CN101927340A - 连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品 - Google Patents

连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品 Download PDF

Info

Publication number
CN101927340A
CN101927340A CN2010101736175A CN201010173617A CN101927340A CN 101927340 A CN101927340 A CN 101927340A CN 2010101736175 A CN2010101736175 A CN 2010101736175A CN 201010173617 A CN201010173617 A CN 201010173617A CN 101927340 A CN101927340 A CN 101927340A
Authority
CN
China
Prior art keywords
nozzle
zirconium
aluminium
continuous casting
refractory products
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010101736175A
Other languages
English (en)
Inventor
王世泰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010101736175A priority Critical patent/CN101927340A/zh
Publication of CN101927340A publication Critical patent/CN101927340A/zh
Pending legal-status Critical Current

Abstract

一种连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，采用刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅粉作耐火原料，酚醛树脂作粘合剂，通过混料、冷等静压成型、车床精加工、涂敷防氧化涂层工序制得成品。本发明连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，无需高温烧制过程，使每吨耐火制品降低成本2000余元，降低了劳动强度，加快了加工周期。

Description

连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品
技术领域
本发明涉及连续铸造技术，特别涉及一种连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品。
背景技术
在连续铸造工艺中，需要用到长水口、浸入式水口及整体塞棒等消耗品，传统技术中，这些消耗品都是采用高温烧制的，生产工艺消耗能源高、产品成品率低、尺寸精度差等问题。
发明内容
为弥补上述不足，本发明提供一种无需烧制的连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品。
本发明连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，包括原料刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅，其生产步骤如下：
1)通过添加免烧剂使酚醛树脂改性；
2)将上述改性酚醛树脂和原料刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅分造粒或混料；
3)冷等静压成型；
4)干燥后车床精加工；
5)涂敷防氧化涂层；
6)成品。
本发明连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，无需800-1200℃的高温烧制过程，使每吨耐火制品降低成本2000余元，降低了劳动强度，加快了加工周期。
具体实施方式
下面结合实施例对本发明连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品作更详尽的说明。
本发明连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，采用刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅中的几种或全部作原料，酚醛树脂作粘合剂。先通过添加免烧剂使酚醛树脂改性；再将改性酚醛树脂和原料刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅粉造粒或混料；放入磨具进行冷等静压成型；干燥后车床精加工，以保证精确尺寸：最后涂敷防氧化涂层即得成品。

Claims (2)

1.一种连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，包括耐火原料，其特征在于：所述耐火制品的生产步骤如下：
1)通过添加免烧剂是酚醛树脂改性；
2)将上述改性酚醛树脂和耐火原料混料；
3)冷等静压成型；
4)干燥后车床精加工；
5)涂敷防氧化涂层；
6)成品。
2.根据权利要求1所述的连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品，其特征在于：所述耐火原料包括刚玉、鳞片石墨、轻烧氧化铝、电熔锆莫来石、电熔稳定氧化锆、碳化硅、金属硅粉中的一种、几种或全部，进行造粒或混料。
CN2010101736175A 2010-05-17 2010-05-17 连铸用铝(锆)炭质长水口、浸入式水口及整体塞棒耐火制品 Pending CN101927340A (zh)