CN102031348B - 一种消除热轧制钢板应力的方法 - Google Patents
一种消除热轧制钢板应力的方法 Download PDFInfo
- Publication number
- CN102031348B CN102031348B CN2010105378776A CN201010537877A CN102031348B CN 102031348 B CN102031348 B CN 102031348B CN 2010105378776 A CN2010105378776 A CN 2010105378776A CN 201010537877 A CN201010537877 A CN 201010537877A CN 102031348 B CN102031348 B CN 102031348B
- Authority
- CN
- China
- Prior art keywords
- cooling
- minute
- steel plate
- magnetization
- rolled steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种消除热轧制钢板应力的方法，其特征是依次采用以下步骤：将轧制钢板冷却至400-500℃温度后，进行正火处理加热至600-700℃，保温100-180分钟；按20-30℃/分钟的冷却速度降至400-500℃，保温100-180分钟；按20-30℃/分钟的冷却速度降至300-400℃后，放置在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；按10-20℃/分钟的冷却速度降至100-150℃后，继续在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；按10-20℃/分钟的冷却速度降至50-80℃后，保温100-180分钟后，自然冷却到室温。本发明的有益效果：利用轧制后的余热进行正火和控制冷却速度，对轧制后的钢板进行二次变相处理，改善了金相组织，显著改善了板形质量。
Description
技术领域
本发明涉及轧制钢板的制造加工方法，特别涉及一种消除热轧制钢板应力的方法。
背景技术
热轧钢板产品具有强度高、韧性好，易于加工成型和良好的可焊接性等优良性能，因而被广泛应用于船舶、汽车、桥梁、建筑、机械、压力容器制造行业中。
残余应力是当无任何工作载荷作用的情况下存于构件内部且在整个构件内部保持平衡的应力。经过高温轧制的钢板，即使经过回火处理或长期放置，一般也会残留一定的应力。用它制备的机械部件，在长期使用过程中，会产生一定的变形，影响产品的性能。
发明内容
本发明的目的在于提供一种消除热轧制钢板应力的方法，消除轧制钢板的残余应力，使轧制钢板具有高精度的板形质量，满足用户的使用要求。
为了实现上述目的，本发明采用以下技术方案：
一种消除热轧制钢板应力的方法，其特征是依次采用以下步骤：
（1） 将轧制钢板冷却至400-500℃温度后，进行正火处理加热至600-700℃，保温100-180分钟；
（2） 按20-30℃/分钟的冷却速度降至400-500℃，保温100-180分钟；
（3） 按20-30℃/分钟的冷却速度降至300-400℃后，放置在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
（4） 按10-20℃/分钟的冷却速度降至100-150℃后，继续在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
（5） 按10-20℃/分钟的冷却速度降至50-80℃后，保温100-180分钟后，自然冷却到室温。
本发明的有益效果：
利用轧制后的余热进行正火和控制冷却速度，对轧制后的钢板进行二次变相处理，改善了金相组织，显著改善了板形质量。
具体实施方式
下面对本发明的技术方案做进一步详细说明，下述说明仅是示例性的。
本发明以Mn13 和S38MnSiV两种材料为例，轧制后温度为８５０～１０００℃。
一种消除热轧制钢板应力的方法，依次采用以下步骤：
（1） 将上述轧制钢板冷却至400-500℃温度后，进行正火处理加热至600-700℃，保温100-180分钟；
（2） 按20-30℃/分钟的冷却速度降至400-500℃，保温100-180分钟；
（3） 按20-30℃/分钟的冷却速度降至300-400℃后，放置在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
（4） 按10-20℃/分钟的冷却速度降至100-150℃后，继续在交流磁化场中保温磁化100-180分钟；磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
（5） 按10-20℃/分钟的冷却速度降至50-80℃后，保温100-180分钟后，自然冷却到室温。
去应力前后硬度对比表格：
通过对比可知经过处理的钢材前后硬度指标基本不变，反而呈现了略微上升的趋势。
试验证明采用此方法，可以消除热轧制钢板应力，使钢板具有稳定的平整板形质量。
Claims (1)
1.一种消除Mn13或S38MnSiV热轧制钢板应力的方法，其特征是依次采用以下步骤：
将轧制钢板冷却至400-500℃温度后，进行正火处理加热至600-700℃，保温100-180分钟；
按20-30℃/分钟的冷却速度降至400-500℃，保温100-180分钟；
按20-30℃/分钟的冷却速度降至300-400℃后，放置在交流磁化场中保温磁化100-180分钟；
磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
按10-20℃/分钟的冷却速度降至100-150℃后，继续在交流磁化场中保温磁化100-180分钟；
磁化场的磁场强度为0.01-0.04高斯，交流磁化场的频率为240Hz；
按10-20℃/分钟的冷却速度降至50-80℃后，保温100-180分钟后，自然冷却到室温。