CN 201110054811 2011-03-09 2011-03-09 一种生产白水泥的方法 Expired - Fee Related CN102173618B (zh)