CN101948273B - 一种石英粉修补涂料 - Google Patents
一种石英粉修补涂料 Download PDFInfo
- Publication number
- CN101948273B CN101948273B CN2010102713842A CN201010271384A CN101948273B CN 101948273 B CN101948273 B CN 101948273B CN 2010102713842 A CN2010102713842 A CN 2010102713842A CN 201010271384 A CN201010271384 A CN 201010271384A CN 101948273 B CN101948273 B CN 101948273B
- Authority
- CN
- China
- Prior art keywords
- sodium carboxymethylcellulose
- parts
- silica flour
- constituent
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉70-80，膨润土10-20，羧甲基纤维素钠混合物5-10，聚乙烯醇5-10，强化颗粒2-8，其余为水；强化颗粒的组成成分及其重量份比例为：不锈钢纤维50-60，氧化铁粉40-50，石墨粉10-20；羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠20-30，水100。本发明不仅成分简单、配制操作简易、生产成本较低，而且强度较大、韧性较强、易均匀混合。
Description
技术领域
本发明涉及一种涂料，尤其涉及一种石英粉修补涂料，具体适用于铸造用砂型的内外表面的涂抹与修补。
背景技术
随着铸造业的快速发展，对铸造工件表面质量的要求越来越高，对砂型表面涂料的要求也随之增强，一般都必须要求质量均一、粘结性优良、耐水耐热性强，且在常温和高压下性质稳定，易于涂刷，在浇铸时能达到防止粘砂、夹砂等缺陷，从而得到表面光洁的铸件。
中国专利公开号为CN1082466A，公开日为1994年2月23日的发明专利公开了一种以石墨粉、锆英粉、高铝粉、钛渣粉等为耐火粉料，膨润土、硅溶胶、六偏磷酸钠、CMC、高岭土为悬浮剂和粘结剂，以及三氧化二铁、糠醇和水配制成的水基涂料，经检测其流变性、悬浮性、发气性、防开裂性、高温稳定性均优良。虽然该发明在铸造应用中，涂层具有较高强度，手摸、气吹均不掉灰，铸件落砂后其内、外表面剥离效果好，但其成分过于复杂，配制操作繁琐，而且机械强度较弱，主要体现在强度较差、韧性较弱，在对铸造用砂型的内外表面进行修补时易发生破裂。
发明内容
本发明的目的是克服现有技术中存在的成分过于复杂、配制操作繁琐、强度较差、韧性较弱的缺陷与问题，提供一种成分简单、配制操作简易、强度较大、韧性较强的石英粉修补涂料。
为实现以上目的，本发明的技术解决方案是：一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉70-80，膨润土10-20，羧甲基纤维素钠混合物5-10，聚乙烯醇5-10，强化颗粒2-8，其余为水。
所述石英粉修补涂料的组成成分及其重量份比例为：石英粉75，膨润土15，羧甲基纤维素钠混合物7.5，聚乙烯醇7.5，强化颗粒5，其余为水。
所述强化颗粒的组成成分及其重量份比例为：不锈钢纤维50-60，氧化铁粉40-50，石墨粉10-20。
所述强化颗粒的组成成分及其重量份比例为：不锈钢纤维55，氧化铁粉45，石墨粉15。
所述羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠20-30，水100。
所述羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠25，水100。
与现有技术相比，本发明的有益效果为：
1、由于本发明一种石英粉修补涂料的组成成分及其重量份比例为：石英粉70-80，膨润土10-20，羧甲基纤维素钠混合物5-10，聚乙烯醇5-10，强化颗粒2-8，其余为水，主要原材料只有石英粉、膨润土、羧甲基纤维素钠混合物、聚乙烯醇与强化颗粒，不仅种类较少，易于配制，而且材料普遍，价格低廉。因此本发明不仅成分简单、配制操作简易，而且生产成本较低。
2、由于本发明一种石英粉修补涂料中包括了强化颗粒，其组成成分及其重量份比例为：不锈钢纤维50-60，氧化铁粉40-50，石墨粉10-20，该强化颗粒可以增强本发明的强度与韧性，而且，在此基础上，考虑到混合均匀性的需要，加入了石墨粉有助于强化颗粒与石英粉的均匀混合，此外，本发明中的羧甲基纤维素钠混合物的组成成分及其重量份比例为：羧甲基纤维素钠20-30，水100，可以看出，羧甲基纤维素钠的用量比一般的用量要大，这是为了配合强化颗粒的使用，以便于发挥强化颗粒的强化效果。因此本发明不仅强度较大、韧性较强，而且易均匀混合。
具体实施方式
以下结合具体实施方式对发明作进一步详细的说明
一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉70-80，膨润土10-20，羧甲基纤维素钠混合物5-10，聚乙烯醇5-10，强化颗粒2-8，其余为水。
优选石英粉修补涂料的组成成分及其重量份比例为：石英粉75，膨润土15，羧甲基纤维素钠混合物7.5，聚乙烯醇7.5，强化颗粒5，其余为水。
优选强化颗粒的组成成分及其重量份比例为：不锈钢纤维50-60，氧化铁粉40-50，石墨粉10-20，进一步优选强化颗粒的组成成分及其重量份比例为：不锈钢纤维55，氧化铁粉45，石墨粉15。
优选羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠20-30，水100，进一步优选羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠25，水100。
实施例1：
一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉70，膨润土20，羧甲基纤维素钠混合物10，聚乙烯醇10，强化颗粒2，其余为水；强化颗粒的组成成分及其重量份比例为：不锈钢纤维60，氧化铁粉40，石墨粉10；羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠20，水100。
实施例2：
一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉80，膨润土10，羧甲基纤维素钠混合物5，聚乙烯醇5，强化颗粒8，其余为水；强化颗粒的组成成分及其重量份比例为：不锈钢纤维50，氧化铁粉50，石墨粉20；羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠30，水100。
实施例3：
一种石英粉修补涂料，其组成成分及其重量份比例为：石英粉75，膨润土15，羧甲基纤维素钠混合物7.5，聚乙烯醇7.5，强化颗粒5，其余为水；强化颗粒的组成成分及其重量份比例为：不锈钢纤维55，氧化铁粉45，石墨粉15；羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠25，水100。
由上可见，本发明不仅成分简单、配制操作简易、生产成本较低，而且强度较大、韧性较强、易均匀混合。
以上所述仅为本发明的较佳实施方式，本发明的保护范围并不以上述实施方式为限，但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化，皆应纳入权利要求书中记载的保护范围内。
Claims (5)
1.一种石英粉修补涂料，所述石英粉修补涂料的组成成分及其重量份比例为：石英粉70-80，膨润土10-20，羧甲基纤维素钠混合物5-10，聚乙烯醇5-10，强化颗粒2-8，其余为水，其特征在于：所述强化颗粒的组成成分及其重量份比例为：不锈钢纤维50-60，氧化铁粉40-50，石墨粉10-20。
2.根据权利要求1所述的一种石英粉修补涂料，其特征在于：所述石英粉修补涂料的组成成分及其重量份比例为：石英粉75，膨润土15，羧甲基纤维素钠混合物7.5，聚乙烯醇7.5，强化颗粒5，其余为水。
3.根据权利要求2所述的一种石英粉修补涂料，其特征在于：所述强化颗粒的组成成分及其重量份比例为：不锈钢纤维55，氧化铁粉45，石墨粉15。
4.根据权利要求3所述的一种石英粉修补涂料，其特征在于：所述羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠20-30，水100。
5.根据权利要求4所述的一种石英粉修补涂料，其特征在于：所述羧甲基纤维素钠混合物为糊状溶液，其组成成分及其重量份比例为：羧甲基纤维素钠25，水100。