CN102161293B - Artistic glass bottle and production technology thereof - Google Patents
Artistic glass bottle and production technology thereof Download PDFInfo
- Publication number
- CN102161293B CN102161293B CN2010106107339A CN201010610733A CN102161293B CN 102161293 B CN102161293 B CN 102161293B CN 2010106107339 A CN2010106107339 A CN 2010106107339A CN 201010610733 A CN201010610733 A CN 201010610733A CN 102161293 B CN102161293 B CN 102161293B
- Authority
- CN
- China
- Prior art keywords
- glass
- clear glass
- glass bottle
- bottle
- bladder layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an artistic glass bottle and production technology thereof, wherein the artistic glass bottle comprises a transparent inner liner layer and a transparent glass outer layer; the part between the transparent glass inner liner layer and the transparent glass outer layer is partly or completely provided with an interlayer; the interlayer is a pattern layer; the production technology comprises steps of: fusing glass raw materials, manufacturing a transparent blank, making patterns by pigments, covering the transparent outer layer on the transparent blank to manufacture an artistic glass bottle blank, forming and annealing; the artistic glass bottle is more beautiful; by using the production technology of the artistic glass bottle, the problem of pattern distortion is solved; and the patterns are not worn.
Description
Technical field
The invention belongs to glassware manufacturing technology field, particularly the art glass bottle is made this technical field.
Background technology
Generally be to draw then on the vial surface that sintering forms for the pattern of art glass bottle at present, this pattern is distortion easily in sintering process, and easy abrasion comes off in some cases, and product is not attractive in appearance.
Summary of the invention
Deficiency to prior art; The technical problem that the present invention will solve provides a kind of art glass bottle and production technology thereof; This art glass bottle is more attractive in appearance; The production technology of this art glass bottle has solved the problem of pattern distortion, and there is not the problem that is worn in pattern, and the product that utilizes this production technology to produce is more attractive in appearance.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is:
A kind of art glass bottle is made up of clear glass bladder layer and clear glass skin, partly or entirely is provided with interlayer between said clear glass bladder layer and the clear glass skin, and said interlayer is the pattern layer.Because the pattern layer is arranged between bladder layer clear glass and the clear glass skin, therefore can distortion in sintering process, can not wear and tear in the use comes off, and product is more attractive in appearance, and third dimension is strong.
A kind of production technology of art glass bottle may further comprise the steps:
A, glass raw material is added fusion in the crucible, melt temperature 1000-1500 ℃;
B, make transparent idiosome, do pattern at transparent idiosome external application pigment then, put into oven again and be heated to 1000-1500 ℃ with melting charge;
C, outer at transparent idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, annealing temperature 500-600 ℃;
Melt temperature is according to the difference of glass raw material and different in the steps A; General melt temperature is good at 1200-1300 ℃; Pigment described in the step B can all cover the idiosome outer surface according to the needs of pattern or part covers the idiosome outer surface, can be the glass of versicolor fusing, cold glass blocks, cold glass dust, in the metal oxide one or more according to the needs of the color of pattern.
Description of drawings
Fig. 1 is an art glass bottle sketch map
Among the figure: 1, clear glass is outer; 2, pattern layer; 3, clear glass bladder layer
Fig. 2 is an art glass bottle wall cutaway view
1, clear glass is outer; 2, pattern layer; 3, clear glass bladder layer
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is done and to further describe.
A kind of art glass bottle is made up of clear glass bladder layer and clear glass skin, is provided with interlayer between said clear glass bladder layer and the clear glass skin, and said interlayer is the pattern layer.
A kind of production technology of art glass bottle may further comprise the steps:
A, glass raw material is added fusion in the crucible, 1100 ℃ of melt temperatures;
B, make transparent idiosome, do pattern at the glass of the colored fusing of transparent idiosome external application then, put into oven again and be heated to 1100 ℃ with melting charge;
C, outer at transparent idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, 510 ℃ of annealing temperatures.
A kind of art glass bottle is made up of clear glass bladder layer and clear glass skin, is provided with interlayer between said clear glass bladder layer and the clear glass skin, and said interlayer is the pattern layer.
A kind of production technology of art glass bottle may further comprise the steps:
A, glass raw material is added fusion in the crucible, 1250 ℃ of melt temperatures;
B, make transparent idiosome, do pattern at the colored cold glass blocks of transparent idiosome external application, cold glass dust then, put into oven again and be heated to 1250 ℃ with melting charge;
C, outer at transparent idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, 580 ℃ of annealing temperatures.
A kind of art glass bottle is made up of clear glass bladder layer and clear glass skin, is provided with interlayer between said clear glass bladder layer and the clear glass skin, and said interlayer is the pattern layer.
A kind of production technology of art glass bottle may further comprise the steps:
A, glass raw material is added fusion in the crucible, 1450 ℃ of melt temperatures;
B, make transparent idiosome, do pattern at the colored cold glass dust of transparent idiosome external application, metal oxide then, put into oven again and be heated to 1450 ℃ with melting charge;
C, outer at transparent idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, 550 ℃ of annealing temperatures.
Claims (2)
1. an art glass bottle is made up of clear glass bladder layer and clear glass skin, it is characterized in that partly or entirely be provided with interlayer between said clear glass bladder layer and the clear glass skin, said interlayer is the pattern layer; Said art glass bottle is made by following production technology:
A, glass raw material is added fusion in the crucible, melt temperature 1000-1500 ℃;
B, make clear glass bladder layer idiosome, do pattern at clear glass bladder layer idiosome external application pigment then, put into oven again and be heated to 1000-1500 ℃ with melting charge;
C, outer at clear glass bladder layer idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, annealing temperature 500-600 ℃.
2. the production technology of an art glass bottle is characterized in that may further comprise the steps:
A, glass raw material is added fusion in the crucible, melt temperature 1000-1500 ℃;
B, make clear glass bladder layer idiosome, do pattern at clear glass bladder layer idiosome external application pigment then, put into oven again and be heated to 1000-1500 ℃ with melting charge;
C, outer at clear glass bladder layer idiosome overcoat clear glass processes art glass bottle blank;
D, art glass bottle blank is put into mould, utilize a mouthful blowing technology to make the bottle moulding;
E, put into annealing kiln annealing after, kiln discharge, annealing temperature 500-600 ℃;
Said art glass bottle is made up of clear glass bladder layer and clear glass skin, partly or entirely is provided with interlayer between said clear glass bladder layer and the clear glass skin, and said interlayer is the pattern layer.