CN101914746A - 一种不锈钢弹簧氧化着色方法 - Google Patents
一种不锈钢弹簧氧化着色方法 Download PDFInfo
- Publication number
- CN101914746A CN101914746A CN 201010271227 CN201010271227A CN101914746A CN 101914746 A CN101914746 A CN 101914746A CN 201010271227 CN201010271227 CN 201010271227 CN 201010271227 A CN201010271227 A CN 201010271227A CN 101914746 A CN101914746 A CN 101914746A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel spring
- spring
- temperature
- brown
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不锈钢弹簧氧化着色方法，它包括如下步骤：将经过绕制、磨削而成的不锈钢弹簧进行清洗；对不锈钢弹簧进行水洗；将不锈钢弹簧在460～500℃的温度下保温50～70分钟即得棕色弹簧：将不锈钢弹簧在540～580℃的温度下保温50～70分钟即得褐色弹簧。现有的化学方法着色法首先要配溶液，然后进行加热，浸泡等工序，既污染环境，又使工序步骤复杂；本发明只需将不锈钢弹簧成品直接放进多用炉中加热、保温，用电量很少，降低了生产成本；且对环境无污染，操作简便。
Description
技术领域
本发明涉及一种不锈钢弹簧氧化着色方法。
背景技术
现有的不锈钢弹簧着色方法有如下几种：学氧化着色法、电化学氧化着色法、离子沉积氧化物着色法和高温氧化着色法；
各种方法简单概况如下：
(1)化学氧化着色法就是在特定溶液中，通过化学氧化形成膜的颜色，有重铬酸盐法、混合钠盐法、硫化法、酸性氧化法和碱性氧化法。一般“茵科法”(INCO)使用较多，不过要想保证一批产品色泽一致的话，必须用参比电极来控制。
(2)电化学着色法：是在特定溶液中，通过电化学氧化形成膜的颜色。
(3)离子沉积氧化物着色法化学法：就是将不锈钢工件放在真空镀膜机中进行真空蒸发镀。例如：镀钛金的手表壳、手表带，一般是金黄色。这种方法适用于大批量产品加工。因为投资大，成本高，小批量产品不合算。
(4)高温氧化着色法：是在特定的熔盐中，浸入工件保持在一定的工艺参数，使工件形成一定厚度氧化膜，而呈现出各种不同色泽。
以上四种方法都属于化学方法，这四种方法还存在能耗高，时间长、效率低，以及成本高的问题，要用到对环境有污染的化学物质，对环境污染严重。
发明内容
发明目的：本发明的目的克服现有技术的不足，提供一种不锈钢弹簧氧化着色方法，以降低成本，减少环境污染。
技术方案：为了解决上述技术问题，本发明采用了如下的技术方案：
一种不锈钢弹簧氧化着色方法，它包括如下步骤：
(1)将经过绕制、磨削而成的不锈钢弹簧进行清洗；
(2)对不锈钢弹簧进行水洗；
(3)将不锈钢弹簧在460～500℃的温度下保温50～70分钟即得棕色弹簧；将不锈钢弹簧在540～580℃的温度下保温50～70分钟即得褐色弹簧。
其中，步骤(1)中清洗用的水中加有碱，所述的碱与水的质量百分比为1∶10。
其中，步骤(2)中用流动水进行水洗。
其中，步骤(3)中，保温是将不锈钢弹簧放置在多用炉中进行。
其中，步骤(3)中，将不锈钢弹簧在470～490℃的温度下保温50～70分钟即得 棕色弹簧；将不锈钢弹簧在550～570℃的温度下保温50～70分钟即得褐色弹簧。
其中，步骤(3)中，将不锈钢弹簧在480℃的温度下保温60分钟即得棕色弹簧；将不锈钢弹簧在560℃的温度下保温60分钟即得褐色弹簧。
有益效果：现有的化学方法着色法首先要配溶液，然后进行加热，浸泡等工序，既污染环境，又使工序步骤复杂；本发明只需将不锈钢弹簧成品直接放进多用炉中加热、保温，用电量很少，降低了生产成本；且对环境无污染，操作简便。
具体实施方式：
根据下述实施例，可以更好的理解本发明。然而，本领域的技术人员容易理解，实施例所描述的具体的物料配比、工艺条件及其结果仅用于说明本发明，而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1：以生产康明斯6BT棕色弹簧为例。
1、弹簧加工：将经过绕制、磨削而成的不锈钢弹簧进行清洗，其中8112∶水＝1∶10，温度50℃；其中8112是一种固体清洗剂，是由上海斐洁化工有限公司生产；
2、水洗：用流动自来水对不锈钢弹簧进行水洗；
3、将不锈钢弹簧成品放入多用炉中，保温在480℃，保温1小时，得到棕色弹簧。还可以利用企业其他产品加热的温度进行热处理，如结合本企业情况，利用活塞环回火的余温进行热处理，进一步降低了生产成本。
实施例2：以生产道依茨102褐色弹簧为例。
1、弹簧加工：将经过绕制、磨削而成的不锈钢弹簧进行清洗，其中8112∶水＝1∶10，温度50℃；其中8112是一种固体清洗剂，是由上海斐洁化工有限公司生产；
2、水洗：用流动自来水对不锈钢弹簧进行水洗；
3、将不锈钢弹簧成品放入多用炉中，保温在560℃，保温1小时，得到褐色弹簧。还可以利用企业其他产品加热的温度进行热处理，如利用活塞环回火的余温进行热处理，进一步降低了生产成本。
Claims (6)
1.一种不锈钢弹簧氧化着色方法，其特征在于它包括如下步骤：
(1)将经过绕制、磨削而成的不锈钢弹簧进行清洗；
(2)对不锈钢弹簧进行水洗；
(3)将不锈钢弹簧在460～500℃的温度下保温50～70分钟即得棕色弹簧；将不锈钢弹簧在540～580℃的温度下保温50～70分钟即得褐色弹簧。
2.根据权利要求1所述的一种不锈钢弹簧氧化着色方法，其特征在于，步骤(1)中清洗用的水中加有碱，所述的碱与水的质量百分比为1∶10。
3.根据权利要求1所述的一种不锈钢弹簧氧化着色方法，其特征在于，步骤(2)中用流动水进行水洗。
4.根据权利要求1所述的一种不锈钢弹簧氧化着色方法，其特征在于，步骤(3)中，保温是将不锈钢弹簧放置在多用炉中进行。
5.根据权利要求1所述的一种不锈钢弹簧氧化着色方法，其特征在于，步骤(3)中，将不锈钢弹簧在470～490℃的温度下保温50～70分钟即得棕色弹簧；将不锈钢弹簧在550～570℃的温度下保温50～70分钟即得褐色弹簧。
6.根据权利要求1或5所述的一种不锈钢弹簧氧化着色方法，其特征在于，步骤(3)中，将不锈钢弹簧在480℃的温度下保温60分钟即得棕色弹簧；将不锈钢弹簧在560℃的温度下保温60分钟即得褐色弹簧。