CN102040754A - 斜交轮胎胎肩胶料 - Google Patents

斜交轮胎胎肩胶料 Download PDF

Info

Publication number
CN102040754A
CN102040754A CN 201010584067 CN201010584067A CN102040754A CN 102040754 A CN102040754 A CN 102040754A CN 201010584067 CN201010584067 CN 201010584067 CN 201010584067 A CN201010584067 A CN 201010584067A CN 102040754 A CN102040754 A CN 102040754A
Authority
CN
China
Prior art keywords
tire shoulder
bias tire
carbon black
stock
bias
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010584067
Other languages
English (en)
Other versions
CN102040754B (zh
Inventor
杨齐
张勋民
卿勤
蒋化学
黄玉君
陈文喜
何晓东
熊国华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Original Assignee
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN TYRE RUBBER (GROUP) CO Ltd filed Critical SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority to CN2010105840676A priority Critical patent/CN102040754B/zh
Publication of CN102040754A publication Critical patent/CN102040754A/zh
Application granted granted Critical
Publication of CN102040754B publication Critical patent/CN102040754B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是斜交轮胎胎肩胶料，本发明胶料中含有天然橡胶、丁二烯橡胶BR9000、氧化锌、促进剂NS。其要点在于：由多种原料配制而成，该种斜交轮胎胎肩胶料的原料包括：天然橡胶、丁二烯橡胶BR9000、氧化锌、硬脂酸、防老剂4020、防老剂RD、炭黑N330、炭黑N660、芳烃油、促进剂NS、硫化剂DTDM、不溶性硫黄IS-6005。本发明胶料主要用于斜交轮胎胎肩中，使用本发明胶料可明显提高斜交轮胎胎肩胶的弹性、降低胎肩胶的生热，减少成品斜交轮胎胎肩与胎体的脱层现象；从而提高斜交轮胎的使用寿命。

Description

斜交轮胎胎肩胶料
 
所属技术领域
本发明涉及一种斜交轮胎胎肩胶料，该胶料用于斜交轮胎生产。
背景技术
汽车轮胎是汽车的一个重要部件，优质的轮胎对汽车的使用性能显得越来越来越重要；斜交轮胎胎体厚，滚动时周向变形大，生热高，而且散热慢，肩空是斜交轮胎损坏的主要形式，因此胎肩胶的配方设计质量的好坏影响斜交轮胎质量的优劣；增加胎肩胶的弹性、降低其生热能有效降低斜交轮胎的肩空，提高斜交轮胎的使用性能，也是轮胎配方设计工程技术人员攻克的难点。
发明内容
本发明的目的是提供斜交轮胎胎肩胶料。
本发明的目的是通过以下技术方案实现的：斜交轮胎胎肩胶料，其特征在于：由下述原料按质量比配制而成：
原  材  料 质量配比
天然橡胶 60.0-90.0
丁二烯橡胶BR9000 10.0-30.0
氧化锌 8.0-12.0
硬脂酸 2.5
防老剂4020 1.5
防老剂RD 1.5
炭黑N330 5.0-20.0
炭黑N660 25.0-45.0
芳烃油 4.0-6.0
促进剂NS 0.8-1.2
硫化剂DTDM 0.5-1.0
不溶性硫黄IS-6005 1.2-1.8
本发明的技术原理是：在生胶体系上采用综合性能最好的天然橡胶为主，并用弹性好生热低的国产丁二烯橡胶BR9000；用炭黑N660和N330作为补强剂，改善胶料的物理机械性能的同时降低配方材料成本；使用促进剂NS、硫化剂DTDM、不溶性硫黄IS-6005作为硫化剂，使用硫给予体硫化剂DTDM能有效降低硫黄的用量，使硫化胶能有效降低多硫键的数量，从而能提高硫化胶的耐老化性能。
 
具体实施方式：
原  材  料 质量配比
天然橡胶 80.0
丁二烯橡胶BR9000 20.0
氧化锌 10.0
硬脂酸 2.5
防老剂4020 1.5
防老剂RD 1.5
炭黑N330 10.0
炭黑N660 35.0
芳烃油 5.0
促进剂NS 1.0
硫化剂DTDM 0.8
不溶性硫黄IS-6005 1.5
在本实施例中，制造胶料采取以下工艺：
胶料制造分为二段混炼生产，均执行自动混炼工艺。一段胶料配方加入天然橡胶、丁二烯橡胶BR9000、炭黑N330、炭黑N660、硬脂酸、氧化锌、防老剂4020、防老剂RD、芳烃油，二段混炼是以一段混炼生成的混炼胶作为母胶，然后加入一段中未加入的促进剂NS、硫化剂DTDM、不溶性硫黄IS-6005于密炼机中再次进行混炼。一段胶料在GK270N密炼机内进行混炼制造；二段混炼胶料在GK255N密炼机内混炼制造，胶料在压片机上捣炼5个来回后出片冷却停放。段间胶料停放不少于4个小时后才能进入下一个加工步骤。
使用本实施例配方制成的斜交轮胎胎肩胶料性能测试数据见下表。
项       目 实验数据
门尼焦烧时间(127℃)/min 25.50
门尼粘度[ML(1+4) 100℃] 58.00
硫化仪数据（143℃）
ML/（dN.m） 0.55
MH/（dN.m） 5.06
T10/min 9.80
T50/min 14.25
T90/min 24.50
胶料物理机械性能
硫化时间(143℃)/min 40
300%定伸应力/ MPa 9.2
拉伸强度/MPa 20.8
拉断伸长率/% 519
拉断永久变形/% 15
邵尔A 型硬度/度 61
撕裂力/（kN.m-1） 100
密度/（Mg.m-3） 1.21
回弹性 50.0
压缩温升1）/℃ 13.5
注：1）冲程 4.45mm；负荷 1.00MPa；频率 30.0HZ；温度 55℃
使用本实施例配方生产的斜交轮胎胎肩胶料，在炼胶、压出过程中，胶料未发生焦烧现象，压出速度快，生产效率高，压出胎面的胎肩部位胶料的致密性好、表面光泽性好且无气孔，下工序的成型和硫化工艺均正常，完全能满足批量性工业化生产。同时使用本实施例配方生产的斜交轮胎胎肩胶料具有高弹性，低生热性，使用本实施例生产的胎肩胶料，经压出用于轮胎制造。

Claims (1)

1.一种斜交轮胎胎肩胶料，该发明主要用于斜交轮胎中，该类斜交轮胎胎肩胶料的要点在于：
原  材  料 质量配比 天然橡胶 80.0 丁二烯橡胶BR9000 20.0 氧化锌 10.0 硬脂酸 2.5 防老剂4020 1.5 防老剂RD 1.5 炭黑N330 10.0 炭黑N660 35.0 芳烃油 5.0 促进剂NS 1.0 硫化剂DTDM 0.8 不溶性硫黄IS-6005 1.5
。
CN2010105840676A 2010-12-13 2010-12-13 斜交轮胎胎肩胶料 Expired - Fee Related CN102040754B (zh)