CN102115325A - 一种负温度系数钛酸锶基的高压陶瓷电容器材料 - Google Patents
一种负温度系数钛酸锶基的高压陶瓷电容器材料 Download PDFInfo
- Publication number
- CN102115325A CN102115325A CN2010106031306A CN201010603130A CN102115325A CN 102115325 A CN102115325 A CN 102115325A CN 2010106031306 A CN2010106031306 A CN 2010106031306A CN 201010603130 A CN201010603130 A CN 201010603130A CN 102115325 A CN102115325 A CN 102115325A
- Authority
- CN
- China
- Prior art keywords
- titanate
- strontium titanate
- temperature coefficient
- capacitor material
- negative temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种负温度系数钛酸锶基的高压陶瓷电容器材料,由钛酸锶SrTiO380~84%,钛酸钙BiTiO38-10%、钛酸铋CaTiO31.5-3%、钛酸镁MgTiO310.5-13%组成的高压陶瓷电容器材料,采用本配方,就可以将电容的工作范围拓展到-65度~65度,有更好的抗低温特性。
Description
技术领域
本发明涉及一种电容材料,尤其是高压陶瓷电容材料。
背景技术
目前的高压电容多数是-30度~65度的工作温度范围,但在极地或者太空的环境中就不能满足使用。
发明内容
本发明的目的提供一种耐低温强的高压陶瓷电容材料。
一种负温度系数钛酸锶基的高压陶瓷电容器材料,其特征在于由钛酸锶SrTiO380~84%,钛酸钙BiTiO38-10%、钛酸铋CaTiO31.5-3%、钛酸镁MgTiO310.5-13%组成的高压陶瓷电容器材料。
采用本配方,就可以将电容的工作范围拓展到-65度~85度,有更好的抗低温特性。
具体实施方式
在配比时,我们首先将碳酸锶SrCO3和二氧化钛TiO2、碳酸钙CaCO3和二氧化钛TiO2按照一定配比,经过球磨混合,进行干燥,然后在1000到1200摄氏度合成得到钛酸锶钛酸钙CaTiO3;在得到钛酸锶钛酸钙CaTiO3后,上述其余材料等按照配比搅拌球磨混合,用少量丙酮稀释,高速搅拌(7000r/min)20min,使无机材料充分分散,加入8%的聚乙烯醇进行喷雾造粒,然后置于130℃烘箱中1h,就可以得到本配方的电介质,其介电常数为2600,介质损耗小于0.0005,耐压强度大于16KV/mm,温度特性在-40,电容量变化不大于25%,在85度不小于-25%,且呈线性变化的高性能负温度系数陶瓷材料。
Claims (3)
1.一种负温度系数钛酸锶基的高压陶瓷电容器材料,其特征在于由钛酸锶SrTiO380~84%,钛酸钙BiTiO38-10%、钛酸铋CaTiO31.5-3%、钛酸镁MgTiO310.5-13%组成的高压陶瓷电容器材料。