CN101994875A - 无缝铜管的制造方法及冷轧机用的棒芯 - Google Patents

无缝铜管的制造方法及冷轧机用的棒芯 Download PDF

Info

Publication number
CN101994875A
CN101994875A CN200910169255XA CN200910169255A CN101994875A CN 101994875 A CN101994875 A CN 101994875A CN 200910169255X A CN200910169255X A CN 200910169255XA CN 200910169255 A CN200910169255 A CN 200910169255A CN 101994875 A CN101994875 A CN 101994875A
Authority
CN
China
Prior art keywords
copper pipe
diameter
seamless copper
manufacture method
pipe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910169255XA
Other languages
English (en)
Other versions
CN101994875B (zh
Inventor
赵钦海
彭永聪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Zhongjia New Materials Co Ltd
Original Assignee
Shandong Zhongjia New Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Zhongjia New Materials Co Ltd filed Critical Shandong Zhongjia New Materials Co Ltd
Priority to CN200910169255XA priority Critical patent/CN101994875B/zh
Publication of CN101994875A publication Critical patent/CN101994875A/zh
Application granted granted Critical
Publication of CN101994875B publication Critical patent/CN101994875B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种无缝铜管的制造方法及冷轧机用的棒芯，方法包括如下步骤：用高纯度阴极铜通过半连续铸造机组铸造实心坯锭；将实心坯锭用燃气加热炉加热至800℃～900℃，在卧式双动水封挤压机上挤压出厚壁管坯；最后通过冷轧管机轧制而成所需要的无缝铜管。所述冷轧机用的棒芯，由多节连续的圆柱和圆台构成。通过本发明的制造方法可以制造出壁比较厚，孔比较小的铜管，降低了生产厂家的生产成本。

Description

无缝铜管的制造方法及冷轧机用的棒芯
技术领域
本发明涉及一种无缝管的制造方法，具体地说是涉及一种厚壁无缝铜管的制造方法及冷轧机用的棒芯。
背景技术
厚壁无缝铜管是一种高效节能产品，长期以来我国一直不能解决生产厚壁无缝铜管的技术难题，对于此类产品，一是依赖从国外进口，但是价格昂贵；二是采用铜棒车床加工，这种方法受车床的限制，制出的铜管长度受限并且效率低下、成品率低，造成人力、物力等资源的浪费。
发明内容
本发明的目的在于克服现有技术的缺点，提供一种壁厚、孔小和成本低廉的无缝铜管的制造方法。
本发明另一目的还在于提供一个实现本方法的冷轧机用的棒芯。
本发明的目的是这样实现的：一种无缝铜管的制造方法，包括如下步骤：用高纯度阴极铜通过半连续铸造机组铸造实心坯锭；将实心坯锭用燃气加热炉加热至800℃～900℃，在卧式双动水封挤压机上挤压出厚壁管坯；最后通过冷轧管机轧制而成所需要的无缝铜管。
所述高纯度阴极铜是Cu-CATH-1。
所述实心坯锭经过燃气加热炉加热至850℃。
所述实心坯锭的铸造直径为185mm、长度为500mm，所述卧式双动水封挤压机上挤压出的厚壁管坯为外径80mm、壁厚11mm的管坯，最后通过带有芯棒的冷轧管机轧制出外径40mm、壁厚10mm的铜管。
所述冷轧管机采用LG-60II-H型冷轧管机。
为了实现上述无缝铜管的制造方法，本发明还设计了一种冷轧机用的棒芯，该棒芯由多节连续的圆柱和圆台构成，从前到后依次是：直径为20mm、长为335mm的圆柱形，前端直径为20mm、后端直径为26mm、长为525mm的圆台形，直径为26mm、长为10mm的圆柱形，前端直径为26mm、后端直径为24mm、长为50mm的圆台形，直径为20mm、长为40mm的圆柱形。
本发明的优点在于：通过本发明的制造方法可以制造出壁比较厚，孔比较小的铜管，并且不偏心的铜管，降低了生产厂家的生产成本。本方法减少了传统工艺的多重繁琐工序，成品合格率提高了42％，人员减少了20％，电费减少了15％，节约铜材30％。
附图说明
图1为本发明制造方法中冷轧管机中芯棒的结构示意图。
具体实施方式
下面结合附图和具体实施方式对本发明做进一步说明。
一种无缝铜管的制造方法，包括如下步骤：用高纯度阴极铜Cu-CATH-1通过1T半连续铸造机组铸造直径为185mm、长度为500mm的实心坯锭；将实心坯锭用燃气加热炉加热至850℃，在1600T卧式双动水封挤压机上挤压出外径为80mm、壁厚为11mm的厚壁管坯；通过LG-60II-H型冷轧管机轧制而成外径40mm、壁厚10mm的铜管。
如图1所示，该冷轧机用的棒芯是由多节连续的圆柱和圆台构成，从前到后依次是：直径为20mm、长为335mm的圆柱形1，前端直径为20mm、后端直径为26mm、长为525mm的圆台形2，直径为26mm、长为10mm的圆柱形3，前端直径为26mm、后端直径为24mm、长为50mm的圆台形4，直径为20mm、长为40mm的圆柱形5。

Claims (6)

1.一种无缝铜管的制造方法，包括如下步骤：用高纯度阴极铜通过半连续铸造机组铸造实心坯锭；将实心坯锭用燃气加热炉加热至800℃～900℃，在卧式双动水封挤压机上挤压出厚壁管坯；最后通过冷轧管机轧制而成所需要的无缝铜管。
2.按着权利要求1所述的无缝铜管的制造方法，其特征在于：所述高纯度阴极铜是Cu-CATH-1。
3.按着权利要求1或2所述的无缝铜管的制造方法，其特征在于：所述实心坯锭经过燃气加热炉加热至850℃。
4.按着权利要求3所述的无缝铜管的制造方法，其特征在于：所述实心坯锭的铸造直径为185mm、长度为500mm，所述卧式双动水封挤压机上挤压出的厚壁管坯为外径80mm、壁厚11mm的管坯，最后通过带有芯棒的冷轧管机轧制出外径40mm、壁厚10mm的铜管。
5.按着权利要求4所述的无缝铜管的制造方法，其特征在于：所述冷轧管机采用LG-60II-H型冷轧管机。
6.一种实现权利要求5所述无缝铜管的制造方法中冷轧机用的棒芯，该棒芯由多节连续的圆柱和圆台构成，从前到后依次是：直径为20mm、长为335mm的圆柱形(1)，前端直径为20mm、后端直径为26mm、长为525mm的圆台形(2)，直径为26mm、长为10mm的圆柱形(3)，前端直径为26mm、后端直径为24mm、长为50mm的圆台形(4)，直径为20mm、长为40mm的圆柱形(5)。
CN200910169255XA 2009-08-25 2009-08-25 无缝铜管的制造方法及冷轧机用的棒芯 Expired - Fee Related CN101994875B (zh)