CN101941049A - 一种石英粉修补膏 - Google Patents
一种石英粉修补膏 Download PDFInfo
- Publication number
- CN101941049A CN101941049A CN 201010271362 CN201010271362A CN101941049A CN 101941049 A CN101941049 A CN 101941049A CN 201010271362 CN201010271362 CN 201010271362 CN 201010271362 A CN201010271362 A CN 201010271362A CN 101941049 A CN101941049 A CN 101941049A
- Authority
- CN
- China
- Prior art keywords
- silica flour
- mixture
- polyvinyl alcohol
- water
- sodium carboxymethylcellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种石英粉修补膏,其组成成分及其重量份比例为:石英粉90-110,活化膨润土2-10,羧甲基纤维素钠混合物0.2-1,聚乙烯醇混合物1-4,其余为水,石英粉修补膏中还包括一种耐火纤维,该耐火纤维占石英粉修补膏的质量百分比为3-6%,耐火纤维为氧化锆耐火纤维、硅酸铝耐火纤维或它们的混合物,羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠10-15,水100,聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇8-10,水100。本发明不仅成分简单、配制操作简易、生产成本较低,而且粘合性较大、耐火性较强、韧性较好。
Description
技术领域
本发明涉及一种涂料,尤其涉及一种石英粉修补膏,具体适用于铸造用砂型的内外表面的修补。
背景技术
随着铸造业的快速发展,对铸造工件表面质量的要求越来越高,对砂型表面涂料的要求也随之增强,一般都必须要求质量均一、粘结性优良、耐水耐热性强,且在常温和高压下性质稳定,易于涂刷,在浇铸时能达到防止粘砂、夹砂等缺陷,从而得到表面光洁的铸件。
中国专利公开号为CN1082466A,公开日为1994年2月23日的发明专利公开了一种以石墨粉、锆英粉、高铝粉、钛渣粉等为耐火粉料,膨润土、硅溶胶、六偏磷酸钠、CMC、高岭土为悬浮剂和粘结剂,以及三氧化二铁、糠醇和水配制成的水基涂料,经检测其流变性、悬浮性、发气性、防开裂性、高温稳定性均优良。虽然该发明在铸造应用中,涂层具有较高强度,手摸、气吹均不掉灰,铸件落砂后其内、外表面剥离效果好,但其成分过于复杂,配制操作繁琐,而且粘合性较弱、耐火性不强,不适合于对铸造用砂型的内外表面进行修补。
发明内容
本发明的目的是克服现有技术中存在的成分过于复杂、配制操作繁琐、粘合性较弱、耐火性不强的缺陷与问题,提供一种成分简单、配制操作简易、粘合性较强、耐火性较强的石英粉修补膏。
为实现以上目的,本发明的技术解决方案是:一种石英粉修补膏,其组成成分及其重量份比例为:石英粉90-110,活化膨润土2-10,羧甲基纤维素钠混合物0.2-1,聚乙烯醇混合物1-4,其余为水。
所述石英粉修补膏的组成成分及其重量份比例为:石英粉100,活化膨润土4-5,羧甲基纤维素钠混合物0.4-0.5,聚乙烯醇混合物1.5-2,其余为水。
所述石英粉修补膏中还包括一种耐火纤维,该耐火纤维占石英粉修补膏的质量百分比为3-6%。
所述耐火纤维为氧化锆耐火纤维、硅酸铝耐火纤维或它们的混合物。
所述羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠10-15,水100。
所述聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇8-10,水100。
与现有技术相比,本发明的有益效果为:
1、由于本发明一种石英粉修补膏中的组成成分及其重量份比例为:石英粉90-110,活化膨润土2-10,羧甲基纤维素钠混合物0.2-1,聚乙烯醇混合物1-4,其余为水,主要原材料只有石英粉、活化膨润土、羧甲基纤维素钠混合物与聚乙烯醇混合物,不仅种类较少,易于配制,而且材料普遍,价格低廉。因此本发明不仅成分简单、配制操作简易,而且生产成本较低。
2、由于本发明一种石英粉修补膏中包括了羧甲基纤维素钠混合物,羧甲基纤维素钠混合物的组成成分及其重量份比例为:羧甲基纤维素钠10-15,水100,该种混合物能够提高涂料中原材料的悬浮作用,便于原材料的均匀混合,提高涂料的粘结性,而且,本发明中还包括聚乙烯醇混合物,其组成成分及其重量份比例为:聚乙烯醇8-10,水100,该聚乙烯醇便于材料之间的混合,能增强涂料的粘结性,此外,本发明中还包括耐火纤维,该耐火纤维占石英粉修补膏的质量百分比为3-6%,该耐火纤维不仅能够提高本发明的耐火性,还能提高本发明的韧性。因此本发明不仅粘合性与耐火性较强,而且韧性较大。
具体实施方式
以下结合具体实施方式对发明作进一步详细的说明
一种石英粉修补膏,其组成成分及其重量份比例为:石英粉90-110,活化膨润土2-10,羧甲基纤维素钠混合物0.2-1,聚乙烯醇混合物1-4,其余为水。
优选石英粉修补膏的组成成分及其重量份比例为:石英粉100,活化膨润土4-5,
羧甲基纤维素钠混合物0.4-0.5,聚乙烯醇混合物1.5-2,其余为水。
优选石英粉修补膏中还包括一种耐火纤维,该耐火纤维占石英粉修补膏的质量百分比为3-6%,进一步优选耐火纤维为氧化锆耐火纤维、硅酸铝耐火纤维或它们的混合物。
优选羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠10-15,水100。
优选聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇8-10,水100。
实施例1:
一种石英粉修补膏,其组成成分及其重量份比例为:石英粉90,活化膨润土10,羧甲基纤维素钠混合物1,聚乙烯醇混合物4,其余为水;石英粉修补膏中还包括硅酸铝耐火纤维,其占石英粉修补膏的质量百分比为6%;羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠15,水100;聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇8,水100。
实施例2:
一种石英粉修补膏,其组成成分及其重量份比例为:石英粉110,活化膨润土2,羧甲基纤维素钠混合物0.2,聚乙烯醇混合物1,其余为水;石英粉修补膏中还包括氧化锆耐火纤维,其占石英粉修补膏的质量百分比为3%;羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠10,水100;聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇10,水100。
实施例3:
一种石英粉修补膏,其组成成分及其重量份比例为:石英粉100,活化膨润土5,羧甲基纤维素钠混合物0.4,聚乙烯醇混合物2,其余为水;石英粉修补膏中还包括氧化锆耐火纤维与硅酸铝耐火纤维的混合物,其占石英粉修补膏的质量百分比为4.5%;羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠12,水100;聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇9,水100。
由上可见,本发明不仅成分简单、配制操作简易、生产成本较低,而且粘合性较大、耐火性较强、韧性较好。
以上所述仅为本发明的较佳实施方式,本发明的保护范围并不以上述实施方式为限,但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化,皆应纳入权利要求书中记载的保护范围内。
Claims (6)
1.一种石英粉修补膏,其特征在于:所述石英粉修补膏的组成成分及其重量份比例为:石英粉90-110,活化膨润土2-10,羧甲基纤维素钠混合物0.2-1,聚乙烯醇混合物1-4,其余为水。
2.根据权利要求1所述的一种石英粉修补膏,其特征在于:所述石英粉修补膏的组成成分及其重量份比例为:石英粉100,活化膨润土4-5,羧甲基纤维素钠混合物0.4-0.5,聚乙烯醇混合物1.5-2,其余为水。
3.根据权利要求1或2所述的一种石英粉修补膏,其特征在于:所述英粉修补膏中还包括一种耐火纤维,该耐火纤维占石英粉修补膏的质量百分比为3-6%。
4.根据权利要求3所述的一种石英粉修补膏,其特征在于:所述耐火纤维为氧化锆耐火纤维、硅酸铝耐火纤维或它们的混合物。
5.根据权利要求4所述的一种石英粉修补膏,其特征在于:所述羧甲基纤维素钠混合物为糊状溶液,其组成成分及其重量份比例为:羧甲基纤维素钠10-15,水100。
6.根据权利要求4或5所述的一种石英粉修补膏,其特征在于:所述聚乙烯醇混合物为胶体状溶液,其组成成分及其重量份比例为:聚乙烯醇8-10,水100。