CN101948281A - 一种水泥聚合物泡沫塑料粉轻体绝热板及其制备方法 - Google Patents

一种水泥聚合物泡沫塑料粉轻体绝热板及其制备方法 Download PDF

Info

Publication number
CN101948281A
CN101948281A CN2010102373982A CN201010237398A CN101948281A CN 101948281 A CN101948281 A CN 101948281A CN 2010102373982 A CN2010102373982 A CN 2010102373982A CN 201010237398 A CN201010237398 A CN 201010237398A CN 101948281 A CN101948281 A CN 101948281A
Authority
CN
China
Prior art keywords
parts
cement
heat
insulating shield
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2010102373982A
Other languages
English (en)
Other versions
CN101948281B (zh
Inventor
李季
杨勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liaoning JZ Real Estate Development Co., Ltd.
Original Assignee
Liaoniang Kaoke Environmental Protection & Energy-Saving Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liaoniang Kaoke Environmental Protection & Energy-Saving Building Material Co Ltd filed Critical Liaoniang Kaoke Environmental Protection & Energy-Saving Building Material Co Ltd
Priority to CN2010102373982A priority Critical patent/CN101948281B/zh
Publication of CN101948281A publication Critical patent/CN101948281A/zh
Application granted granted Critical
Publication of CN101948281B publication Critical patent/CN101948281B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种水泥聚合物泡沫塑料粉轻体绝热板，包括以下原材料按重量份配比制成：水泥100份、粉煤灰40～80份、硅藻土10～20份、可再分散乳胶粉1～3份、纤维素醚0.5～1份、憎水剂0.1～0.5份、泡沫塑料粉40～80份、水100～200份；将上述比例的材料混合搅拌均匀注入模型内加压0.1～1MPa成型，常温或加温40～80℃养护而成。本发明的这种水泥聚合物泡沫塑料粉轻体绝热板制作工艺简单，成本低，具有稳定的化学性能，优良的保温、阻燃、隔音性能，且节能环保，无污染。

Description

一种水泥聚合物泡沫塑料粉轻体绝热板及其制备方法
技术领域
本发明涉及一种水泥聚合物泡沫塑料粉轻体绝热板，属于一种建筑材料。
背景技术
已有的绝热板多采用模塑聚苯乙烯塑料泡沫板和挤塑聚苯乙烯塑料泡沫板，此类材料导热系数小，绝热性能好，但强度比较低，防火性能差。接连发生的由建筑外保温系统及外装饰材料引发的火灾事故表明，建筑节能与建筑装饰的防火安全问题十分突出、亟待解决。随着社会发展，建筑物的防火性能越来越受到重视，对建筑防火等级要求的也有所提高。为有效防止建筑外保温系统火灾事故，2009年9月25日，公安部、住房和城乡建设部联合制定了《民用建筑外保温系统及外墙装饰防火暂行规定》(公通字[2009]46号)，民用建筑外保温材料的燃烧性能宜为A级，且不应低于B2级。高度大于等于100m的住宅建筑和高度大于等于100m的住宅建筑，其保温材料的燃烧性能应为A级。当采用B1、B2级保温材料时，按规定的层数应设置水平防火隔离带，规定需要设置防火隔离带时，应沿楼板位置设置宽度不小于300mm的A级保温材料。通常A级材料有水泥珍珠岩，加气混凝土块，岩棉、玻璃棉等，水泥珍珠岩容重较大，易吸水，导热系数也大，岩棉、玻璃棉在生产和使用中对环境和人员健康上存在一定影响。加气混凝土块、发泡水泥则工艺复杂或受温度等因素影响在生产中不易控制。因此，选择绝热材料时应考虑到材料的阻热性能、燃烧性、抗压强度、对环境的友好性和可操作性。
发明内容
本发明的目的是提供一种水泥聚合物泡沫塑料粉轻体绝热板，为泡沫塑料粉以不同掺量与水泥聚合物混合并添加憎水剂和纤维等制作而成，其制作工艺简单，成本低，具有稳定的化学性能，优良的保温、阻燃、隔音性能，且节能环保，无污染。
为解决以上问题，本发明的具体技术方案如下：一种水泥聚合物泡沫塑料粉轻体绝热板，其特征在于：
包括以下原材料按重量份配比制成：
水泥100份、             粉煤灰40～80份、
硅藻土10～20份、        可再分散乳胶粉1～3份、
纤维素醚0.5～1份、      泡沫塑料粉40～80份、
憎水剂0.1～0.5份、      水100～200份。
所述的水泥为选用42.5强度等级以上的普通硅酸盐水泥、硫(铁)铝酸盐水泥或高铝水泥；所述的粉煤灰为一级或二级干排灰；可再分散乳胶粉为醋酸乙烯酯与乙烯共聚胶粉(Vac/E)、乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉(E/Vc/VL)、醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉(Vac/E/VeoVa)、醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉(Vac/VeoVa)，醋酸乙烯酯与叔碳酸乙烯酯-VeoVa或聚乙烯醇胶粉等；纤维素醚为甲基纤维素、羟丙基甲基纤维素或羧甲基羟乙基纤维素等；憎水剂为有机硅憎水剂、硅烷基憎水剂和脂肪酸金属盐憎水剂如硬脂酸钙、硬脂酸铝；泡沫塑料粉为公开号CN101215400A的专利所公开的保温隔热泡沫粉或公开号为CN 1736936的专利所公开的脲醛泡沫塑料保温板粉碎成20～100目的粉末而成的脲醛泡沫塑料粉。
在上述配比中，为了加快模具周转，增加了早强剂0～3份；为了增强抗裂，在上述配比中，还可加入聚丙烯纤维0.1～0.3份，也可用聚苯颗粒0～10份部分代替泡沫塑料粉。浇筑成型时，为了提高流性，可加入减水剂0.2～0.6份。
所述的早强剂为硫酸盐类早强剂如硫酸钠、亚硝酸钠、亚硝酸钙或有机化合物早强剂如三乙醇胺或甲酸钙等；为了增强抗裂，在上述配比中，还可加入聚丙烯纤维0.1～0.3份，该聚丙烯纤维直径为20～40μm，长度为3～18mm，聚苯颗粒为粒径不大于5mm；减水剂为萘系高效减水剂，脂肪族高效减水剂，氨基减水剂或聚羧酸系减水剂中的一种或两种以上混合。
水泥聚合物泡沫塑料粉轻体绝热板的制备方法：将上述比例的材料混合搅拌均匀注入模型内加压0.1～1MPa成型为厚度20～200mm厚的绝热板或50～200mm厚的空腔结构绝热板，也可直接浇筑在模框内成型，常温或加温40～80℃养护而成。
本发明的优点和效果：
1、本发明的水泥聚合物泡沫塑料粉轻体绝热板主要绝热材料为泡沫塑料粉，泡沫塑料粉的表观密度为18～40kg/m3，其导热系数为0.025～0.040W/(m·K)，有优良的保温性能，还具有稳定的化学性能、隔音性能。
泡沫塑料粉与其他无机保温材料、有机粘剂、无机胶凝材料复合应用，可制成建筑节能用的粉状保温材料、板材、块材材料。
2、本发明的水泥聚合物泡沫塑料粉轻体绝热板生产工艺简单，可操作性好，成品率高；泡沫塑料粉较单一粒径的聚苯颗粒级配好，成型后表面平滑，无颗粒感；其生产温度条件较水泥发泡材料要求低。
3、本发明的水泥聚合物泡沫塑料粉轻体绝热板本较水泥珍珠岩板，水泥玻化微珠等干密度小，传热阻小，阻燃性能好，环保节能、生产成本低。
4、本发明的水泥聚合物泡沫塑料粉轻体绝热板还可与模塑聚苯乙烯塑料泡沫板(EPS板)，挤塑聚苯乙烯塑料泡沫板(XPS板)，岩棉板等复合使用，可提高节能防火效果。
5、本发明的水泥聚合物泡沫塑料粉轻体绝热板采用了比例较大的工业废弃物，为可再生资源利用产品，有利于环保；且对人体无危害，无污染。
6、本发明是一种防火节能效果显著的保温材料，适宜用于建筑内外墙、屋面、地面保温，各类保温屋面板、楼层板、墙板的绝热芯材，管道的保温制品、防火隔离带等。
具体实施方式
实施例一：
一种水泥聚合物泡沫塑料粉轻体绝热板按重量份配比：
硫铝酸盐水泥100份、        II级粉煤灰60份、
硅藻土15份、
醋酸乙烯酯与乙烯共聚胶粉(Vac/E)2份、
羟丙基甲基纤维素醚0.8份、  保温隔热泡沫粉55份、
硅烷基憎水剂0.3份、        水150份。
实施例二：
一种水泥聚合物泡沫塑料粉轻体绝热板按重量份配比：
普通硅酸盐水泥100份、       I级粉煤灰40份、
硅藻土10份、                聚乙烯醇胶粉1份、
甲基纤维素醚0.5份、         硬脂酸钙憎水剂0.1份、
脲醛泡沫塑料粉40份、        亚硝酸钠早强剂2份、
水100份。
实施例三：
一种水泥聚合物泡沫塑料粉轻体绝热板按重量份配比：
铁铝酸盐水泥100份、          II级粉煤灰80份、
硅藻土20份、
醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉
(Vac/E/VeoVa)3份
羧甲基羟乙基纤维素醚1份      硫酸钠早强剂3份
硬脂酸铝憎水剂0.5份、        聚丙烯纤维0.1份、
保温隔热泡沫粉80份、         水200份。
实施例四：
一种水泥聚合物泡沫塑料粉轻体绝热板按重量份配比：
硫铝酸盐水泥100份、    I级粉煤灰60份、
硅藻土15份、
醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉(Vac/VeoVa)胶粉2份、
羟丙基甲基纤维素纤维素醚0.8份、    聚丙烯纤维0.2份、
有机硅憎水剂0.3份、                脲醛泡沫塑料粉55份、
聚苯颗粒10份、    萘系减水剂0.6份
水150份。
实施例五：
一种水泥聚合物泡沫塑料粉轻体绝热板按重量份配比：
高铝水泥100份、        I级粉煤灰60份、
硅藻土15份、
醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉(Vac/VeoVa)胶粉2份、
羟丙基甲基纤维素纤维素醚0.8份、  聚羧酸减水剂0.4份
有机硅憎水剂0.3份、              甲酸钙早强剂1.5份、
聚丙烯纤维0.3份、                聚苯颗粒5份、
脲醛泡沫塑料粉55份、             水150份。
水泥聚合物泡沫塑料粉轻体绝热板的制备方法：将上述比例的材料混合搅拌均匀注入模型内加压0.1～1MPa成型为厚度20～200mm厚的绝热板或50～200mm厚的空腔结构绝热板，也可直接浇筑在模框内成型，常温或加温40～80℃养护而成。
实施例1～4的成型、养护方式及主要技术指标如下表：
Figure BSA00000205671000061

Claims (3)

1.一种水泥聚合物泡沫塑料粉轻体绝热板，其特征在于：包括以下原材料
按重量份配比制成：
水泥100份、         粉煤灰40～80份、
硅藻土10～20份、    可再分散乳胶粉1～3份、
纤维素醚0.5～1份、  泡沫塑料粉40～80份、
憎水剂0.1～0.5份、  水100～200份。
2.如权利要求1所述的水泥聚合物泡沫塑料粉轻体绝热板，其特征在于：所述原材料中还包括早强剂0～3份、聚苯颗粒0～10份、聚丙烯纤维0.1～0.3份或减水剂0.2～0.6份中的一种或两种以上混合。
3.一种水泥聚合物泡沫塑料粉轻体绝热板的制备方法：将上述比例的材料混合搅拌均匀注入模型内加压0.1～1MPa成型为厚度20～200mm厚的绝热板或50～200mm厚的空腔结构绝热板，也可直接浇筑在模框内成型，常温或加温40～80℃养护而成。
CN2010102373982A 2010-07-27 2010-07-27 一种水泥聚合物泡沫塑料粉轻体绝热板及其制备方法 Active CN101948281B (zh)