CN102093034A - Ceramic and preparation method thereof - Google Patents
Ceramic and preparation method thereof Download PDFInfo
- Publication number
- CN102093034A CN102093034A CN 201010581093 CN201010581093A CN102093034A CN 102093034 A CN102093034 A CN 102093034A CN 201010581093 CN201010581093 CN 201010581093 CN 201010581093 A CN201010581093 A CN 201010581093A CN 102093034 A CN102093034 A CN 102093034A
- Authority
- CN
- China
- Prior art keywords
- clay
- vermiform
- laterite
- ceramic
- vermicular
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ceramic and a preparation method thereof. The ceramic is burnt by the following raw materials in percentage by weight: 25 to 45 percent of vermicular red soil, 12 to 38 percent of porcelain clay and the balance of one or more of clay, feldspar powder, titanium oxide, talcpowder and quartz powder. The preparation method for the ceramic comprises the following steps of: thinning the vermicular red soil to be less than 1 millimeter, mixing the thinned vermicular red soil and other raw materials, preparing a blank, and burning the ceramic. The vermicular red soil deserted in the past is effectively utilized, the raw material category and source are enlarged, and the production cost is remarkably reduced particularly for the regions with a large amount of vermicular red soil.
Description
Technical field
The present invention relates to a kind of pottery and preparation method thereof.
Background technology
Existing pottery is mainly fired by china clay and clay and is formed.Because the region of china clay and a large amount of exploitation, its resource is more and more limited, and the problem that therefore how to solve the china clay scarcity of resources has become an important subject of the industry.
Summary of the invention
The object of the present invention is to provide a kind of vermiform laterite of using to substitute pottery of part china clay and preparation method thereof.
This pottery provided by the invention is fired by following raw materials by weight percent and is formed: vermiform laterite 25-45%; China clay 18-38%; All the other are one or more the material in clay, Feldspar Powder, titanium oxide, talcum powder, the silica powder.
The method that the present invention makes above-mentioned pottery is: earlier vermiform laterite is refined to＜1mm, mixes with other raw material then, base is fired again.
Vermiform laterite has another name called " south of the River red soil ", and appearance is maroon.Because particle is coarse, quality is hard, lack viscosity, the iron-holder height, in the past not only not as ceramic raw material, even fill out the road walling, also seldom use, the contriver is by the chemistry to vermiform laterite, physicals is analyzed, though find the coarse and poor plasticity of vermiform laterite particle but still possess the fundamental property of ceramic raw material, through contriver's 6 years repetition test, the continuous various prescriptions of trial are also fired, sintering curve is studied, and the conclusion that draws at last is that vermiform laterite accounts for can not and will refineing to earlier less than 1mm above 45% of raw material total amount, could burn out different classes of qualified pottery with other mixing of materials base.The present invention has carried out effective utilization with the vermiform laterite of nobody shows any interest in the past, has enlarged ceramic raw material type and source, especially this locality is had the area of a large amount of vermiform laterite, will significantly reduce production costs.
Embodiment
Find that in contriver's research vermiform laterite mineral consist of quartz, kaolinite, halloysite, illite etc., and contain rhombohedral iron ore, when the vermiform laterite composition that contains in the raw material especially content at more than 25% of raw material total amount, can significantly improve the anti-ultimate compression strength of tearing open of ceramic.But the content of vermiform laterite should be controlled at below 45% of raw material total amount when making ceramic product, and it will be refine to granularity less than 1mm earlier, mixes with other composition again.
Embodiment one: utilize vermiform laterite to fire the art pottery as one of ceramic raw material.
The raw material of firing the art pottery is: vermiform laterite 40%, official are towards pier china clay 24%, clay 35%, titanium oxide 1%, wherein the official is the on-site place name of contriver towards pier, though local china clay is inferior slightly, cost is relatively low, and can reach the requirement of the art pottery.Raw material should be refined to vermiform laterite＜1mm earlier when being equipped with, and mixes with other raw material then, and base is fired again.
Embodiment two: fire architectural pottery.
The raw material of firing architectural pottery is: vermiform laterite 40%, official are towards Ao china clay 18%, clay 42%.
Embodiment three: fire large-scale mural painting.
The raw material of firing large-scale mural painting is: vermiform laterite 42%, official are towards Ao china clay 27%, clay 32%.
Embodiment four: fire pottery modelled after an antique.
The raw material of firing pottery modelled after an antique is: vermiform laterite 25%, Yiyang china clay 18%, official are towards Ao china clay 20%, Feldspar Powder 16%, talcum powder 8%, silica powder 13%.
The quality of Yiyang china clay is more quite a lot of towards Ao china clay than the official, adds the quality that some Yiyang china clay can guarantee pottery modelled after an antique.
Embodiment five: fire the electrothermal dark-red pottery product.
The raw material of firing the electrothermal dark-red pottery product is: vermiform laterite 45%, Yiyang china clay 18%, official are towards Ao china clay 12%, clay 13%, Feldspar Powder 12%.The natural maroon of vermiform laterite is colour-fast in sintering process, is the good raw material of producing " boccaro ".
The china clay that uses in the above-described embodiment be the official towards pier china clay and Yiyang china clay, also can be with other local china clay, so long as the production location gets final product nearby.
Claims (7)
1. pottery is characterized in that this pottery is fired by following raw materials by weight percent to form: vermiform laterite 25-45%; China clay 18-38%; All the other are one or more the material in clay, Feldspar Powder, titanium oxide, talcum powder, the silica powder.
2. potter's clay according to claim 1 is characterized in that vermiform laterite 40%; China clay 24%;
Clay 35%; Titanium oxide 1%.
3. potter's clay according to claim 1 is characterized in that vermiform laterite 40%; China clay 18%; Clay 42%.
4. potter's clay according to claim 1 is characterized in that vermiform laterite 42%; China clay 27%; Clay 31%.
5. potter's clay according to claim 1 is characterized in that vermiform laterite 25%; China clay 38%; Feldspar Powder 16%; Talcum powder 8%; Silica powder 13%.
6. potter's clay according to claim 1 is characterized in that vermiform laterite 45%; China clay 30%; Clay 13%; Feldspar Powder 12%.
7. method that is used to make the described pottery of one of claim 1 to 6 is characterized in that: earlier vermiform laterite is refined to＜1mm, mixes with other raw material then, base is fired again.