Summary of the invention
The purpose of this invention is to provide a kind of concentrated type antifog glass sanitising agent, its effectively decontamination, antifog makes the glass surface smooth.
Concentrated type antifog glass sanitising agent of the present invention, its component and mass fraction thereof are:
Ammoniacal liquor 0.1-1 part
Trolamine 0.1-5 part
Membrane-forming agent 0.1-10 part
Sequestrant 0.1-5 part
Tensio-active agent 1-20 part
Ethanol 1-50 part.
As required, can also contain deionized water 9-97.6 part.
Preferably, above-mentioned membrane-forming agent is selected from least a among Surf-s110, the Surf-s210.Surf-s is a kind of functional polymer additive of uniqueness; The net effect that it can give moisture film effect and anti-flushing obtains long-acting persistent cleaning power; Can give controllable, persistent surface-treated; Not only promote the initial outward appearance on surface, and reduced adhering to and making that cleaning is easier of dirt.
Preferably, above-mentioned tensio-active agent is selected from polyoxyethylenated alcohol sodium sulfate, SAS, AEO, at least a in empgen BB (BS-12), the amine oxide.
Preferably, above-mentioned sequestrant is selected from least a in YD 30, the disodium edta.
It is understandable that glass cleaner of the present invention can add some ancillary components commonly used, for example essence or spices, pigment etc. as required.
Characteristics of the present invention are the application of membrane-forming agent; Its its specific structure makes it have good hydrophilicity; Form the bright film of one deck at glass surface when cleaning; Given glass surface a lot of good performances: to prevent that glass from polluting once more, antifog, fast doing, make the glass surface hydrophilicity better.The content of this membrane-forming agent is better effects if between 0.5 part to 10 parts.
Concentrated type antifog glass sanitising agent of the present invention has multi-efficiency, can form one deck shiny film at glass surface, give the anti-recontaminate of glass surface, hydrophilic, fast dried, antifog and wash after the excellent properties that leaves no trace.
Embodiment
Illustrate in greater detail concentrated type antifog glass sanitising agent of the present invention through embodiment below.
Embodiment 1
A kind of concentrated type antifog glass sanitising agent, its component and mass fraction thereof are:
0.5 part of ammoniacal liquor
8 parts of Surf-s110
3 parts of EDTA Disodiums (EDTA-2Na)
Fatty Alcohol(C12-C14 and C12-C18) (C
12-16) 2 parts in T 46155 (9) ether (AEO-9)
5 parts of amine oxides
6 parts of polyoxyethylenated alcohol sodium sulfate
45 parts of ethanol
0.5 part in essence
0.1 part of light blue pigment (1% aqueous solution)
29.9 parts of deionized waters
Aliphatic alcohol polyethenoxy (9) ether (AEO-9), ammonium oxide, polyoxyethylenated alcohol sodium sulfate are tensio-active agent; Ethanol is solvent; Surf-s110 is a membrane-forming agent, and available from Guangdong Xin Tu Fine Chemical Co., Ltd, EDTA Disodium (EDTA-2Na) is a sequestrant.
The preparation method of the concentrated type antifog glass sanitising agent of embodiment 1 is following:
1. add 45 parts of the ethanol measure; Add 2 parts in aliphatic alcohol polyethenoxy (9) ether (AEO-9), 5 parts of amine oxides, 6 parts of polyoxyethylenated alcohol sodium sulfate, 8 parts of Surf-s110 then, stir and make its dissolving;
2. add 29.9 parts of deionized waters, 0.5 part of ammoniacal liquor, 3 parts of EDTA-2Na, 0.5 part in essence, 0.1 part of light blue pigment (1% aqueous solution), stir and make it dissolving.
3. filtering the back with 300 mesh filter screens packs.
Embodiment 2
According to the preparation method same with embodiment 1, preparation has the concentrated type antifog glass sanitising agent of following main active component and mass fraction:
1 part of ammoniacal liquor
8 parts of Surf-s210
2 parts of EDTA Disodiums (EDTA-2Na)
Fatty Alcohol(C12-C14 and C12-C18) (C
12-16) 5 parts in T 46155 (9) ether (AEO-9)
7 parts of SASs
8 parts of empgen BBs (BS-12)
35 parts of ethanol
0.1 part in essence
Lemon yellow (1% aqueous solution) 0.1 part
33.8 parts of deionized waters
Aliphatic alcohol polyethenoxy (9) ether (AEO-9), SAS, empgen BB (BS-12) are tensio-active agent; Ethanol is solvent; Surf-s210 is a membrane-forming agent, and available from Guangdong Xin Tu Fine Chemical Co., Ltd, EDTA Disodium (EDTA-2Na) is a sequestrant.
Embodiment 3
According to the preparation method same with embodiment 1, preparation has the concentrated type antifog glass sanitising agent of following main active component and mass fraction:
0.2 part of ammoniacal liquor
3 parts of trolamines
3 parts of Surf-s110
5 parts of Surf-s210
2 parts of EDTA Disodiums (EDTA-2Na)
Fatty Alcohol(C12-C14 and C12-C18) (C
12-14) 5 parts of polyethenoxy ether sodium sulfates (AES)
3 parts of ammonium oxide
4 parts of empgen BBs (BS-12)
45 parts of ethanol
0.5 part in essence
0.2 part of light green pigment (1% aqueous solution)
29.1 parts of deionized waters
Polyoxyethylenated alcohol sodium sulfate (AES), ammonium oxide, empgen BB (BS-12) are tensio-active agent; Ethanol is solvent; Surf-s110, Surf-s210 are membrane-forming agent; Available from Guangdong Xin Tu Fine Chemical Co., Ltd, EDTA Disodium (EDTA-2Na) is a sequestrant.
The result of use evaluation of concentrated type antifog glass sanitising agent
The concentrated type antifog glass sanitising agent for preparing among the embodiment 1-3 is respectively applied for windshield, bathroom washing mirror, house glass, has obtained following ideal effect:
Behind 50 times of the dilute with waters, be used for windshield winter, the anti-fog effect continuous and effective time: more than 15 days;
Behind 80 times of the dilute with waters, just be usually used in bathroom washing mirror, the anti-fog effect continuous and effective time: more than 7 days;
Behind 100 times of the dilute with waters, be used for glass cleaning at home winter, the anti-fog effect continuous and effective time: more than 20 days.
The above is merely preferred embodiment of the present invention, is not to be used to limit protection scope of the present invention.One skilled in the art will appreciate that protection scope of the present invention is as the criterion with appending claims.