CN101948593B - 一种用于稀土双色彩条手柄的粒料配方 - Google Patents
一种用于稀土双色彩条手柄的粒料配方 Download PDFInfo
- Publication number
- CN101948593B CN101948593B CN2010102825405A CN201010282540A CN101948593B CN 101948593 B CN101948593 B CN 101948593B CN 2010102825405 A CN2010102825405 A CN 2010102825405A CN 201010282540 A CN201010282540 A CN 201010282540A CN 101948593 B CN101948593 B CN 101948593B
- Authority
- CN
- China
- Prior art keywords
- rare earth
- formula
- bar handle
- rare
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用于稀土双色彩条手柄的粒料配方,各原料的重量份配比为:聚氯乙烯PVC 80-100份,邻苯二甲酸二辛酯6-16份,偏苯三酸三辛酯6-10份,有机锡稳定剂TM181-FS0.2-0.6份,白油0.2-0.4份,稀土材料0.1-0.3份。本发明有益的效果是:采用本配方制备出来的粒料来生产手柄,手柄的外观更具有光泽、手感强、尺寸标准,采用烯土材料混合使聚氯乙烯中氯分子量充分挥发,材料有光泽,重金属含量减少,比原生产工艺减少环境污染及产品报废率,大大提高了产品质量。
Description
技术领域
本发明属于螺丝批手柄领域,尤其是一种用于稀土双色彩条手柄的粒料配方。
背景技术
普通的螺丝批手柄均采用普通的PVC制成,其光泽度和手感较差,在挤出过程中尺寸不标准,且产生较多的废气排放量,对环境影响较大。
发明内容
本发明要解决上述现有技术的缺点,提供一种用于稀土双色彩条手柄的粒料配方。
本发明解决其技术问题采用的技术方案。这种用于稀土双色彩条手柄的粒料配方,各原料的重量份配比为:聚氯乙烯PVC 80-100份,邻苯二甲酸二辛酯6-16份,偏苯三酸三辛酯6-10份,有机锡稳定剂TM181-FS 0.2-0.6份,白油0.2-0.4份,稀土材料0.1-0.3份。
所述的稀土材料是镧、铈、镨、钕的一种或多种。
在上述的配方中增加润滑油S-160.2-0.4份。
本发明有益的效果是:采用本配方制备出来的粒料来生产手柄,手柄的外观更具有光泽、手感强、尺寸标准,采用烯土材料混合使聚氯乙烯中氯分子量充分挥发,材料有光泽,重金属含量减少,比原生产工艺减少环境污染及产品报废率,大大提高了产品质量。
具体实施方式
下面结合实施例对本发明作进一步说明:
实施例1:这种用于稀土双色彩条手柄的粒料配方,粉料通过造粒机制备成粒料,各原料的重量份配比为:聚氯乙烯PVC 80-100份(聚氯乙烯采用台塑S60和台塑S65型按照1∶1的重量配比混合),邻苯二甲酸二辛酯(作为增塑剂)6-16份,偏苯三酸三辛酯6-10份,有机锡稳定剂TM181-FS 0.2-0.6份(加热稳定剂),白油(作为外润滑剂)0.2-0.4份,稀土材料0.1-0.3份。所述的稀土材料是镧、铈、镨、钕的一种或多种。在上述的配方中,还可以根据需要加入不同的颜料,如红、蓝、绿等等,形成不同的颜色,通过挤出机制成双色彩条手柄。
美国罗门哈斯(莫顿),TM181-FS是一种高效率液态热有机锡稳定剂,特别适用于制造食品包装之硬性聚氯乙烯或其聚合物,性能表:TM-181-FS,锡含量%19.1Mercaptan%12.0,酸值3.0,色值(Gardner最高),透光率%(440mm,最低)80mm,比重Spec.Grav25℃1.17 Wt.Lbs/gal25℃9.7外观:透明。
实施例2:在实施例1不同之处在于,在上述的配方中增加润滑油S-160.2-0.4份(作为内润滑剂)。采用日本NOK株式会社生产的SEALUB S-16高性能润滑油。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。
Claims (2)
1.一种用于稀土双色彩条手柄的粒料,其特征在于:各原料的重量份配比为:聚氯乙烯PVC 80-100份,邻苯二甲酸二辛酯6-16份,偏苯三酸三辛酯6-10份,有机锡稳定剂TM181-FS0.2-0.6份,白油0.2-0.4份,稀土材料0.1-0.3份;所述的稀土材料是镧、铈、镨、钕的一种或多种。
2.根据权利要求1所述的用于稀土双色彩条手柄的粒料,其特征是:在上述的配方中增加润滑油S-16 0.2-0.4份。