CN102050614A - 一种白云石镁水泥混凝土及其制造方法 - Google Patents

一种白云石镁水泥混凝土及其制造方法 Download PDF

Info

Publication number
CN102050614A
CN102050614A CN 201010541809 CN201010541809A CN102050614A CN 102050614 A CN102050614 A CN 102050614A CN 201010541809 CN201010541809 CN 201010541809 CN 201010541809 A CN201010541809 A CN 201010541809A CN 102050614 A CN102050614 A CN 102050614A
Authority
CN
China
Prior art keywords
cement concrete
dolomite
magnesium cement
manufacture method
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010541809
Other languages
English (en)
Inventor
肖学英
王继东
张全有
常成功
王永晏
孙庆国
火焱
王惠娟
王明英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinghai Zhongke Yanhu Technology Innovation Co ltd
Qinghai Institute of Salt Lakes Research of CAS
Original Assignee
Qinghai Zhongke Yanhu Technology Innovation Co ltd
Qinghai Institute of Salt Lakes Research of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinghai Zhongke Yanhu Technology Innovation Co ltd, Qinghai Institute of Salt Lakes Research of CAS filed Critical Qinghai Zhongke Yanhu Technology Innovation Co ltd
Priority to CN 201010541809 priority Critical patent/CN102050614A/zh
Publication of CN102050614A publication Critical patent/CN102050614A/zh
Pending legal-status Critical Current

Abstract

本发明是一种白云石镁水泥混凝土及其制造方法，属于化工建筑领域。白云石镁水泥混凝土由苛性白云石粉、氯化镁、砂、石、惰性填料和水组成，其质量比为1.00∶0.12～0.29∶0～3.0∶0～6.0∶0.10～0.3∶0.44～0.87，其制造方法为拌浆→成型固化→养护。本发明提出采用活性较好的苛性白云石粉制造白云石镁水泥混凝土，而白云石矿资源则分布广泛，就地就近取材，将会降低生产该产品的成本，拓展镁水泥材料的应用，采用本发明制造方法所生产的白云石镁水泥混凝土，具有强度高，胶凝性能强，耐久性强、和易性好、填料添加量大，快速固化，养护容易能等特点，属绿色环保建材，可广泛应用于建筑业。

Description

一种白云石镁水泥混凝土及其制造方法
一、技术领域
本发明是一种白云石镁水泥混凝土及其制造方法，属于化工建筑领域。
二、背景技术
氯氧镁水泥混凝土胶凝材料是一种气硬性材料，以其强度高，胶凝性能强，耐久性强、和易性好、填料添加量大，快速固化，养护容易等特点在建材、筑路、修路等领域广泛使用，目前，生产氯氧镁水泥的主要原料轻烧粉(菱苦土)产地主要集中在我国辽宁，受资源地域限制，生产氯氧镁水泥混凝土原料成本较高，不易推广。
三、发明内容
本发明是将白云石矿(它是碳酸钙和碳酸镁复盐为主要成分的矿石，分子式为CaMg(CO3)2)，经焙烧后得到的苛性白云石粉与氯化镁为主要原料，通过拌浆、成型固化、养护等工序制造白云石镁水泥混凝土。本发明拟采取的技术方案为：一种白云石镁水泥混凝土及其制造方法，其特征在于白云石镁水泥混凝土由苛性白云石粉、氯化镁、砂、石、惰性填料和水组成，其质量比为1.00∶0.12～0.29∶0～3.0∶0～6.0∶0.10～0.3∶0.44～0.87，惰性填料为粉煤灰或矿渣粉或滑石粉或其混合物，其制造方法为拌浆→成型固化→养护，拌浆的工艺要求为将氯化镁按比例溶解于水中形成氯化镁溶液，氯化镁溶液与苛性白云石粉、砂、石和惰性填料按比例的混合物进行拌合，形成白云石镁水泥混凝土料浆，成型固化的工艺要求为将上述白云石镁水泥混凝土料浆直接浇注或注入模板中，固化12～24小时，养护的工艺要求为在环境温度、空气相对湿度小于80％条件下养护后为产品，预制构件养护大于28天。本发明中氯化镁可以用氯化镁的水合物替代。本发明是这样实现的，首先将氯化镁或氯化镁的水合物用水配制成溶液，然后与苛性白云石粉、砂、石、惰性填料的混合物拌合成均匀的浆料，浆料可直接浇注，或制成预制构件成型固化，养护完成即为混凝土产品。本发明提出采用活性较好的苛性白云石粉制造白云石镁水泥混凝土，而白云石矿资源则分布广泛，几乎全国各省均有，储量更丰富，充分利用白云石资源，就地就近取材，将会降低生产该产品的成本，拓展镁水泥材料的应用，为发展各地经济及我国大量节约木材具有重要的意义。采用本发明制造方法所生产的白云石镁水泥混凝土，具有强度高，胶凝性能强，耐久性强、和易性好、填料添加量大，快速固化，养护容易能等特点，属绿色环保建材，可广泛应用于建筑业。
四、附图说明
图1为本发明工艺流程图
五、具体实施方式
实施例1：一种白云石镁水泥混凝土制造方法，取苛性白云石粉10.0kg，砂30kg，粉煤灰1.0kg，用4.4kg水将1.2kg氯化镁配制成溶液，溶液和物料在拌料器中搅拌均匀，制成浆料后注入模板或标准模具中在环境温度条件下成型，脱模后在环境温度下，空气相对湿度小于80％条件下养护至28天，成为砂浆混凝土，测其力学性能。
经测定其主要技术指标如下：
密度等级：1800kg/m3    抗压强度：41.5MPa    轴心抗压强度：27.1MPa
轴心抗拉强度：2.42MPa    静力受压弹性模量：3.12×104MPa
劈裂抗拉强度：5.92MPa    抗折强度：8.4MPa
实施例2：一种白云石镁水泥混凝土制造方法，取苛性白云石粉10.0kg，砂1kg，滑石粉3.0kg，用6.1kg水将1.9kg氯化镁配制成溶液，溶液和物料在拌料器中搅拌均匀，制成浆料后注入模板或标准模具中在环境温度条件下成型，脱模后在环境温度、空气相对湿度小于80％条件下养护至28天，成为砂浆混凝土，测其力学性能。
经测定其主要技术指标如下：
密度等级：1700kg/m3    抗压强度：63.8MPa    轴心抗压强度：28.8MPa  抗折强度：15.6MPa  轴心抗拉强度：2.42MPa  静力受压弹性模量：3.18×104MPa劈裂抗拉强度：9.1MPa
实施例3：一种白云石镁水泥混凝土制造方法，取苛性白云石粉10.0kg，砂20kg，石60.0kg，粉煤灰20kg，用7.6kg水将2.4kg氯化镁配制成溶液，溶液和物料在拌料器中搅拌均匀，制成浆料后注入标准模具中在环境温度条件下成型，脱模后在环境温度、空气相对湿度小于80％条件下养护至28天，成为沙石混凝土，测其力学性能。
经测定其主要技术指标如下：
密度等级：2435kg/m3    抗压强度：41.5MPa    轴心抗压强度：28.5MPa
轴心抗拉强度：2.45MPa    静力受压弹性模量：3.31×104MPa
劈裂抗拉强度：5.9MPa    抗折强度：8.4MPa
实施例4：一种白云石镁水泥混凝土制造方法，取苛性白云石粉10.0kg，砂10kg，石30kg，矿渣粉15kg，用6.9kg水将2.1kg氯化镁配制成溶液，溶液和物料在拌料器中搅拌均匀，制成浆料后注入模板中在环境温度条件下成型，脱模后在环境温度，空气相对湿度小于80％条件下养护至28天，成为沙石混凝土，测其力学性能。
经测定其主要技术指标如下：
密度等级：2410kg/m3  抗压强度：53.8MPa  轴心抗压强度：32.3MPa轴心抗拉强度：2.67MPa    静力受压弹性模量：3.38×104MPa  劈裂抗拉强度：7.7MPa  抗折强度：8.4MPa

Claims (1)

1.一种白云石镁水泥混凝土及其制造方法，其特征在于白云石镁水泥混凝土由苛性白云石粉、氯化镁、砂、石、惰性填料和水组成，其质量比为1.00∶0.12～0.29∶0～3.0∶0～6.0∶0.10～0.3∶0.44～0.87，惰性填料为粉煤灰或矿渣粉或滑石粉或其混合物，其制造方法为拌浆→成型固化→养护，拌浆的工艺要求为将氯化镁按比例溶解于水中形成氯化镁溶液，氯化镁溶液与苛性白云石粉、砂、石和惰性填料按比例的混合物进行拌合，形成白云石镁水泥混凝土料浆，成型固化的工艺要求为将上述白云石镁水泥混凝土料浆直接浇注或注入模板中，固化12～24小时，养护的工艺要求为在环境温度、空气相对湿度小于80％条件下养护后为产品，预制构件养护大于28天。
CN 201010541809 2010-11-03 2010-11-03 一种白云石镁水泥混凝土及其制造方法 Pending CN102050614A (zh)