CN101955714A - 一种用于不锈钢集装箱的高性能底漆涂料 - Google Patents

一种用于不锈钢集装箱的高性能底漆涂料 Download PDF

Info

Publication number
CN101955714A
CN101955714A CN2009100551605A CN200910055160A CN101955714A CN 101955714 A CN101955714 A CN 101955714A CN 2009100551605 A CN2009100551605 A CN 2009100551605A CN 200910055160 A CN200910055160 A CN 200910055160A CN 101955714 A CN101955714 A CN 101955714A
Authority
CN
China
Prior art keywords
solvent
stainless steel
freight container
mixture
primer base
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100551605A
Other languages
English (en)
Inventor
王勇
王玉珏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongtu Chemical (Shanghai) Co Ltd
Original Assignee
Zhongtu Chemical (Shanghai) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongtu Chemical (Shanghai) Co Ltd filed Critical Zhongtu Chemical (Shanghai) Co Ltd
Priority to CN2009100551605A priority Critical patent/CN101955714A/zh
Publication of CN101955714A publication Critical patent/CN101955714A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，该涂料包括主剂和固化剂，所述的主剂和固化剂的重量比为4～6∶1；所述的主剂包含以下组分及重量百分含量，以主剂的总重量为100％计：环氧树脂20％～35％，成膜助剂1％～3％，颜料40％～60％，溶剂余量；所述的固化剂包含以下组分及重量百分含量，以固化剂的总重量为100％计：聚酰胺树脂60％～70％，溶剂余量。与现有技术相比，本发明涂料不含铅铬类颜料，与各类型不锈钢底材附着力优良，产品硬度高，耐划擦能力强，并具有良好的耐腐蚀性。

Description

一种用于不锈钢集装箱的高性能底漆涂料
技术领域
本发明涉及一种溶剂型涂料，尤其涉及一种用于不锈钢集装箱的高性能底漆涂料。
背景技术
目前，集装箱制造工业主要集中在中国境内，中国汇集了全球制造集装箱活动的八成以上，在世界涂料业加快转移之际，作为全球涂料生产大国之一的我国，伴随着集装箱业的发展同时率先在集装箱涂料领域取得了领航地位。随着不同规格不同用途的集装箱的孕育而生，急需开发出具有特别性能并且使用方便的涂料，以满足特殊集装箱的要求。本发明产品为不锈钢集装箱特别设计。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种不含铅铬类颜料，与各类型不锈钢底材附着力优良，产品硬度高，耐划擦能力强，并具有良好的耐腐蚀性的用于不锈钢集装箱的高性能底漆涂料。
本发明的目的可以通过以下技术方案来实现：一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，该涂料包括主剂和固化剂，所述的主剂和固化剂的重量比为4～6∶1；
所述的主剂包含以下组分及重量百分含量，以主剂的总重量为100％计：
环氧树脂    20％～35％，
成膜助剂    1％～3％，
颜料        40％～60％，
溶剂        余量；
所述的固化剂包含以下组分及重量百分含量，以固化剂的总重量为100％计：
聚酰胺树脂    60％～70％，
溶剂        余量。
所述的环氧树脂包括双酚A型环氧树脂，为主要成膜物质。
所述的成膜助剂包括防流挂剂、偶联剂中的一种或几种。
所述的防流挂剂为聚酰胺石蜡或聚乙烯石蜡中的一种或几种。
所述的偶联剂为有机硅烷偶联剂。
所述的颜料为着色颜料和体质颜料的混合物，也为主要成膜物质。
所述的着色颜料为金红石型钛白、碳黑、钛青蓝、钛青绿、氧化铁红、氧化铁黄、有机永固红、有机紫、无铅铬黄、无铅铬桔或它们的混合物；所述的体质颜料为沉淀硫酸钡、碳酸钙、滑石粉、云母粉或它们的混合物。
所述的聚酰胺树脂为以间二甲苯二胺与二元酸合成的聚酰胺树脂。
所述的主剂的溶剂为芳香烃溶剂、醇类溶剂、酮类溶剂、酯类溶剂、醚类溶剂或它们的混合物，所述的固化剂的溶剂为芳香烃溶剂、醇类溶剂或它们的混合物。
所述的芳香烃溶剂为甲苯、二甲苯或它们的混合物；所述的醇类溶剂为异丙醇、丁醇、异丁醇、仲丁醇、叔丁醇或它们的混合物；所述的酮类溶剂为甲乙酮、甲基丁基酮、甲基异丁基酮或它们的混合物；所述的酯类溶剂醋酸甲酯、醋酸乙酯、醋酸丁酯或它们的混合物，所述的醚类溶剂包括丙二醇甲醚。
本发明为一种非水介质的适合于不锈钢集装箱外涂层配套的底漆涂料，其中所述的环氧树脂包括双酚A型环氧树脂，为主要成膜物质；所述的成膜助剂包括防流挂剂、偶联剂中的一种或几种，偶联剂可显著提高该产品与不锈钢底材的附着力；所述的颜料为着色颜料和体质颜料的混合物，也是主要成膜物质，它可以赋予涂膜颜色及遮盖力，可以改善涂料的耐划擦性、附着力、流变性、耐候性、透气性、光泽、耐化学性等，使用高硬度颜料，可以显著提高漆膜硬度以达到改善产品耐划擦性的目的；所述的聚酰胺树脂通过与环氧树脂反应固化成膜，其具有良好的耐化学性。
与现有技术相比，本发明涂料与不锈钢底材具有优良的附着力，较高的漆膜硬度使其具有优良的耐划擦性，当涂布不锈钢集装箱时，具有较强的施工性能，可广泛用于各类不锈钢集装箱，如冷柜箱，不锈钢罐式集装箱等等。本发明涂料不含铅铬类颜料，与各类型不锈钢底材附着力优良，产品硬度高，耐划擦能力强，并具有良好的耐腐蚀性。
具体实施方式
实施例1
一种用于不锈钢集装箱的高性能底漆涂料，该涂料包括主剂和固化剂，主剂和固化剂的重量比为5∶1，主剂和固化剂的具体组分及含量(重量百分比)如下所示：
主剂
双酚A型环氧树脂        30％
聚乙烯石蜡             2％
有机硅烷偶联剂         1％
碳酸钙                 40％
金红石型钛白粉         10％
二甲苯                 10％
正丁醇                 6％
        固化剂
聚酰胺树脂             65％
二甲苯                 35％。
实施例2
一种用于不锈钢集装箱的高性能底漆涂料，该涂料包括主剂和固化剂，主剂和固化剂的重量比为4∶1，主剂和固化剂的具体组分及含量(重量百分比)如下所示：
主剂
双酚A型环氧树脂        20％
聚酰胺石蜡             3％
沉淀硫酸钡             20％
炭黑                   10％
钛青蓝                 10％
甲乙酮                 17％
醋酸酯                 20％
    固化剂
聚酰胺树脂        60％
甲苯              20％
丁醇              20％。
实施例3
一种用于不锈钢集装箱的高性能底漆涂料，该涂料包括主剂和固化剂，主剂和固化剂的重量比为6∶1，主剂和固化剂的具体组分及含量(重量百分比)如下所示：
    主剂
双酚A型环氧树脂    35％
有机硅烷偶联剂     1％
滑石粉             20％
云母粉             20％
氧化铁红           10％
有机永固红         5％
无铅铬桔           5％
丙二醇甲醚         17％
    固化剂
以间二甲苯二胺与二元酸合成的聚酰胺树脂    70％
异丙醇             30％。

Claims (10)

1.一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，该涂料包括主剂和固化剂，所述的主剂和固化剂的重量比为4～6∶1；
所述的主剂包含以下组分及重量百分含量，以主剂的总重量为100％计：
环氧树脂    20％～35％，
成膜助剂    1％～3％，
颜料        40％～60％，
溶剂        余量；
所述的固化剂包含以下组分及重量百分含量，以固化剂的总重量为100％计：
聚酰胺树脂    60％～70％，
溶剂          余量。
2.根据权利要求1所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的环氧树脂包括双酚A型环氧树脂，为主要成膜物质。
3.根据权利要求1所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的成膜助剂包括防流挂剂、偶联剂中的一种或几种。
4.根据权利要求3所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的防流挂剂为聚酰胺石蜡或聚乙烯石蜡中的一种或几种。
5.根据权利要求3所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的偶联剂为有机硅烷偶联剂。
6.根据权利要求1所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的颜料为着色颜料和体质颜料的混合物，也为主要成膜物质。
7.根据权利要求6所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的着色颜料为金红石型钛白、碳黑、钛青蓝、钛青绿、氧化铁红、氧化铁黄、有机永固红、有机紫、无铅铬黄、无铅铬桔或它们的混合物；所述的体质颜料为沉淀硫酸钡、碳酸钙、滑石粉、云母粉或它们的混合物。
8.根据权利要求1所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的聚酰胺树脂为以间二甲苯二胺与二元酸合成的聚酰胺树脂。
9.根据权利要求1所述的一种一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的主剂的溶剂为芳香烃溶剂、醇类溶剂、酮类溶剂、酯类溶剂、醚类溶剂或它们的混合物，所述的固化剂的溶剂为芳香烃溶剂、醇类溶剂或它们的混合物。
10.根据权利要求9所述的一种用于不锈钢集装箱的高性能底漆涂料，其特征在于，所述的芳香烃溶剂为甲苯、二甲苯或它们的混合物；所述的醇类溶剂为异丙醇、丁醇、异丁醇、仲丁醇、叔丁醇或它们的混合物；所述的酮类溶剂为甲乙酮、甲基丁基酮、甲基异丁基酮或它们的混合物；所述的酯类溶剂醋酸甲酯、醋酸乙酯、醋酸丁酯或它们的混合物，所述的醚类溶剂包括丙二醇甲醚。
CN2009100551605A 2009-07-21 2009-07-21 一种用于不锈钢集装箱的高性能底漆涂料 Pending CN101955714A (zh)