CN105086786A - 一种胶合板用着色涂料 - Google Patents
一种胶合板用着色涂料 Download PDFInfo
- Publication number
- CN105086786A CN105086786A CN201410598487.8A CN201410598487A CN105086786A CN 105086786 A CN105086786 A CN 105086786A CN 201410598487 A CN201410598487 A CN 201410598487A CN 105086786 A CN105086786 A CN 105086786A
- Authority
- CN
- China
- Prior art keywords
- parts
- rotating speed
- add
- ethyl acetate
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种胶合板用着色涂料，按重量份计，由以下各原料组成：乙酸乙酯30-35份、二氧化钛12-15份、聚四氢呋喃醚二醇7.5-8.5份、硬脂酸铝0.2-0.6份、催干剂0.4-1.5份、二甲苯3-5份、含氯醇酸树脂25-30份、分散剂2-4份、流平剂1.5-2.5份、甲苯4-10份、有机硅油0.5-0.9份、纳米氧化铝溶胶7-9份、磷酸2.5-4份、乙二醇1.6-2.5份、硅灰石粉1.4-4.5份、水30-35份、颜料适量。本发明原材料价格低、有害化学品用量少，漆膜附着力好，着色力强，耐冲击强度优秀。
Description
技术领域
本发明涉及建筑装饰涂料领域，具体属于一种胶合板用着色涂料。
背景技术
涂料是一种可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。
对于胶合板用着色涂料，市场上品种很少，但是都具有价格昂贵、环保性能差等缺点，各种性能指标不佳。
发明内容
本发明的目的是提供一种胶合板用着色涂料，原材料价格低、有害化学品用量少，漆膜附着力好，着色力强，耐冲击强度优秀。
本发明采用的技术方案如下：
一种胶合板用着色涂料，按重量份计，由以下各原料组成：
乙酸乙酯30-35份、二氧化钛12-15份、聚四氢呋喃醚二醇7.5-8.5份、硬脂酸铝0.2-0.6份、催干剂0.4-1.5份、二甲苯3-5份、含氯醇酸树脂25-30份、分散剂2-4份、流平剂1.5-2.5份、甲苯4-10份、有机硅油0.5-0.9份、纳米氧化铝溶胶7-9份、磷酸2.5-4份、乙二醇1.6-2.5份、硅灰石粉1.4-4.5份、水30-35份、颜料适量；
其具体制备方法如下：
在搅拌槽中，先将聚四氢呋喃醚二醇、催干剂、含氯醇酸树脂、乙二醇和三分之一的水加入，开动搅拌，转速350-400转/分，再先依次加入乙酸乙酯、二氧化钛、硬脂酸铝、二甲苯、分散剂，搅拌10-15min，转速550-600转/分，最后加入剩余原料搅拌约15-22min后出料，料浆放入胶体磨中循环研磨35-40min，即可出料、过滤、装桶。
本发明的涂料性能测试如下：
吸水率0.06kg/m2h优等
透气阻力，Sd-值0.034m优等
附着力4.2N/mm2
贮存稳定性，28天/50℃OK
湿擦洗，4天>2250次
湿擦洗，28天>11000次
漆膜厚度，0-2000μm不开裂
耐老化试验(100小时Qq-uvb)不变色，憎水性明显。
本发明以乙酸乙酯、含氯醇酸树脂为主料，以硬脂酸铝、有机硅油、硅灰石粉为辅料，配方比例合理，原材料价格低、有害化学品用量少，漆膜附着力好，着色力强，耐冲击强度优秀。
具体实施方式
一种胶合板用着色涂料，按重量份计，由以下各原料组成：
乙酸乙酯30-35份、二氧化钛12-15份、聚四氢呋喃醚二醇7.5-8.5份、硬脂酸铝0.2-0.6份、催干剂0.4-1.5份、二甲苯3-5份、含氯醇酸树脂25-30份、分散剂2-4份、流平剂1.5-2.5份、甲苯4-10份、有机硅油0.5-0.9份、纳米氧化铝溶胶7-9份、磷酸2.5-4份、乙二醇1.6-2.5份、硅灰石粉1.4-4.5份、水30-35份、颜料适量；
其具体制备方法如下：
在搅拌槽中，先将聚四氢呋喃醚二醇、催干剂、含氯醇酸树脂、乙二醇和三分之一的水加入，开动搅拌，转速380转/分，再先依次加入乙酸乙酯、二氧化钛、硬脂酸铝、二甲苯、分散剂，搅拌12min，转速580转/分，最后加入剩余原料搅拌约18min后出料，料浆放入胶体磨中循环研磨37min，即可出料、过滤、装桶。
Claims (2)
1.一种胶合板用着色涂料，按重量份计，其特征在于，由以下各原料组成：
乙酸乙酯30-35份、二氧化钛12-15份、聚四氢呋喃醚二醇7.5-8.5份、硬脂酸铝0.2-0.6份、催干剂0.4-1.5份、二甲苯3-5份、含氯醇酸树脂25-30份、分散剂2-4份、流平剂1.5-2.5份、甲苯4-10份、有机硅油0.5-0.9份、纳米氧化铝溶胶7-9份、磷酸2.5-4份、乙二醇1.6-2.5份、硅灰石粉1.4-4.5份、水30-35份、颜料适量；
其具体制备方法如下：
在搅拌槽中，先将聚四氢呋喃醚二醇、催干剂、含氯醇酸树脂、乙二醇和三分之一的水加入，开动搅拌，转速350-400转/分，再先依次加入乙酸乙酯、二氧化钛、硬脂酸铝、二甲苯、分散剂，搅拌10-15min，转速550-600转/分，最后加入剩余原料搅拌约15-22min后出料，料浆放入胶体磨中循环研磨35-40min，即可出料、过滤、装桶。
2.根据权利要求1所述胶合板用着色涂料，其特征在于，在搅拌槽中，先将聚四氢呋喃醚二醇、催干剂、含氯醇酸树脂、乙二醇和三分之一的水加入，开动搅拌，转速380转/分，再先依次加入乙酸乙酯、二氧化钛、硬脂酸铝、二甲苯、分散剂，搅拌12min，转速580转/分，最后加入剩余原料搅拌约18min后出料，料浆放入胶体磨中循环研磨37min，即可出料、过滤、装桶。