CN102101771B - Golden stone mud ceramics and preparation method thereof - Google Patents
Golden stone mud ceramics and preparation method thereof Download PDFInfo
- Publication number
- CN102101771B CN102101771B CN200910248587A CN200910248587A CN102101771B CN 102101771 B CN102101771 B CN 102101771B CN 200910248587 A CN200910248587 A CN 200910248587A CN 200910248587 A CN200910248587 A CN 200910248587A CN 102101771 B CN102101771 B CN 102101771B
- Authority
- CN
- China
- Prior art keywords
- mud
- stone mud
- metal
- stone
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to golden stone mud ceramics produced by utilizing the mud of a golden stone beach area of the Dalian development zone of Liaoning province and a preparation method thereof. In the preparation method, the soil, namely the golden stone mud of the golden stone beach area of the Dalian development zone of Liaoning province is used as a raw material, and the corrosion time of raw materials is six years; in the pulping process, the weight ratio of mud to water is equal to 6:4, and the mixture is continuously stirred for 72 hours by using a pulping machine; the granularity of a screen in the screening process is 60 meshes; glaze contains quartz powder, feldspar powder, clay powder and quick lime; smokeless kiln calcination is adopted in the calcining process, the temperature is controlled to gradually rise from normal temperature to 1,180 DEG C in 9 hours, and heating is stopped; and after the glaze is cooled for 9 hours, the kiln is opened. The method disclosed by the invention for producing the olden stone mud ceramics utilizes local resources and has the advantages of easy raw material source, freight saving, low cost and high production benefit; the texture of the glazing refined ceramics prepared by the golden stone mud is close to that of red enameled ceramics; and the golden stone mud ceramics have local characteristics and add a new species for developing tourism products of the Dalian zone.
Description
What technical field the present invention relates to is to utilize the geographic earth of development area, Dalian Pebble Beach Resort, produces metal and stone mud pottery and making method.
Background technology is before the present invention, and the area, Dalian is the local earth system fine pottery of human never, if system fine pottery, used potter's clay all ship outside other is local, will spend a lot of freight charges like this, the production cost height, and product can not be represented local characteristic.
Summary of the invention is for solving no marks property native country, area, Dalian travelling products and the native problem of using of not having the system fine pottery; Reduce the outer potter's clay institute trouble caused of buying, reduce the production cost of ceramic, the inventor is through research for many years; Experiment repeatedly is for the invention provides metal and stone mud pottery and preparation method.Comprised heavy corruption in the making method of metal and stone mud of the present invention pottery, pulled an oar, sieved, pugging, moulding, rest, technological process such as fired; And adopt the geographic earth of development area, Dalian Pebble Beach Resort, promptly " metal and stone mud " be raw material; In its heavy rotten technology, the heavy rotten time of " metal and stone mud " raw material is 6 years; In beating process, add water in the pug after through heavy rotten 6 years by weight pug: water=6: 4 added the stirring that do not stop with hollander behind the water 72 hours; Screen cloth in the process of sieving is 60 orders; In the rest technology, contain 40% silica powder, 40% Feldspar Powder, 10% clay powder and 10% unslaked lime in the glaze, glaze adds water mixing furnishing glaze slip again, glaze in the glaze slip: water=4: 6; In the sintering technology, fire with smokeless wood kiln in the sintering procedure, temperature is controlled in 9 hours and rises to 1180 ℃ gradually by normal temperature, stops heating then, cools off and opens kiln after 9 hours.Produce metal and stone mud pottery with the inventive method, utilized the geographic local resources in Dalian, raw material sources are easy; Saved trucking costs; Reduced production cost of products, improved productivity effect, the pottery art rest elaboration quality of producing with " metal and stone mud " approaches the boccaro goods; Has local characteristic, for the geographic travelling products in exploitation Dalian have increased new kind.
Embodiment is for to have further understanding to metal and stone mud pottery of the present invention and making method, and details are as follows in conjunction with embodiments of the invention:
Embodiment, metal and stone mud pottery and making method
The making method of metal and stone mud pottery is in the present embodiment; Adopt the geographic earth of development area, Dalian Pebble Beach Resort, promptly " metal and stone mud " be raw material; Make by following process step: 1, heavy rotten technology: " metal and stone mud " raw material that will fetch is put into cement pit or cylinder, adds water then and is as the criterion to flood the mud face, after water evaporation mud face becomes dry, add water logging again and do not have the mud face; Carry out so repeatedly, the heavy rotten time of " metal and stone mud " raw material is 6 years; 2, beating process: be to add water in the pug after through heavy rotten 6 years, by weight pug: water=6: 4, promptly in 100 kilograms of pugs, add 67 kilograms water, the stirring that does not stop with hollander then 72 hours, making beating finishes; 3, the technology of sieving: be with 60 purpose screen clothes with the filtering slurry of accomplishing fluently in the beating process, remove bits, stay mud, it is 30% clod that the mud natural air drying after will filtering then becomes moisture; 4, pugging technology: be that the moisture pugging method that is 30% clod is stepped on artificial pin of air-dry one-tenth is stepped on into mud cake with clod; 5, moulding process: be the greenwave of using the manual kneading of the mud cake of treading or being drawn into different shape, natural air drying after the greenwave moulding; 6, rest technology; Contain 40% above silica powder of 100 orders, 40% Feldspar Powder, 10% clay powder and 10% unslaked lime in the glaze, glaze adds water mixing furnishing glaze slip again, glaze in the glaze slip: water=4: 6; Promptly get the water that 40 kilograms of glaze of working good add 60 kilograms; Again air-dry good greenwave is put into glaze slip and dip in, let glaze slip overwork the greenwave surface, will hang glazed greenwave natural air drying again; 7, sintering technology: the air-dry good greenwave of rest is put into kiln, fire with smokeless wood kiln, temperature is controlled in 9 hours and rises to 1180 ℃ gradually by normal temperature, stops heating then, cools off and opens kiln after 9 hours.Metal and stone mud pottery among the present invention; Be adopt the geographic earth of development area, Dalian Pebble Beach Resort, promptly " metal and stone mud " be raw material, through above-mentioned heavy corruption, pull an oar, sieve, pugging, moulding, rest and the metal and stone mud ceramic product that the technological process making is produced such as fire.
Claims (4)
1. the making method of metal and stone mud pottery; It has comprised heavy corruption, pull an oar, sieve, pugging, moulding, rest, sintering technology process; It is characterized in that adopting the geographic earth of development area, Dalian Pebble Beach Resort, promptly " metal and stone mud " for raw material; In its heavy rotten technology, the heavy rotten time of " metal and stone mud " raw material is 6 years; In the beating process, add water in the pug after through heavy rotten 6 years, by weight pug: water=6: 4 added the stirring that do not stop with hollander behind the water 72 hours; Used screen cloth is 60 orders in the technology of sieving; In the rest technology, contain 40% silica powder, 40% Feldspar Powder, 10% clay powder and 10% unslaked lime in the glaze, glaze adds water mixing furnishing glaze slip again, glaze in the glaze slip: water=4: 6; In the sintering technology, fire with smokeless wood kiln, temperature is controlled in 9 hours and rises to 1180 ℃ gradually by normal temperature, stops heating then, cools off and opens kiln after 9 hours.
2. the making method of the described metal and stone mud pottery of root a tree name claim 1 is characterized in that in the pugging technology, with the clod of air-dry back moisture 30%, with the pugging method that artificial pin is stepped on clod is stepped on synthetic mud cake.
3. the making method of the described metal and stone mud of root a tree name claim 1 pottery is characterized in that in the moulding process, is kneading or be drawn into the greenwave of different shape by hand.
4. metal and stone mud pottery, it is characterized in that it be adopt the geographic earth of development area, Dalian Pebble Beach Resort, promptly " metal and stone mud " be raw material, the metal and stone mud ceramic product of producing by the making method in the claim 1.