CN101923910B - 一种高温抗蚀导电复合材料 - Google Patents
一种高温抗蚀导电复合材料 Download PDFInfo
- Publication number
- CN101923910B CN101923910B CN 201010278479 CN201010278479A CN101923910B CN 101923910 B CN101923910 B CN 101923910B CN 201010278479 CN201010278479 CN 201010278479 CN 201010278479 A CN201010278479 A CN 201010278479A CN 101923910 B CN101923910 B CN 101923910B
- Authority
- CN
- China
- Prior art keywords
- composite material
- copper
- aluminium
- conducting composite
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高温抗蚀导电复合材料，成份为铜和铝按铝-铜-铝方式复合成泊带。此材料可在400℃-600℃高温下，经受含硫气氛的腐蚀，在一定的时间范围内，保持足够的强度和导电能力。满足特种环境下对导电材料的要求。
Description
技术领域
本发明涉及一种导电复合材料，特别是涉及一种高温抗蚀导电复合材料。
背景技术
关于铝铜复合材料已有较多的研究。在电力导线中为降低重量提高强度采用外铜内铝合金的方式复合成铜铝复合材料。在电化学领域，为利用铜铝不同的电化学性能，制备成铜铝复合板材。近年，热电池技术发展迅速，以往使用的镍带和不锈钢导电极耳已不能满足长寿命与大功率热电池的需求，在热电池放电时要求导电极耳能在400℃-600℃的范围内，含硫高压气氛中保持一定的导电性与强度。
发明内容
本发明所要解决的技术问题是提供一种可以满足长寿命大功率热电池的要求，即在有限的温度与时间(＜60分钟)范围内可以防止高压(-20公斤/cm2)含硫气氛的腐蚀，可以保持足够的强度与导电能力的高温抗蚀导电复合材料。
为了解决上述技术问题，本发明提供的高温抗蚀导电复合材料，铜和铝按铝层-铜层-铝层复合成泊带，所述的铝层的厚度为5-30μm，所述的铜层的厚度为0.1-1.0mm。
本发明与现有技术相比，具有以下特点：以往使用的镍带不能抵抗高温下长时间含硫气体的腐蚀，材料脆化，电阻率急剧提高。不锈钢导电极耳电阻率高，不能满足大功率热电池的需求。本发明可以满足长寿命大功率热电池的要求。即在有限的温度与时间(＜60分钟)范围内可以防止高压(-20公斤/cm2)含硫气氛的腐蚀，可以保持足够的强度与导电能力。其机理在于金属铝在此条件下有很好的抗硫腐蚀能力，金属铜有很好的导电能力，两者有很好的结合强度。适当的厚度配比，可以保证在有限的时间范围内，铜铝互扩散不会显著影响本发明材料的抗蚀与导电能力。
附图说明
图1是本发明的结构示意图。
具体实施方式
下面结合附图和实施例对本发明作进一步说明。
参见图1，泊带上层是第一铝层1，中层是铜层2，下层是第二铝层3，第一铝层1和第二铝层3的厚度为17μm，铜层2的厚度为0.22mm，泊带宽度6mm。
依据不同型号热电池的要求，第一铝层1和第二铝层3的厚度还可以为5μm、10μm、20μm或30μm，铜层2的厚度还可以为0.1mm、0.5mm、0.8mm或1.0mm，泊带宽度还可以为2mm、4mm、6mm或8mm。
本发明的制作过程是：
1、采用冷轧复合方法，将铜和铝按第一铝层1-铜层2-第二铝层3复合轧制成泊带。
2、对泊带进行去应力退火。
3、将泊带包装成卷带。
Claims (1)
1.一种高温抗蚀导电复合材料，其特征是：铜和铝按铝层-铜层-铝层复合成泊带，所述的铝层的厚度为5-30μm，所述的铜层的厚度为0.1-1.0mm。