CN105254259A - 一种高强防火板制备方法 - Google Patents

一种高强防火板制备方法 Download PDF

Info

Publication number
CN105254259A
CN105254259A CN201510802532.1A CN201510802532A CN105254259A CN 105254259 A CN105254259 A CN 105254259A CN 201510802532 A CN201510802532 A CN 201510802532A CN 105254259 A CN105254259 A CN 105254259A
Authority
CN
China
Prior art keywords
parts
stirring
speed
glue
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510802532.1A
Other languages
English (en)
Inventor
张斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAIXING HEQING MACHINERY FITTINGS FACTORY
Original Assignee
TAIXING HEQING MACHINERY FITTINGS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAIXING HEQING MACHINERY FITTINGS FACTORY filed Critical TAIXING HEQING MACHINERY FITTINGS FACTORY
Priority to CN201510802532.1A priority Critical patent/CN105254259A/zh
Publication of CN105254259A publication Critical patent/CN105254259A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高强防火板，将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入羟丙基甲基纤维素5-10份、硅酸镁铝3-6份、有机硅流平剂3-5份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。

Description

一种高强防火板制备方法
技术领域
本发明涉及一种高强防火板及其制备方法。
背景技术
传统的卤素发泡门芯防火性能差，易蹿火、返卤，高温易碳化、变形，且在高温受热过程中会释放有害气体，严重影响其使用寿命、安全性能和稳定性能。
发明内容
针对现有技术中的上述不足，本发明提供了一种轻质、高强，耐火性能优异，高温受热无有害气体，隔音抗震、性能稳定、使用安全、寿命长的高强防火板及其制备方法。
本发明采用的技术方案是：一种高强防火板，其特征在于：按质量份数包括：聚乙烯醇30-40份、硫铝酸盐水泥70-95份、羟丙基甲基纤维素5-10份、硅酸镁铝3-6份、胺醇类阻锈剂2-3份、有机硅流平剂3-5份、PVA短丝20-30份、高铝水泥发泡剂0.5-2份、水100-140份。
一种高强防火板制备方法，其特征在于：首先将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入羟丙基甲基纤维素5-10份、硅酸镁铝3-6份、有机硅流平剂3-5份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
本发明客服了现有卤素防火门填充芯材防火性能差、易蹿火、返卤，高温易碳化、变形，在高温受热过程中会释放有害气体的根本性缺点，具有轻质高强，耐火性能优异，在高温受热过程中无有害产生，强度稳定，容重达340-380kg/m3，不粉化，符合GB8624-2006A1级不燃标准，以及GB/T20285-2006AQ1《材料产烟毒性危险分级》，性能明显优于卤素发泡防火门芯材料。且本发明的制备工艺具有材料浪费少、计量精确，发泡效率高、发泡稳定、效果好的优点，结合PVA短丝和钢丝笼，稳定发泡结构以及整体强度，结合羟丙基甲基纤维素进一步提高使用强度。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种高强防火板，按质量份数包括：聚乙烯醇30份、硫铝酸盐水泥100份、羟丙基甲基纤维素5份、硅酸镁铝3份、胺醇类阻锈剂2份、有机硅流平剂3份、PVA短丝3份、高铝水泥发泡剂0.5份、水100份。
一种高强防火板制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入有机硅流平剂、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度6000RPM，剪切时间5min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1000r/min，搅拌时间10min，最后加入PVA短丝搅拌，搅拌转速800r/min，搅拌时间5min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
实施例二
一种高强防火板，按质量份数包括：聚乙烯醇40份、硫铝酸盐水泥120份、羟丙基甲基纤维素10份、硅酸镁铝6份、胺醇类阻锈剂3份、有机硅流平剂5份、PVA短丝5份、高铝水泥发泡剂2份、水140份。
一种高强防火板制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入有机硅流平剂、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度8000RPM，剪切时间10min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1500r/min，搅拌时间15min，最后加入PVA短丝搅拌，搅拌转速1000r/min，搅拌时间10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
实施例三
一种高强防火板，按质量份数包括：聚乙烯醇35份、硫铝酸盐水泥110份、羟丙基甲基纤维素8份、硅酸镁铝5份、胺醇类阻锈剂2份、有机硅流平剂4份、PVA短丝4份、高铝水泥发泡剂1.5份、水130份。
一种高强防火板制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入有机硅流平剂、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度7000RPM，剪切时间8min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1200r/min，搅拌时间12min，最后加入PVA短丝搅拌，搅拌转速900r/min，搅拌时间8min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。

Claims (1)

1.一种高强防火板制备方法，其特征在于：首先将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入羟丙基甲基纤维素5-10份、硅酸镁铝3-6份、有机硅流平剂3-5份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
CN201510802532.1A 2015-11-19 2015-11-19 一种高强防火板制备方法 Pending CN105254259A (zh)