CN101983042A - 发热体 - Google Patents
发热体 Download PDFInfo
- Publication number
- CN101983042A CN101983042A CN2009801119640A CN200980111964A CN101983042A CN 101983042 A CN101983042 A CN 101983042A CN 2009801119640 A CN2009801119640 A CN 2009801119640A CN 200980111964 A CN200980111964 A CN 200980111964A CN 101983042 A CN101983042 A CN 101983042A
- Authority
- CN
- China
- Prior art keywords
- heater
- mentioned
- fibre plate
- resin molding
- bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种发热体,该发热体能够长时间令人满意地反复进行用手抓握或放开的动作的运动,同时能够温热患部。一种发热体,其是在外面为纤维片的具有透气性的袋中封入通过与空气接触而发热的发热组合物而得到的发热体,其特征在于:(1)该袋由在该纤维片上具有树脂膜的叠层体形成;(2)该叠层体是将该纤维片和该树脂膜不连续地粘合而得到的;(3)该发热组合物的填充率为4~95%。
Description
技术领域
本发明涉及发热体,特别涉及作为治疗或康复用器具使用的发热体。
背景技术
以往,作为手、手指等的训练用器具或康复用器具,提出了各种器具。例如,在专利文献1和2中公开了一种设置有带在手指上的下凹装置的手的训练器具。
但是,在使用专利文献1和2的器具时,对手或手指施加过度的负荷,难以长时间连续地训练和康复。
在手、手指、手腕等的关节痛的治疗或康复中,采用使用发热体温热患部的方法。特别是在手指的关节痛治疗或康复中,同时进行边温热手指边反复进行抓握或放开上述发热体的动作的运动。作为这样的发热体,例如,在专利文献3中,报告了内包有与空气接触而发热的发热组合物所得到的大致球形的发热体。
但是,专利文献3的发热体是在用于一般的发热体的包装中封入发热组合物,所以,该发热体与手并不十分吻合,不适合用手掌抓握或放开的运动。因此,在使用专利文献3的发热体时,难以长时间持续上述运动,不能有效地进行治疗或康复。
作为用于进行上述运动的运动器具,例如,在专利文献4中提出以橡胶状膜覆盖凝胶状物质表面而成型得到的手和手指的运动器具。
但是,专利文献4的运动器具由于较硬而与手不吻合。因此,在使用专利文献4的运动器具时,对手施加过度的负担,难以长时间运动。另外,专利文献4的运动器具没有温热效果,因此,不适合手等关节痛的治疗或康复。
在专利文献5中,作为在暂时性或慢性疼痛的治疗中使用的治疗器具,公开了含有通过与空气接触而发热的发热组合物的加热元件。
但是,专利文献5的加热元件是在膝盖、头部、背部等贴合使用的元件,不是用于在手的等关节痛的治疗和康复中使用的器具。
因此,迫切希望开发一种能够长时间令人满意地反复进行用手抓握或放开的动作的运动,同时能够温热患部的发热体。
专利文献1:日本特开平8-336616号公报
专利文献2:日本特开2006-340795号公报
专利文献3:日本特公平7-63493号公报
专利文献4:日本实开平6-75528号公报
专利文献5:日本特表平11-508786号公报
发明内容
本发明的主要目的在于提供一种能够长时间令人满意地反复进行用手抓握或放开的动作的运动、同时能够温热患部的发热体。
本发明的发明人进行了反复深入的研究,结果发现,在具有特定结构的袋中填充特定量的通过与空气接触而发热的发热组合物而得到的发热体能够达到上述目的,从而完成了本发明。
即,本发明涉及下述发热体。
1.一种发热体,其是在外面为纤维片的具有透气性的袋中封入通过与空气接触而发热的发热组合物而得到的发热体,其特征在于:
(1)该袋由在该纤维片上具有树脂膜的叠层体形成;
(2)该叠层体是将该纤维片和该树脂膜不连续地粘合而得到的;
(3)该发热组合物的填充率为4~95%。
2.如上述项1所述的发热体,其中,上述叠层体中的上述纤维片与上述树脂膜的粘合强度为0.2~6N。
3.如上述项1或2所述的发热体,其中,在上述纤维片和上述树脂膜之间,不连续地形成粘合层。
4.如上述项1~3中任一项所述的发热体,其中,上述袋为球形或圆筒形。
5.如上述项1~4中任一项所述的发热体,其中,上述纤维片是天然纤维或合成纤维的无纺布或纺织布。
6.如上述项1~5中任一项所述的发热体,其中,上述发热组合物是包含铁粉、活性炭、金属盐和水的组合物,该铁粉、该活性炭、该金属盐和水的含量分别为30~80质量%、3~25质量%、0.5~10质量%和1~40质量%。
7.如上述项1~6中任一项所述的发热体,其中,上述树脂膜含有选自聚乙烯、聚丙烯、尼龙聚酯和聚氯乙烯中的至少一种合成树脂作为树脂成分。
8.如上述项1~7中任一项所述的发热体,其是治疗或康复用器具。
本发明的发热体是在外面为纤维片的具有透气性的袋中封入通过与空气接触而发热的发热组合物而得到的发热体,其特征在于:
(1)该袋由在该纤维片上具有树脂膜的叠层体形成;
(2)该叠层体是将该纤维片和该树脂膜不连续地粘合而得到的;
(3)该发热组合物的填充率为4~95%。
本发明的发热体,作为用于填充上述发热组合物的袋,使用由通过不连续地粘合纤维片和树脂膜而得到的叠层体形成的袋。通过不连续地粘合纤维片和树脂膜,能够得到与抓握的手令人满意地吻合的发热体。
在本说明书中,所谓“吻合”,指的是在用手抓握发热体时,能够以适度的力量将抓握的手指压入该发热体中,而且,如果收回压入的手指,就可以感到适度的斥力。
由于本发明的发热体与抓握的手令人满意地吻合,所以能够长时间反复进行抓握或放开的运动。而且,本发明的发热体能够令人满意地发挥温热效果。
在本说明书中,所谓“温热效果”,指的是通过发热来温热患部。通过温热效果,例如,能够改善患部的血液循环,除去患部组织的代谢废物,并且促进患部的修复。
本发明的发热体能够长时间反复进行抓握或放开的运动,而且,在上述运动时,能够令人满意地发挥温热效果,因此,作为用于在手指等的关节痛的治疗或康复中使用的器具是最适合的。
袋
构成本发明发热体的袋具有透气性。本发明的发热体通过使空气从外部流入袋内,使空气与发热组合物接触而使该发热组合物发热。
上述袋的外面是纤维片,由通过在该纤维片上叠层树脂膜而成的叠层体形成。即,上述袋采用复层结构,该复层结构与手接触的外面是纤维片,不与手接触而与上述发热组合物接触的内面是树脂膜。
作为上述纤维片,例如,可以使用天然纤维或合成纤维的无纺布或纺织布。作为上述天然纤维,例如,可以列举棉、麻、丝、毛等。作为合成纤维,例如,可以列举尼龙、聚乙烯、聚丙烯、聚酯、聚氯乙烯、维尼纶、人造丝、腈纶等。特别是从发热体容易与手吻合的方面出发,作为上述纤维片,优选尼龙的无纺布或纺织布。
关于上述纤维片的透气性,只要是能够将空气充分导入袋内的范围即可,没有特别限定。
上述纤维片的厚度,只要为发热体能够充分与手吻合且能够令人满意地发挥温热效果的范围即可,通常为100~350μm左右,优选为200~300μm左右。
上述树脂膜,例如,优选包含聚乙烯、聚丙烯、尼龙、聚酯、聚氯乙烯等合成树脂作为树脂成分的树脂膜。上述合成树脂可以单独使用一种或组合二种以上使用。上述合成树脂膜特别优选树脂成分是聚乙烯。只要在不妨碍本发明效果的范围内,则除了上述树脂成分以外,上述树脂膜也可以根据需要配合抗氧化剂、紫外线吸收剂、染料、颜料、抗静电剂、成核剂等添加物。
上述树脂膜具有透气性。作为上述树脂膜,例如,可以列举通过拉伸在上述树脂成分中添加碳酸钙等无机填充剂和液体石蜡制备得到的树脂组合物而形成的膜;利用针、激光、放电加工等穿出透气孔而具有透气性的膜;本来具有多个微孔作为透气孔的微多孔质膜等。
上述树脂膜的透气性能够根据发热组合物的种类、量、发热温度等,通过适当设定该树脂膜的透气孔大小、数量等来调整。由于上述纤维片具有充分的透气性,所以,上述袋的透气性实质上取决于上述树脂膜的透气孔的孔径。
上述树脂膜的透气性能够通过测定透气度来确认。上述袋的透湿度通常为100~1000g/m2·日左右,优选为200~600g/m2·日左右,更优选为300~400g/m2·日左右。
其中,在本说明书中记载的透湿度值,是利用在JIS Z0208中规定的“防湿包装材料的透湿度试验方法(杯法)”测得的值。
上述树脂膜的厚度,只要是不妨碍本发明的效果的范围即可,通常为5~200μm左右,优选为50~100μm左右。
上述叠层体是将上述纤维片和上述树脂膜不连续地粘合而得到的叠层体。通过使纤维片和树脂膜不连续地粘合,用手抓握发热体时的使用实际感觉变得良好。即,发热体充分与手吻合。
在这里,所谓“不连续地粘合”,指的是使上述纤维片和上述树脂膜非连续地粘合,不规则设置粘合区域和非粘合区域而使两者粘合。即,是指不在上述纤维片的整个面而是在一部分设置与上述树脂膜的粘合区域。
上述叠层体中的上述纤维片与上述树脂膜的粘合强度优选为0.2~6N左右,更优选为0.3~3N左右。虽然不希望是限定性的解释,但当上述粘合强度为0.2~6N左右时,在使用本发明的发热体时,推断在一部分粘合区域中,上述树脂膜容易从上述纤维片剥离,可以认为通过产生这样的剥离而使发热体令人满意地与手吻合。
上述粘合强度可以按照在JIS Z0237中规定的“180度拉剥粘合力”试验法测定。
特别是上述叠层体中的上述纤维片与上述树脂膜粘合的面积,优选为上述纤维片的总面积的30~90%左右,更优选为45~75%左右。
作为上述纤维片与上述树脂膜的粘合形态,可以列举通过在该纤维片和该树脂膜之间设置粘合层而粘合两者的形态、和不通过粘合层而直接粘合两者的形态。作为上述叠层体,特别优选采用前者的粘合形态。
上述粘合层,例如,可以通过在上述纤维片上涂布树脂成分而形成。
作为上述树脂成分,优选可挠性的树脂。作为可挠性的树脂,例如,可以列举醋酸乙烯、聚乙烯醇缩乙醛、乙烯乙酸乙烯酯、氯乙烯、丙烯酸酯、聚酰胺类、纤维素类、α-链烯烃类等。这些树脂可以单独使用一种或组合二种以上使用。作为上述树脂,特别优选乙烯乙酸乙烯酯树脂。
作为涂布树脂成分的方法,可以适当采用公知的方法,但优选使用喷枪进行涂布的方法。在使用喷枪进行涂布时,能够令人满意地形成不连续的粘合层。
树脂成分的涂布量,可以在能够形成不连续的粘合层、能够得到目的粘合强度的范围内适当设定。
上述粘合层的厚度只要为发热体与手充分吻合的范围即可,没有特别限定,通常为1~50μm左右,优选为1~20μm左右。
作为不利用粘合层而使上述纤维片与上述树脂膜直接粘合的方法,可以列举使该纤维片与该树脂膜热压合的方法。具体而言,通过在使用热处理手段加热的同时根据需要进行加压,能够使纤维片与树脂膜粘合。作为上述热处理手段,例如,可以列举热封器、热辊、热风等。
当利用该方法进行热压合时,通过适当设定加热条件、压力条件等,使上述纤维片与上述树脂膜不连续地粘合。例如,当使用热封器进行热压合时,密封温度优选为60~150℃左右。另外,密封时间优选为0.5~10秒左右。
上述袋的形状只要是能够令人满意地进行用手抓握或放开的运动那样的形状即可。上述袋特别优选为球形或圆筒形,更优选为球形。其中,上述所谓“球形”,不限于完全的球形,例如,也包含蛋形、圆锥形等大致的球形。作为本发明的发热体的优选形态,特别可以列举荷包。
所谓荷包,指的是如图1所示那样的以细绳束口的球形容器。
上述袋的容积只要为能够收纳后述的发热组合物的范围内即可,没有特别限定。
发热组合物
作为在上述袋中封入的发热组合物,只要是通过与空气接触而发热的组合物即可,可以使用公知的发热组合物。在本发明中,作为上述发热组合物,特别优选使用包含铁粉、活性炭、金属盐和水的组合物。
在上述发热组合物中的铁粉、活性炭、金属盐和水的合计质量优选为80~100质量%左右。
以下,以包含铁粉、活性炭、金属盐和水的发热组合物为代表性例子,具体说明上述发热组合物。
<铁粉>
利用铁粉和空气中的氧反应而发热,本发明的发热体能够发挥温热效果。
作为上述铁粉,可以列举还原铁、铸铁等。这些可以单独使用一种或组合二种以上使用。
作为上述铁粉的形状,可以列举粒状、纤维状等。这些形状的铁粉既可以单独使用,也可以并用二种以上。特别是从发热体容易与手吻合的方面出发,优选使用粒状的铁粉。
粒状铁粉的粒径只要为发热体能够充分与手吻合且能够令人满意地发挥温热效果的范围即可,通常为10~300μm左右,优选为10~100μm左右。
其中,在本说明书中记载的粒径能够通过下述方法算出,即,将100g作为测定对象的试样(铁粉等)加在自上而下依次设有700μm、650μm、500μm、400μm、300μm、250μm、100μm、50μm、10μm的筛子的电动振动筛机上,振动15分钟后,测定各筛子的残留量和通过量,由此算出粒径。
上述发热组合物中的上述铁粉的含量优选为30~80质量%左右,更优选为45~65质量%左右。
<活性炭>
活性炭能够在表面的微孔中吸入空气,促进氧的供给,保持热量而保温,以使放热温度不发生波动。活性炭内部是非常多孔性的,因此带来特别良好的保水能力。活性炭不仅良好地吸水,而且也吸收因发热组合物产生的热而蒸发的水蒸汽,有助于防止水的逃逸。因此,活性炭能够作为保水物质发挥作用。活性炭还能够吸收由铁粉氧化而产生的臭气。
作为上述活性炭,例如,能够适合使用从椰子壳、木材、木炭、煤炭、骨炭等制备的活性炭。
作为上述活性炭的形状,可以列举粒状、纤维状等。这些形状的活性炭可以单独使用,也可以并用二种以上。在本发明中,特别是从发热体容易与手吻合的方面出发,优选使用粒状的活性炭。
粒状活性炭的粒径只要为发热体能够充分与手吻合且能够令人满意地发挥温热效果的范围即可,通常为10~300μm左右,优选为10~100μm左右。
发热组合物中的上述活性炭的含量优选为3~25质量%左右,更优选是10~20质量%左右。
<金属盐>
金属盐,例如,为了使铁粉与空气的氧化反应容易进行,将铁粉的表面活性化,从而能够促进铁的氧化反应。
作为上述金属盐,可以使用在公知的发热组合物中所使用的金属盐。作为上述金属盐,例如,可以列举硫酸铁、硫酸钾、硫酸钠、硫酸锰、磷酸镁等硫酸盐;氯化铜、氯化钾、氯化钠、氯化钙、氯化锰、氯化镁、氯化亚铜等氯化物等。另外,也可以使用碳酸盐、醋酸盐、硝酸盐和其它盐。关于这些金属盐,可以单独使用一种或组合二种以上使用。
上述金属盐的粒径只要为不妨碍本发明效果的范围即可,通常为100~700μm左右,优选为250~650μm左右。
发热组合物中的上述金属盐的含量优选为0.5~10质量%左右,更优选为1~3质量%左右。
<水>
作为水,例如,可以使用蒸馏水、自来水等。
发热组合物中的上述水的含量优选为1~40质量%左右,更优选为20~30质量%左右。
<其它添加物>
除了上述铁粉、活性炭、金属盐和水以外,根据需要,上述发热组合物也可以含有公知的添加剂。
作为公知的添加剂,例如,可以列举吸水性树脂、保水剂等。通过含有吸水性树脂,容易将上述发热组合物持续保持在干爽的状态。作为上述吸水性树脂,例如,可以列举异丁烯-马来酸酐共聚物、聚乙烯醇-丙烯酸共聚物、淀粉-丙烯酸盐接枝共聚物、聚丙烯酸盐交联物、丙烯酸盐-丙烯酸酯共聚物、丙烯酸盐-丙烯酰胺共聚物、聚丙烯腈交联物等。这些吸水性树脂,可以单独使用一种或组合二种以上使用。
上述吸水性树脂的粒径只要为不妨碍本发明效果的范围即可,通常为100~500μm左右,优选为250~400μm左右。
发热组合物中的上述吸水性树脂的含量优选为1~10重量%左右,更优选为1~3重量%左右。
作为保水剂,可以列举木粉、珍珠岩、蛭石、蛭石等。可以并用。
上述保水剂的粒径只要为不妨碍本发明效果的范围即可,通常为300μm左右以下,优选为250μm左右以下。
发热组合物中的上述保水剂含量优选为1~10质量%左右,更优选为2~5质量%左右。
<各成分的混合>
通过混合上述各成分,能够制备上述发热组合物。根据需要,混合可以在真空下或不活泼气体氛围下进行。例如,可以按照在美国专利第4,649,895号中记载的方法混合。
发热体
通过在上述袋中封入上述发热组合物,能够得到本发明的发热体。作为封入方法,可以列举在上述袋中放入上述发热组合物、以不使该组合物漏出的方式将袋闭合的方法。例如,制成为荷包形的发热体能够通过使用圆形的上述叠层体包入上述发热组合物,以细绳束口而制造。
上述发热体中的上述发热组合物的填充率为4~95%左右,优选为4~40%左右。填充率为4~95%左右时,发热体令人满意地与手吻合。
上述填充率能够通过下式算出。
A÷B×100
(式中,A表示实际封入的发热组合物重量(g)。B表示将发热组合物最大限度地装入袋中时的该发热组合物的重量(g)。)
上述发热组合物的大小只要容易在手中抓握即可。例如,制成为荷包形的发热体的直径优选为7~50cm左右,更优选为10~45cm左右。
上述发热组合物的重量优选为5g左右以上,更优选为15g左右以上,进一步优选为15~200g左右。当重量为5g左右以上时,上述发热体容易与手吻合,能够令人满意地发挥温热效果。另外,当重量为200g左右以下时,手不易疲劳,可以长时间不勉强地进行用手抓握或放开的运动。
上述发热体内部的铁粉容易与空气中的氧发生反应。因此,上述发热体以不接触空气的方式、通常将该发热体放入不透过空气的包装体中而以密封的状态流通。
上述发热体的用途
本发明的发热体在用手抓握时与手吻合。因此,上述发热体能够在用手抓握或放开的运动中令人满意地使用。另外,通过进行上述运动,内部的发热组合物发热,上述发热体通常能够保持40℃左右的温度。因此,本发明的发热体在人进行上述运动的同时能够发挥温热效果。
本发明的发热体能够改善例如手、手指、手腕等手腕部(优选手指)的疾病和症状。本发明的发热体还可以作为用于在治疗后进行康复的器具令人满意地使用。
本发明的发热体可以在各种疾病的治疗中使用。本发明的发热体特别在腱鞘炎、关节风湿病等的关节痛的治疗中有效。
另外,由于本发明的发热体容易与接触的身体部位吻合,所以也可以在痔疮、腰痛等的治疗中令人满意地使用。
而且,由于本发明的发热体在发热时使水份散发,所以能够对接触的身体部位带来湿润而赋予保湿效果。
由于本发明的发热体的温热效果优异,所以不限于治疗和康复,也可以作为用于温热身体的怀炉而令人满意地使用。由于本发明的发热体容易与接触的身体部位吻合,所以,即使在温热手指侧面部等以往难以温热到的部分方面,也是适合的。
发明的效果
本发明的发热体在用手抓握时充分与手吻合。因此,能够长时间令人满意地进行用手抓握或放开本发明的发热体的运动。
另外,本发明的发热体通过反复上述运动,温度上升到40℃左右,并保持这样的温度。因此,本发明的发热体在上述运动时能够令人满意地发挥温热效果。
而且,由于本发明的发热体在发热时使水份散发,所以能够对接触的身体部位带来湿润而赋予保湿效果。
附图说明
图1是表示作为本发明的发热体的一个例子的制成为荷包形的发热体的图。
图2是表示形成本发明的发热体的袋的叠层体的上面图的图。
图3是表示形成本发明的发热体的袋的叠层体的截面图的图。
符号说明
1...树脂膜、2...粘合层、3...纤维片
具体实施方式
以下例示实施例和比较例更具体地说明本发明。但本发明不受实施例所限定。
其中,透湿度利用在JIS Z0208中规定的“防湿包装材料的透湿度试验方法(杯法)”测定。具体而言,在温度25±0.5℃和相对湿度90±2%的氛围中,使用透湿杯测定。
另外,粘合强度按照在JIS Z0237中规定的“180度拉剥粘合力”试验法测定。具体而言,在试验板上贴附在实施例和比较例中得到的叠层体,使之在温度23±2℃和相对湿度50±5%的氛围中静置5分钟以上后,以300±30mm/min的速度连续拉剥叠层体而测定。
实施例1~12和比较例1~9
<纤维片和树脂膜的叠层体的制作>
在厚度250μm的尼龙纺织布(纵向19cm×横向100cm)上,使用喷枪涂布乙烯乙酸乙烯酯树脂(EVA),由此使粘合层不连续地形成。上述粘合层的厚度为5μm。
在上述纤维片的形成有上述粘合层的面上,叠层聚乙烯膜。上述膜的厚度为70μm。另外,上述膜的透湿度为380g/m2·日。
上述叠层体中的上述纤维片与上述树脂膜的粘合强度为0.7N。
通过以上方法制作了厚度350μm的叠层体。
<发热组合物的制备>
通过混合粒径50μm的铁粉、粒径200μm的活性炭、粒径380μm的食盐、水、粒径100μm的蛭石和粒径380μm的聚丙烯酸钠,制备了发热组合物。上述发热组合物中,上述铁粉、活性炭、氯化钠、水、蛭石和聚丙烯酸钠的含量分别为55质量%、13质量%、1质量%、26质量%、3质量%和2质量%。
通过以上方法制备了发热组合物。
<发热体的制造>
从上述叠层体切取比在表1~4中记载的直径多2cm的直径的圆。在上述圆的聚乙烯膜一侧装载上述发热组合物。接着,在相同氛围下将上述发热组合物包入,以细绳束住头部,使上述圆的端部富裕2cm。
通过以上方法制造了荷包形的发热体。
在表1~4中表示发热体中的发热组合物的重量(g)、发热组合物的填充率(%)。
将所得到的发热体装入由聚偏氯乙烯涂布膜(KOP)制成的袋中密封,使其不与空气接触。
其中,下述试验例1~2在从由聚偏氯乙烯涂布膜制成的袋中取出发热体后立即进行。
试验例1
以10名健康正常人为对象,在进行用手反复抓握或放开实施例1~12和比较例1~9中制得的发热体的运动5分钟时,评价该发热体是否充分吻合。
A...感到充分与手吻合的人7名以上时
B...感到充分与手吻合的人5~6名时
C...感到充分与手吻合的人4名以下时
在表1~4中表示结果。
试验例2
以10名健康正常人为对象,在进行用手反复抓握或放开实施例1~12和比较例1~9中制得的发热体的运动5分钟时,评价该发热体的温热效果。
A...感到40℃左右的适度温热的人7名以上时
B...感到40℃左右的适度温热的人5~6名时
C...感到40℃左右的适度温热的人4名以下时
在表1~4中表示结果。
[表1]
实施例 | 1 | 2 | 3 | 4 | 5 | 6 |
直径(cm) | 10 | 10 | 10 | 20 | 20 | 20 |
重量(g) | 5 | 15 | 35 | 10 | 65 | 190 |
填充率 | 11.1 | 33.3 | 77.7 | 4.3 | 28.2 | 82.6 |
试验例1的结果 | A | A | B | A | A | B |
试验例2的结果 | B | A | A | B | A | A |
[表2]
实施例 | 7 | 8 | 9 | 10 | 11 | 12 |
直径(cm) | 30 | 30 | 30 | 40 | 40 | 40 |
重量(g) | 20 | 115 | 345 | 30 | 165 | 500 |
填充率 | 5.2 | 30.3 | 90.7 | 5.4 | 29.7 | 90 |
试验例1的结果 | A | A | B | A | A | B |
试验例2的结果 | A | A | A | A | A | A |
[表3]
比较例 | 1 | 2 | 3 | 4 |
直径(cm) | 10 | 20 | 20 | 30 |
重量(g) | 45 | 5 | 230 | 10 |
填充率 | 100 | 2.17 | 100 | 2.6 |
试验例1的结果 | C | C | C | C |
试验例2的结果 | A | B | A | B |
[表4]
比较例 | 5 | 6 | 7 | 8 | 9 |
直径(cm) | 30 | 40 | 40 | 45 | 45 |
重量(g) | 380 | 15 | 555 | 20 | 650 |
填充率 | 100 | 2.7 | 100 | 3 | 100 |
试验例1的结果 | C | C | C | C | C |
试验例2的结果 | A | A | A | A | A |
实施例13~21
如表5~6中所示地设定上述叠层体中的上述纤维片与上述树脂膜的粘合强度,除此以外,通过与上述实施例5同样的方法制造了荷包形的发热体。
比较例10
在尼龙纺织布上不叠层聚乙烯膜,除此以外,通过与上述实施例5同样的方法制造了荷包形的发热体。即,作为用于包入上述发热组合物的袋,不使用上述叠层体,而使用了尼龙的纺织布。
比较例11
作为用于包入上述发热组合物的袋,使用上述聚乙烯膜取代上述叠层体,除此以外,通过与上述实施例5同样的方法制造了荷包形的发热体。
比较例12
在上述尼龙纺织布上不形成粘合层,除此以外,通过与上述实施例5同样的方法制造了荷包形的发热体。即,作为用于包入上述发热组合物的袋,不使用上述叠层体,而使用上述尼龙的纺织布和上述聚乙烯的膜简单重叠的重叠体。
比较例13~14
如表7中所示地设定在上述叠层体中的上述纤维片与上述树脂膜的粘合强度,除此以外,通过与上述实施例5同样的方法制造了荷包形的发热体。
其中,将实施例13~21和比较例10~14中所得到的发热体分别装入由聚偏氯乙烯涂布膜(KOP)制成的袋中密封,使其不与空气接触。
下述试验例3~5在从由聚偏氯乙烯涂布膜制成的袋中取出发热体后立即进行。
试验例3
以10名健康正常人为对象,在进行用手反复抓握或放开实施例13~21和比较例10~14中制得的发热体的运动5分钟时,评价该发热体是否充分吻合。
A...感到充分与手吻合的人7名以上时
B...感到充分与手吻合的人5~6名时
C...感到充分与手吻合的人4名以下时
在表5~7中表示结果。
试验例4
以10名因腱鞘炎而引起关节痛的患者为对象,在进行用手反复抓握或放开实施例15和18及比较例13~14中制得的发热体的运动5分钟时,评价该发热体是否充分吻合。
A...感到充分与手吻合的人7名以上时
B...感到充分与手吻合的人5~6名时
C...感到充分与手吻合的人4名以下时
在表8中表示结果。
试验例5
以10名因腱鞘炎而引起关节痛的患者为对象,在进行用手反复抓握或放开实施例15和18及比较例13~14中制得的发热体的运动5分钟后,评价疼痛是否缓解。
A...感到疼痛缓解的人7名以上时
B...感到疼痛缓解的人5~6名时
C...感到疼痛缓解的人4名以下时
在表8中表示结果。
[表5]
实施例 | 13 | 14 | 15 | 16 | 17 |
粘合强度(N) | 0.3 | 0.5 | 1 | 1.5 | 2 |
试验例3的结果 | A | A | A | A | A |
[表6]
实施例 | 18 | 19 | 20 | 21 |
粘合强度(N) | 2.5 | 3 | 3.5 | 5 |
试验例3的结果 | A | A | B | B |
[表7]
比较例 | 10 | 11 | 12 | 13 | 14 |
粘合强度(N) | - | - | 0 | 7 | 10 |
试验例3的结果 | C | C | C | C | C |
[表8]
试验例6
以10名手干燥的人为对象,在进行用手反复抓握或放开实施例1~21中制得的发热体的运动5分钟时,评价该发热体是否发挥保湿效果。
全部10人评价实施例1~21中制得的发热体具有保湿效果。
Claims (8)
1.一种发热体,其是在外面为纤维片的具有透气性的袋中封入通过与空气接触而发热的发热组合物而得到的发热体,其特征在于:
(1)该袋由在该纤维片上具有树脂膜的叠层体形成;
(2)该叠层体是将该纤维片和该树脂膜不连续地粘合而得到的;
(3)该发热组合物的填充率为4~95%。
2.如权利要求1所述的发热体,其特征在于:
所述叠层体中的所述纤维片与所述树脂膜的粘合强度为0.2~6N。
3.如权利要求1或2所述的发热体,其特征在于:
在所述纤维片和所述树脂膜之间,不连续地形成粘合层。
4.如权利要求1~3中任一项所述的发热体,其特征在于:
所述袋为球形或圆筒形。
5.如权利要求1~4中任一项所述的发热体,其特征在于:
所述纤维片是天然纤维或合成纤维的无纺布或纺织布。
6.如权利要求1~5中任一项所述的发热体,其特征在于:
所述发热组合物是包含铁粉、活性炭、金属盐和水的组合物,该铁粉、该活性炭、该金属盐和水的含量分别为30~80质量%、3~25质量%、0.5~10质量%和1~40质量%。
7.如权利要求1~6中任一项所述的发热体,其特征在于:
所述树脂膜含有选自聚乙烯、聚丙烯、尼龙聚酯和聚氯乙烯中的至少一种合成树脂作为树脂成分。
8.如权利要求1~7中任一项所述的发热体,其特征在于:
其是治疗或康复用器具。