CN102002855B - 玄武岩纤维过滤毡用浸润剂 - Google Patents

玄武岩纤维过滤毡用浸润剂 Download PDF

Info

Publication number
CN102002855B
CN102002855B CN201010541724A CN201010541724A CN102002855B CN 102002855 B CN102002855 B CN 102002855B CN 201010541724 A CN201010541724 A CN 201010541724A CN 201010541724 A CN201010541724 A CN 201010541724A CN 102002855 B CN102002855 B CN 102002855B
Authority
CN
China
Prior art keywords
filter felt
solid content
percent
fiber filter
basalt fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201010541724A
Other languages
English (en)
Other versions
CN102002855A (zh
Inventor
李大福
王玉华
张茂奎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL CO Ltd
Original Assignee
SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL CO Ltd filed Critical SHANDONG XINLI ENVIRONMENTAL PROTECTION MATERIAL CO Ltd
Priority to CN201010541724A priority Critical patent/CN102002855B/zh
Publication of CN102002855A publication Critical patent/CN102002855A/zh
Application granted granted Critical
Publication of CN102002855B publication Critical patent/CN102002855B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种具有耐高温、防静电性能的高温过滤毡浸润剂，特别适合用于玄武岩纤维过滤毡。本发明旨在提供一种具有耐高温、防静电性能的玄武岩纤维过滤毡浸润剂，克服玄武岩纤维过滤毡所处工作环境恶劣的问题。其技术方案为：一种玄武岩纤维过滤毡用浸润剂，包括如下重量百分组成：固含量为20％的石墨乳液5％～6％、固含量为60％的PTFE溶液8％～10％、固含量为60％的硅油乳液4％～6％、固含量为30％的聚丙烯酸酯3％～5％和余量的水。采用本发明表面涂覆玄武岩纤维过滤毡，耐高温、防静电性能好。经过实际检测用这种配方生产的玄武岩纤维过滤毡高温损失率大幅度降低，大大提高了产品性能。

Description

玄武岩纤维过滤毡用浸润剂
技术领域
本发明涉及一种具有耐高温、防静电性能的高温过滤毡浸润剂，特别适合用于玄武岩纤维过滤毡。
背景技术
目前，玄武岩纤维过滤毡是一种全新的过滤材料，没有一种专用的后处理用浸润剂。因玄武岩纤维过滤毡一般应用于交通运输、建筑、石油化工等领域，所处的工作环境比较恶劣，对耐高温、防静电等的性能要求比较高。所以，需要一种浸润剂来提高玄武岩纤维过滤毡的耐高温、防静电性能，并且延长其使用寿命。
发明内容
本发明所要解决的技术问题是提供一种具有耐高温、防静电性能的玄武岩纤维过滤毡浸润剂，克服玄武岩纤维过滤毡所处工作环境恶劣的问题。
本发明的技术方案为：一种玄武岩纤维过滤毡用浸润剂，包括如下重量百分组成：固含量为20％的石墨乳液5％～6％、固含量为60％的PTFE溶液8％～10％、固含量为60％的硅油乳液4％～6％、固含量为30％的聚丙烯酸酯3％～5％和余量的水。
所述固含量为20％的石墨乳液为石墨颗粒直径为1微米的石墨悬浮液。
所述固含量为60％的PTFE溶液为PTFE浓缩分散液，可选用中昊晨光化院或东岳集团氟化工厂生产的PTFE产品，加水稀释成固含量为60％的PTFE溶液。
所述的固含量为60％的硅油乳液为长链烷基、苯基改性有机硅油乳液，选用型号为SE-2203。
所述的固含量为30％的聚丙烯酸酯乳液为改性乳液，型号为LI-3。
采用本发明表面涂覆玄武岩纤维过滤毡，耐高温、防静电性能好。经过实际检测用这种配方生产的玄武岩纤维过滤毡高温损失率大幅度降低，大大提高了产品性能。
本发明的配制工艺为：1、将配置量一半的水加入匀速搅拌桶，并开动搅拌。2、将按比例称重的石墨乳液倒入搅拌桶。3、将按比例称重的PTFE溶液倒入搅拌桶。4、将按比例称重的硅油乳液倒入搅拌桶。5、将按比例称重的聚丙烯酸酯乳液倒入搅拌桶。6、搅拌约30分钟后，加入余量的水即成。。
本发明的有益效果在于，采用本发明表面涂覆玄武岩纤维过滤毡，其各项技术指标经检测都达到国家标准(GB/T18371-2002)。并且由于使用了石墨和改性硅油两种耐高温的润滑剂，大大提高毡的耐温性和使用期限。由于石墨导电，使毡具有了抗静电的性能。大大提高了产品性能，具有良好的社会效益和经济效益。
具体实施方式
以下结合实施例说明本发明，但不限制本发明。均以重量百分数计。
实施例1：
固含量为20％的石墨乳液                    5％
固含量为60％的PTFE溶液                    8％
固含量为60％的硅油乳液(SE-2203)           5％
固含量为30％的聚丙烯酸酯乳液(LI-3)        4％
水                                        余量
实施例2：
固含量为20％的石墨乳液                    6％
固含量为60％的PTFE溶液                    10％
固含量为60％的硅油乳液(SE-2203)           6％
固含量为30％的聚丙烯酸酯乳液(LI-3)        5％
水                                        余量
以下为检测结果：(均以百分计)
由检测结果可以看出：使用本发明表面涂覆玄武岩纤维过滤毡后，玄武岩纤维过滤毡的高温损失率大幅度降低，耐高温性能大大提高。

Claims (4)

1.一种玄武岩纤维过滤毡用浸润剂，其特征在于，包括如下重量百分组成：固含量为20％的石墨乳液5％～6％、固含量为60％的PTFE溶液8％～10％、固含量为60％的硅油乳液4％～6％、固含量为30％的聚丙烯酸酯3％～5％和余量的水。
2.根据权利要求1所述的玄武岩纤维过滤毡用浸润剂，其特征在于，所述固含量为20％的石墨乳液为石墨颗粒直径为1微米的石墨悬浮液。
3.根据权利要求1所述的玄武岩纤维过滤毡用浸润剂，其特征在于，所述固含量为60％的PTFE溶液为PTFE浓缩分散液。
4.根据权利要求1所述的玄武岩纤维过滤毡用浸润剂，其特征在于，所述的固含量为60％的硅油乳液为长链烷基、苯基改性有机硅油乳液。
CN201010541724A 2010-11-12 2010-11-12 玄武岩纤维过滤毡用浸润剂 Active CN102002855B (zh)