CN101962454A - 一种导热导电改性塑料材料及制备方法 - Google Patents
一种导热导电改性塑料材料及制备方法 Download PDFInfo
- Publication number
- CN101962454A CN101962454A CN2009101582386A CN200910158238A CN101962454A CN 101962454 A CN101962454 A CN 101962454A CN 2009101582386 A CN2009101582386 A CN 2009101582386A CN 200910158238 A CN200910158238 A CN 200910158238A CN 101962454 A CN101962454 A CN 101962454A
- Authority
- CN
- China
- Prior art keywords
- heat
- plastic material
- modified plastic
- conductivity conducting
- conducting modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是一种改性塑料材料及制备方法。该材料是由聚丙烯、苯乙烯热塑弹性体、高碳膨胀石墨(或鳞片石墨)、钛酸酯偶联剂、抗氧剂及光稳定剂经过密炼造粒工序制成，该材料具有导电、导热、耐酸碱腐蚀及耐低温等特性。
Description
一、技术领域
本发明用于导热、换热、散热及防静电等领域的改性塑料材料及制备方法
二、背景技术
1、现有的导热、散热、换热等材料多为金属或含金属的材料制成，他们大都是不抗氧化、易腐蚀、寿命短、造价高及制备工艺复杂等缺点。
2、目前也出现一些非金属导热和换热材料，多半是聚烯烃类材料和石墨的共混，缺点是：零下5度以下容易产生低脆性，生产出的产品在冬季运输容易出现破碎。
三、发明内容
发明的目的是用改性塑料材料克服已有的金属材料在导热、换热散热中所有难以克服的缺点，提供一种新型的耐弱酸弱碱腐蚀、抗氧化、防静电及寿命长且加工工艺简单的改性塑料材料，同时与其他非金属换热材料在零下15度时进行破坏性试验，发现有很好的耐低脆性能。
本发明的导热导电改性塑料材料是有下列重量份的原料制成：
1、聚丙烯均聚物(8101)或无规共聚聚丙烯(4220) 40-70份
2、苯乙烯热塑弹性体 5-30份
3、膨胀石墨或鳞片石墨 30-60份
4、钛酸酯偶联剂 1-5份
6、抗氧剂 1-5.5份
7、光稳定剂 1-3份
所述苯乙烯类热塑弹性体为SBS或SEBS。
所述抗氧剂为四元酚或三元酚。
所述光稳定剂是受阻胺或二苯甲酮。
将聚丙烯、膨胀石墨或鳞片石墨、苯乙烯塑料弹性体放置密炼设备中混合搅拌至温度达到70度以上，加入钛酸酯偶联剂、抗氧剂及光稳定剂，待充分搅匀温度升至90-100度时，将搅好的物料取出放入双螺杆造粒机中造出母粒。
采用上述导热导电改性塑料材料制造的产品(如散热器、管道……)在零下15度以下，具有良好的低温稳定性，产品在冬季运输过程中不会破碎。
四、具体实施方式
实例一：
取出聚丙烯均聚40份，SBS 20份，鳞片石墨1500目35份，将其放入密炼设备中高速搅拌，当温度升至70度以上时，加入钛酸酯偶联剂2份、三元酚2份、受阻胺1份，待温度升至90-100度时，将其取出放入双螺杆造粒机中造出成功母粒，采用此材料制造的散热器、管道……在零下35度以下，具有良好的低温稳定性。
实例二：
取出无规共聚聚丙烯35份，SEBS 15份，膨胀石墨200目20份，鳞片石墨2000目26份，将其放入密炼设备中高速搅拌，当温度升高至70度以上时，加入钛酸酯偶联剂1.5份、四元酚1.5份、二苯甲酮1份，待充分搅匀温度升至90-100度时，将搅好物料取出放入双螺杆造粒机中造出成功母粒，采用此材料制造的散热器、管道……在零下25度以下，具有良好的稳定性。
实例三：
取出无规共聚聚丙烯45份，SEBS 6份，鳞片石墨2000目45份，将其放入密炼设备中高速搅拌，当温度升至70度以上时，加入钛酸酯偶联剂2份、四元酚1份、受阻胺1份，待充分搅匀温度升至90-100度时，将搅好的物料取出放入双螺杆造粒机中造出成功母粒，采用此材料制造的散热器、管道……在零下15度以下，具有良好的稳定性。
实例四：
取出无规共聚聚丙烯40份，SEBS 10份，鳞片石墨2000目45份，将其放入密炼设备中高速搅拌，当温度升至70度以上时，加入钛酸酯偶联剂2份、四元酚1.5份、二苯甲酮1.5份，待充分搅匀温度升至90-100度时，将搅好的物料取出放入双螺杆造粒机中造出成功母粒，采用此材料制造的散热器、管道……在零下20度以下，具有良好的稳定性。
Claims (8)
1.一种导热导电改性塑料材料，其特征在于：它的组分和重量份范围为聚丙烯40-70份、膨胀石墨或鳞片石墨30-60份、苯乙烯类热塑弹性体5-30份、钛酸酯偶联剂1-5份、抗氧剂1-5.5份、光稳定剂1-3份。
2.如权利要求1所述的导热导电改性塑料材料，其特征在于所述聚丙烯为无规共聚聚丙烯，或均聚物聚丙烯。
3.如权利要求1所述的导热导电改性塑料材料，其特征在于所述膨胀石墨要求含碳量在98％以上，粒数在80-1500目，鳞片石墨要求含碳量也在98％以上，粒数在1200-3000目。
4.如权利要求1所述的导热导电改性塑料材料，其特征在于所述苯乙烯类热塑弹性体为SBS或SEBS。
5.如权利要求1所述的导热导电改性塑料材料，其特征在于所述抗氧剂为四元酚或三元酚。
6.如权利要求1所述的导热导电改性塑料材料，其特征在于所述光稳定剂是受阻胺或二苯甲酮。
7.如权利要求1所述的导热导电改性塑料材料的制备方法，其特征在于所述聚丙烯、膨胀石墨或鳞片石墨、苯乙烯类热塑弹性体，放入密炼设备中高速搅拌，当温度升至70度以上时，加入钛酸酯偶联剂、抗氧剂、光稳定剂，待充分搅匀温度升至90-100度时，将其取出放入双螺杆造粒机中造粒。
8.一种带型腔的散热器，采用权利要求1-6任一项所述的导热导电改性塑料材料。