CN102154649A - 医用NiTi形状记忆合金抛光液 - Google Patents
医用NiTi形状记忆合金抛光液 Download PDFInfo
- Publication number
- CN102154649A CN102154649A CN 201110080101 CN201110080101A CN102154649A CN 102154649 A CN102154649 A CN 102154649A CN 201110080101 CN201110080101 CN 201110080101 CN 201110080101 A CN201110080101 A CN 201110080101A CN 102154649 A CN102154649 A CN 102154649A
- Authority
- CN
- China
- Prior art keywords
- grams
- shape memory
- polishing
- polishing solution
- memory alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种医用NiTi形状记忆合金抛光液,属于金属材料抛光液;旨在提供一种配制工艺简单、失重少、抛光效率高的钛合金抛光液。它是以氢氟酸和硝酸为基液,加入氧化剂、添加剂和水配制而成;每升抛光液中含浓氢氟酸250~350克、浓硝酸300~400克、氧化剂250~350克、添加剂70~150克,氧化剂为H2O2、添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。本发明不仅具有配制工艺简单、失重少、抛光效率高等优点,而且能够明显提高NiTi形状记忆合金表面光洁度和耐腐蚀性能;是一种可替代电化学抛光方法对形状复杂的医用NiTi形状记忆合金表面进行抛光处理或精细加工的理想溶液。
Description
技术领域:本发明涉及一种金属材料抛光液,尤其涉及一种钛合金抛光液。
背景技术:NiTi合金因不仅具有形状记忆效应和超弹性特殊性能,而且还具有优良的力学性能、抗疲劳、耐腐蚀性、高阻尼、无磁性和良好的生物相容性等特点;是一种公认为继316L不锈钢和Ti6Al4V之后的良好生物医用金属材料。作为医用金属材料必须对其表面进行抛光加工,使其表面光洁度达到一定的要求。目前,传统的机械抛光方法不仅效率低,而且很难满足医用合金材料形状复杂的要求;而电化学抛光方法又容易在医用合金材料表面产生尖端放电而导致过度腐蚀的缺陷。
发明内容:针对现有技术中存在的上述缺陷,本发明旨在提供一种配制工艺简单、失重少、抛光效率高的医用NiTi形状记忆合金抛光液。
为了实现上述目的,本发明采用以下技术方案,它是以氢氟酸和硝酸为基液,加入氧化剂、添加剂和水配制而成;其中,每升抛光液中含浓氢氟酸250~350克、浓硝酸300~400克、氧化剂250~350克、添加剂70~150克,所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
本发明的优选技术方案为:每升抛光液中含浓氢氟酸300克、浓硝酸350克、氧化剂300克、添加剂110克。
与现有技术比较,本发明不仅具有配制工艺简单、失重少、抛光效率高等优点,而且能够明显提高NiTi形状记忆合金表面光洁度和耐腐蚀性能,可用于对形状复杂的医用NiTi形状记忆合金表面进行抛光处理或精细加工。
具体实施方式:下面结合具体的实施例对本发明作进一步说明:
实施例1
取浓氢氟酸250克、浓硝酸300克、氧化剂250克、添加剂70克混合均匀,加水配制成1000毫升溶液;所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
实施例2
取浓氢氟酸350克、浓硝酸400克、氧化剂350克、添加剂150克混合均匀,加水配制成1000毫升溶液;所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
实施例3
取浓氢氟酸250克、浓硝酸400克、氧化剂250克、添加剂150克混合均匀,加水配制成1000毫升溶液;所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
实施例4
取浓氢氟酸350克、浓硝酸300克、氧化剂350克、添加剂70克混合均匀,加水配制成1000毫升溶液;所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
实施例5
取浓氢氟酸300克、浓硝酸350克、氧化剂300克、添加剂110混合均匀,加水配制成1000毫升溶液;所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
抛光时,将医用NiTi形状记忆合金试样置于丙酮溶液中超声波清洗15分钟后取出,用无水乙醇擦拭干净;然后置于5~100℃的本发明抛光液中,转速为150~300转/秒的搅拌器搅拌10~90秒钟取出,清水冲洗干净即可。
Claims (2)
1.一种医用NiTi形状记忆合金抛光液,其特征在于:是以氢氟酸和硝酸为基液,加入氧化剂、添加剂和水配制而成;其中,每升抛光液中含浓氢氟酸250~350克、浓硝酸300~400克、氧化剂250~350克、添加剂70~150克,所述氧化剂为H2O2、所述添加剂由乙二醇和酒石酸按10∶1的质量比配制而成。
2.根据权利要求1所述的医用NiTi形状记忆合金抛光液,其特征在于:每升抛光液中含浓氢氟酸300克、浓硝酸350克、氧化剂300克、添加剂110克。