CN101985539B - 一种硝基木器哑光白面漆 - Google Patents
一种硝基木器哑光白面漆 Download PDFInfo
- Publication number
- CN101985539B CN101985539B CN2010105322747A CN201010532274A CN101985539B CN 101985539 B CN101985539 B CN 101985539B CN 2010105322747 A CN2010105322747 A CN 2010105322747A CN 201010532274 A CN201010532274 A CN 201010532274A CN 101985539 B CN101985539 B CN 101985539B
- Authority
- CN
- China
- Prior art keywords
- nitro
- component
- cotton
- weight percent
- seconds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种硝基木器哑光白面漆,它由甲、乙二个组份组成,涂装时,甲、乙组份重量比为1∶0.1~0.2配漆,刷涂后自然干燥成膜;它能有效地降低空气中甲醛的含量,起到净化空气的作用,环保性能优秀。
Description
技术领域
本发明涉及一种木器哑光白面漆。
背景技术
目前现有技术,普通NC木器硝基哑光白面漆是一种综合性能好的白色涂料,广泛用于木器装饰,施工后溶剂挥发在空气中会残留一些对人体有害的物质,如甲醛等。
发明内容
本发明的目的是:提供一种硝基木器哑光白面漆,它能有效地降低空气中甲醛的含量,起到净化空气的作用,环保性能优秀。
本发明是这样实现的:一种硝基木器哑光白面漆,其特征在于:它由甲、乙二个组份组成,涂装时,甲、乙组份重量比为1∶0.1~0.2配漆,刷涂后自然干燥成膜;
具体制备过程:
(一)甲组份的制备 重量百分比
白面浆 30%-40% 二分之一秒棉液 30%-35%
四分之一秒棉液 10%-14% 氨酯级醋酸正丁酯 6%-8%
DBE 1%-3% 二甲苯 3%-3.6%
消泡剂 0.1%-0.2% 流平剂 0.2%-0.4%
分散剂 0.1%-0.2% 消光粉 1%-1.2%
负离子粉体 1.5%-2.0%
依次入料,分散均匀至细度≤25um,粘度2500~3100CPS/25℃;混合均匀后密封备用;
(1)白面浆的重量百分比及制备方法:
醇酸树脂 46.6% 分散剂 0.4% 丙二醇甲醚醋酸酯 1%
二甲苯 1.5% 钛白粉 50%
将醇酸树脂、分散剂、二甲苯、丙二醇甲醚醋酸酯加入反应釜内,以800-1200转/分中速分散10分钟至充分均匀,然后加入金红石型太白,高速分散10-15分钟,至细度<20UM。
(2)二分之一秒硝化棉浆的制备 重量百分比
氨酯级醋酸正丁酯 64.5%
二分之一秒硝化棉(庐州1/2″NC) 35%
硝化棉抗黄剂 0.5%
(3)四分之一秒硝化棉浆的制备 重量百分比
氨酯级醋酸正丁酯 49.5%
四分之一秒硝化棉(1/4″NC) 50%
硝化棉抗黄剂 0.5%;
(二)乙组份的重量百分比
氨酯级醋酸正丁酯 40~50% 二甲苯 40~50%
乙醇 10~20%;
(三)将甲、乙组份按甲、乙组份重量比为1∶0.1~0.2混合均匀后,即可使用。
具体实施方式
下面结合实施例对本发明作进一步描述。
一种硝基木器哑光白面漆,其特征在于:它由甲、乙二个组份组成,涂装时,甲、乙组份重量比为1∶0.15配漆,刷涂后自然干燥成膜;
具体制备过程:
(一)甲组份的制备 重量百分比
白面浆 38% 二分之一秒棉液 33.5%
四分之一秒棉液 12.8% 氨酯级醋酸正丁酯 7%
DBE 2% 二甲苯 3.6%
消泡剂 0.2% 流平剂 0.2%
分散剂 0.2% 消光粉 1%
负离子粉体 1.5%
依次入料,分散均匀至细度≤25um,粘度2500~3100CPS/25℃;混合均匀后密封备用;
在本实施例中,使用间二甲苯、邻二甲苯、对二甲苯也可以取得与二甲苯同样的技术效果。
负离子粉体 北京天之岩 ASC-02。
(1)白面浆的重量百分比及制备方法:
醇酸树脂 46.6% 分散剂 0.4% 丙二醇甲醚醋酸酯 1%
二甲苯 2.0% 钛白粉 50%
将醇酸树脂、分散剂、二甲苯、丙二醇甲醚醋酸酯加入反应釜内,以800-1200转/分中速分散10分钟至充分均匀,然后加入金红石型太白,高 速分散10-15分钟,至细度<20UM。
钛白粉为美礼联的595,具有高耐候性。醇酸树脂为中国巴德士化工厂生产的牌号为A146树脂。
(2)二分之一秒硝化棉浆的制备 重量百分比
氨酯级醋酸正丁酯 64.5%
二分之一秒硝化棉 35%
硝化棉抗黄剂 0.5%
将依次溶解,混合均匀后备用;
氨酯级醋酸正丁酯:水份<0.05、醇≤0.3
硝化棉抗黄剂 新乡三尾公司生产 型号KH-10。
(3)四分之一秒硝化棉浆的制备 重量百分比
氨酯级醋酸正丁酯 49.5%
四分之一秒硝化棉 50%
硝化棉抗黄剂 0.5%;
将四分之一秒硝化棉溶化后,然后加入硝化棉抗黄剂、氨酯级醋酸正丁酯混合均匀后,备用。
(二)乙组份的重量百分比
氨酯级醋酸正丁酯 45% 二甲苯 45% 乙醇 10%;
将分别入料,混合均匀后,备用。
其重量百分比也可以是:氨酯级醋酸正丁酯 40% 二甲苯 40%乙醇 20%
(三)将甲、乙组份按甲、乙组份重量比为1∶0.1~0.2混合均匀后, 即可使用。
本发明抗甲醛的硝基木器白面漆的各性能指标如下:
具体测试结果:
检测方法:性能指标可参照Q/BDSH001-2007,限量物参照GB18581。
由以上数据可知,本发明白面漆是一种抗甲醛十分优秀的室内装修NC漆,环保性特优是白色漆装修漆首选。
甲组∶乙组=1∶0.2,乙组份,仅起调稀施工作用。
本发明的抗甲醛硝基,经检测和试用证明,其涂层的附着力强,耐磨、耐温、耐水、耐化学性好,施工性、流平性也十分优秀,特别是在降低空气中甲醛含量的性能上,有领先地位。
本发明的白面漆与市面上购回的白面漆的性能比较,见下表:
检验项目 | 本发明 | 样品A | 样品B |
表干 | 12min | 15min | 16min |
实干h | 1.3 | 2 | 3 |
附着力 | 1级 | 2级 | 2级 |
柔韧性mm | 1 | 3 | 3 |
耐热性 | 通过 | 通过 | 通过 |
耐冲击 | ≥30 | 15 | 25 |
甲醛(降解度96h) | 93.1% | 90.0% | 85.5% |
Claims (1)
1.一种硝基木器哑光白面漆,其特征在于:它由甲、乙二个组份组成,涂装时,甲、乙组份重量比为1∶0.1~0.2配漆,刷涂后自然干燥成膜;
具体制备过程:
(一)甲组份的制备重量百分比
依次入料,分散均匀至细度≤25μm,粘度2500~3100CPS/25℃;混合均匀后密封备用;
(1)白面浆的重量百分比及制备方法:
醇酸树脂 40%-50% 分散剂 0.2%-0.4% 丙二醇甲醚醋酸酯 1%-3%二甲苯 1%-2% 钛白粉 50%-55%,上述各组份重量百分比之和为100%;
将醇酸树脂、分散剂、二甲苯、丙二醇甲醚醋酸酯加入反应釜内,以800-1200转/分中速分散10分钟至充分均匀,然后加入金红石型钛白,高速分散10-15分钟,至细度<20μm;
(2)二分之一秒硝化棉液的制备重量百分比
氨酯级醋酸正丁酯 64.5~65%
二分之一秒硝化棉 34.5%-35%
硝化棉抗黄剂 0.2~0.5%
(3)四分之一秒硝化棉液的制备 重量百分比
氨酯级醋酸正丁酯 49.5%
四分之一秒硝化棉 50%
硝化棉抗黄剂 0.5%;
(二)乙组份的重量百分比
氨酯级醋酸正丁酯 40~50% 二甲苯 40~50%
乙醇 10~20%;
(三)将甲、乙组份按甲、乙组份重量比为1∶0.1~0.2混合均匀后,
即可使用。