CN102020912A - 一种pe透明漆及其制备方法 - Google Patents

一种pe透明漆及其制备方法 Download PDF

Info

Publication number
CN102020912A
CN102020912A CN 201010587276 CN201010587276A CN102020912A CN 102020912 A CN102020912 A CN 102020912A CN 201010587276 CN201010587276 CN 201010587276 CN 201010587276 A CN201010587276 A CN 201010587276A CN 102020912 A CN102020912 A CN 102020912A
Authority
CN
China
Prior art keywords
component
agent
powder
flow agent
clear lacquer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010587276
Other languages
English (en)
Other versions
CN102020912B (zh
Inventor
莫荣飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Libang Changrunfa Science and Technology Material Co., Ltd.
Original Assignee
Huizhou Changrunfa Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huizhou Changrunfa Coating Co Ltd filed Critical Huizhou Changrunfa Coating Co Ltd
Priority to CN 201010587276 priority Critical patent/CN102020912B/zh
Publication of CN102020912A publication Critical patent/CN102020912A/zh
Application granted granted Critical
Publication of CN102020912B publication Critical patent/CN102020912B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种PE透明漆及其制备方法,该PE透明漆的配方为双组份,成膜物质采用富马酸改性低气味不饱和聚酯合成树脂、高效分散剂和渗透粉,涂料成膜过程由于涂膜经过富马酸改性、所以成膜后漆膜本身的气味极低,同时高效分散剂让体系有很好的分散性,润湿性、加上选用特殊填料渗透粉,使得该产品具有低气味,高渗透的特点。本发明的PE透明漆可用于高档实木、木皮家具,项目实施以后能够大大适应家具厂施工,施工气味低,容易渗透、施工遍数少、填充性好、以及有很少的防下陷性能。

Description

一种PE透明漆及其制备方法
技术领域
本发明涉及涂料技术领域,具体涉及家具装饰用漆,尤其涉及一种可用于实木家具或贴木皮家具的PE透明漆及其制备方法。
背景技术
目前,实木家具和贴木皮家具常用的透明漆都是PU漆,但是PU漆在实木、木皮家具上容易下陷、硬度低一直是个难以解决的问题。
现在,不饱和PE漆在家具应用越来越广泛,但是PE漆存在气味大,刺激鼻子,而且难施工,因此一直很难推广和替代PU漆。
发明内容
本发明的目的在于针对现有技术的不足,提供一种低气味高渗透的,可用于实木家具和贴木皮家具的PE透明漆。
本发明的另一个目的在于提供上述PE透明漆的制备方法。
本发明的上述目的是通过如下方案予以实现的:
一种PE透明漆,该PE透明漆为双组分涂料,其原料配方具体包括如下两种组分:
1.组分A,按重量百分比计,由如下组分组成:
PE树脂                              65~70%;
分散剂                               0.5~1.5%; 
消泡剂                               0.2~0.5%;
流平剂1                             0.1~0.3%;
流平剂2                             0.1~0.3%;
防沉剂                               0.5~1.5%;
打磨粉                                2~5%;
渗透粉                               15~20%;
苯乙烯                               6.0~8.0%。
上述PE树脂采用市售的富马酸不饱和聚酯合成树脂;
上述分散剂采用颜料分散剂,能够赋予产品很好的渗透和分散效果,如BYK2150;
上述消泡剂采用本领域技术人员在制备PE漆时常用的消泡剂即可实现本发明,如消泡剂BYK354;
上述流平剂1和流平剂2均采用埃夫卡流平剂;本发明人通过研究发现,涂料中助剂搭配起来使用效果更好,能够弥补单独使用时难以弥补的性能缺陷,所以组分A中采用两种埃夫卡流平剂配合起来使用,流平剂1采用10%EFKA3600(10%EFKA3600是由EFKA3600稀释后得到质量百分比浓度为10%的EFKA3600),流平剂2采用EFKA3035。
上述防沉剂的作用是使涂料具有触变性,黏度大大提高,采用本领域技术人员在制备涂料时常用的防沉剂即可实现本发明,如有机膨润土、聚烯烃蜡或蓖麻油衍生物等。
上述打磨粉是制备底漆时普遍会用到的组分,采用本领域技术人员进行油漆制备时常用的打磨粉即可实现本发明,如硬脂酸锌。
上述渗透粉的作用是增强渗透性和细腻性,采用本领域技术人员进行油漆制备时常用的渗透粉即可实现本发明,如透明粉、滑石粉,或者透明粉和滑石粉的混合。
    2.组分B(稀释单体),按重量百分比计,由如下组分组成:
苯乙烯                50%;
溶剂                  50%。
上述溶剂的作用是将其它物质溶解而形成均一相溶液体,溶剂在液态涂料中起着很重要的作用,对涂料的粘度、光泽、流平性、润湿性、附着力等性能有很大的影响;上述溶剂采用醋酸丁酯。
上述PE透明漆的制备方法,是按照上述配方,先分别配制组分A和组分B,然后按照组分A:B=100:40的重量比,将配制好的组分A和组分B混在一起后,加入兰水,搅拌均匀后再加入白水,搅拌均匀即可得到本发明所需的PE透明漆。
上述制备方法中,兰水和白水均为PE漆制备时常用的助剂,兰水是促进剂,白水是引发剂,但是在传统的PE面漆制备时,兰水和白水是不能同时加入到主料中的,必须是将主料分成两份,一份加白水混匀,另一份加兰水混匀后,再将两份混合到一起,过程就比较繁琐;而本发明由于配方的改进,所以可以先向主料中加入兰水搅拌均匀后直接加入白水搅拌。
上述制备方法中,兰水和白水的用量是根据当时油漆使用环境的温度来具体做调整的,若温度是25℃,则主料(A组分+B组分):兰水:白水=100:1.2:1.4,重量比,若温度升高则兰水和白水的比例相应地调低,若温度降低则兰水和白水的比例相应地调高,具体可参考PE面漆制备时,兰水和白水的加入比例。
与现有技术相比,本发明具有如下予以效果:
1. 成膜物质是构成涂料的主要基础,是决定漆膜性质的主要因素,本发明人通过实验方案设计和研究后,成膜物质采用富马酸改性低气味不饱和聚酯合成树脂、高效分散剂和渗透粉,涂料成膜过程由于涂膜经过富马酸改性、所以成膜后漆膜本身的气味极低,同时高效分散剂让体系有很好的分散性,润湿性、加上选用特殊填料渗透粉,使得该产品具有低气味,高渗透的特点;
2.本发明的PE透明漆可用于高档实木、木皮家具,项目实施以后能够大大适应家具厂施工,施工气味低,容易渗透、施工遍数少、填充性好、以及有很少的防下陷性能。
具体实施方式
下面结合具体实施例对本发明做进一步地描述。
 本实施例的一种PE透明漆,该PE透明漆为双组分涂料,具体包括如下两种组分:
1.组分A,按重量百分比计,由如下组分组成:
PE树脂                              68%;
分散剂                               1%; 
消泡剂                              0.3%;
流平剂1                             0.2%;
流平剂2                             0.2%;
防沉剂                                1%;
打磨粉                                4%;
渗透粉                               18%;
苯乙烯                               7.3%。
上述PE树脂采用市售的富马酸不饱和聚酯合成树脂;
上述分散剂采用BYK2150;
上述消泡剂采用BYK354;
上述流平剂1采用10%EFKA3600;
上述流平剂2采用EFKA303;
上述防沉剂采用有机膨润土;
上述打磨粉采用硬脂酸锌;
上述渗透粉采用透明粉和3000目滑石粉混合。
    2.组分B(稀释单体),按重量百分比计,由如下组分组成:
苯乙烯                50%;
溶剂                  50%;
上述溶剂采用醋酸丁酯。
上述PE透明漆的制备方法,是按照上述配方,先分别配制组分A和组分B,然后按照组分A:B=100:40的重量比,将配制好的组分A和组分B混在一起后,加入兰水,搅拌均匀后再加入白水,搅拌均匀即可得到所需的PE透明漆。
上述PE透明漆,采用本领域技术人员对清漆进行的常规性能测试后,与普通PE透明底漆进行比较,结果如表1所示。
表1  PE透明漆性能比较结果
Figure 193138DEST_PATH_IMAGE001
本实施例的PE透明漆 普通PE透明底漆
打磨性
气味 优,施工没刺激性 中,施工刺鼻
渗透性 优,渗透木眼 中,渗透性一般,木眼突出
硬度
透明度
防下陷
从表1可以看出,与普通PE透明底漆相比,本发明的PE透明漆,其各项性能指标均显示优良,某些性能甚至超过普通PE透明底漆。

Claims (6)

1.一种PE透明漆,其特征在于该PE透明漆的原料配方由如下两种组分组成:
(1)组分A,按重量百分比计,由如下组分组成:
PE树脂                              65~70%;
分散剂                               0.5~1.5%; 
消泡剂                               0.2~0.5%;
流平剂1                             0.1~0.3%;
流平剂2                             0.1~0.3%;
防沉剂                               0.5~1.5%;
打磨粉                                2~5%;
渗透粉                               15~20%;
苯乙烯                               6.0~8.0%;
上述流平剂1和流平剂2均采用埃夫卡流平剂;
(2)组分B,按重量百分比计,由如下组分组成:
苯乙烯                50%;
溶剂                  50%。
2.根据权利要求1所述一种PE透明漆,其特征在于该PE透明漆的原料配方由如下两种组分组成:
(1)组分A,按重量百分比计,由如下组分组成:
PE树脂                              68%;
分散剂                                1%; 
消泡剂                              0.3%;
流平剂1                             0.2%;
流平剂2                             0.2%;
防沉剂                                1%;
打磨粉                                4%;
渗透粉                               18%;
苯乙烯                               7.3%;
(2)组分B,按重量百分比计,由如下组分组成:
苯乙烯                50%;
溶剂                  50%。
3.根据权利要求1或2所述一种PE透明漆,其特征在于组分A中,所述PE树脂为富马酸不饱和聚酯合成树脂,所述分散剂为颜料分散剂,所述消泡剂为BYK354;所述流平剂1为质量百分比浓度为10%的EFKA3600,所述流平剂2采用EFKA3035,所述防沉剂采用有机膨润土、聚烯烃蜡或蓖麻油衍生物,所述渗透粉采用透明粉或滑石粉或两者的混合。
4.根据权利要求3所述一种PE透明漆,其特征在于所述渗透粉采用透明粉和3000目滑石粉的混合。
5.根据权利要求1或2所述一种PE透明漆,其特征在于组分B中,所述溶剂为醋酸丁酯。
6.一种权利要求1或2所述PE透明漆的制备方法,其特征在于该制备方法是按照上述配方,先分别配制组分A和组分B,然后按照组分A:B=100:40的重量比,将配制好的组分A和组分B混在一起后,加入兰水,搅拌均匀后再加入白水,搅拌均匀即可得到所需的PE透明漆。
CN 201010587276 2010-12-14 2010-12-14 一种pe透明漆及其制备方法 Active CN102020912B (zh)