CN101914050A - 一种蛋氨酸铜的制备方法 - Google Patents
一种蛋氨酸铜的制备方法 Download PDFInfo
- Publication number
- CN101914050A CN101914050A CN2010102653697A CN201010265369A CN101914050A CN 101914050 A CN101914050 A CN 101914050A CN 2010102653697 A CN2010102653697 A CN 2010102653697A CN 201010265369 A CN201010265369 A CN 201010265369A CN 101914050 A CN101914050 A CN 101914050A
- Authority
- CN
- China
- Prior art keywords
- methionine
- product
- copper
- copper methionine
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种蛋氨酸铜的制备方法，包括以下步骤：(1)成盐反应步骤：将蛋氨酸、碱式碳酸铜、引发剂、水投入反应釜中，搅拌，70℃-80℃加热反应，使二氧化碳溢出，生成蛋氨酸铜；(2)烘干步骤：将分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干，得到的产品过筛，得到蛋氨酸铜产品。本制备方法在生产过程中，使用碱式碳酸铜及引发剂，保证得到颗粒状产品，利于干燥，不用粉碎，避免粉尘的产生，具有实现简单，操作方便的特点，节约了生产设备的投资，提高了生产效率。
Description
技术领域
本发明属于有机化合物制备领域，尤其是一种蛋氨酸铜的制备方法。
背景技术
在动物饲料有机矿物添加剂中，蛋氨酸铜做为一种有机铜矿物添加剂，越来越受到重视，具有广泛的应用前景。蛋氨酸铜的通常生产方法是利用蛋氨酸钠与硫酸铜反应，得到的产品为粘稠状物，进一步处理困难，难以销售。现有制备方法存在的问题是：1、在进一步处理步骤中，烘干时透气性不好，水分蒸发慢，不易干燥，易自阴燃，很危险，需增加自动翻动设备，设备多，复杂生产成本高，难以降低生产成本；2、成品粉碎粉尘很多，企业难以大量生产，不利于企业的发展和经济效益的提高。
发明内容
本发明的目的在于克服现有技术的不足，提供一种蛋氨酸铜的制备方法，本方法节约设备投资、降低成本、解除自燃的危险，得到的产品无需粉碎，避免了大量粉尘的产生。
本发明解决其技术问题是采用以下技术方案实现：
一种蛋氨酸铜的制备方法，包括以下步骤：
(1)成盐反应步骤：将蛋氨酸、碱式碳酸铜、引发剂、水投入反应釜中，搅拌，70℃-80℃加热反应，使二氧化碳溢出，生成蛋氨酸铜；
(2)烘干步骤：将分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干，得到的产品过筛，得到蛋氨酸铜产品。
而且，所述的引发剂为甲酸或乙酸。
而且，所述引发剂与蛋氨酸的摩尔比为0.02-0.05∶1。
而且，所述蛋氨酸、水、碱式碳酸铜的摩尔比为2∶30∶1-1.2。
本发明的优点和积极效果是：
1、本制备方法在投料中，使用蛋氨酸代替蛋氨酸钠，使用碱式碳酸铜代替硫酸铜，得到的产品只有蛋氨酸铜，产品单一，纯度高，呈颗粒状，分离后易于干燥，解除自燃的危险，得到的产品无需粉碎，避免了大量粉尘的产生。
2、本制备方法得到的颗粒状产品，易于干燥，减少防护及设备，节约了设备投资，降低了操作成本。
3、本制备方法在生产过程中，使用碱式碳酸铜及引发剂，保证得到颗粒状产品，利于干燥，不用粉碎，避免粉尘的产生，具有实现简单，操作方便的特点，节约了生产设备的投资，提高了生产效率。
具体实施方式
下面通过具体实施例对本发明作进一步详述，以下实施例只是描述性的，不是限定性的，不能以此限定本发明的保护范围。
实施例1：
一种蛋氨酸铜的制备方法，包括以下步骤：
(1)成盐反应步骤：向一个带有加热装置、电搅拌、温度计的100升反应釜中依次投入蛋氨酸100摩尔、水1500摩尔、甲酸2摩尔，在搅拌下同时加热70-80℃反应，分批加入碱式碳酸铜55摩尔，反应过程中不断有二氧化碳气体逸出，直至没有二氧化碳气体逸出，停止加热，成盐反应完成。
(2)烘干步骤：将离心分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干；24小时后，得到的产品过筛，得到蛋氨酸铜成品，该蛋氨酸铜产品含铜量大于15％。
实施例2：
一种蛋氨酸铜的制备方法，包括以下步骤：
(1)成盐反应步骤：向一个带有加热装置、电搅拌、温度计的100升反应釜中依次投入蛋氨酸100摩尔、水1500摩尔、乙酸3摩尔，在搅拌下同时加热70-80℃反应，分批加入碱式碳酸铜55摩尔，反应过程中不断有二氧化碳气体逸出，直至没有二氧化碳气体逸出，停止加热，成盐反应完成。
(2)烘干步骤：将离心分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干；24小时后，得到的产品过筛，得到蛋氨酸铜成品，该蛋氨酸铜产品含铜量大于15％。
实施例3：
一种蛋氨酸铜的制备方法，包括以下步骤：
(1)成盐反应步骤：向一个带有加热装置、电搅拌、温度计的100升反应釜中依次投入蛋氨酸100摩尔、水1500摩尔、甲酸4摩尔，在搅拌下同时加热70-80℃反应，分批加入碱式碳酸铜55摩尔，反应过程中不断有二氧化碳气体逸出，直至没有二氧化碳气体逸出，停止加热，成盐反应完成。
(2)烘干步骤：将离心分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干；24小时后，得到的产品过筛，得到蛋氨酸铜成品，该蛋氨酸铜产品含铜量大于15％。
Claims (4)
1.一种蛋氨酸铜的制备方法，其特征在于：包括以下步骤：
(1)成盐反应步骤：将蛋氨酸、碱式碳酸铜、引发剂、水投入反应釜中，搅拌，70℃-80℃加热反应，使二氧化碳溢出，生成蛋氨酸铜；
(2)烘干步骤：将分离得到的颗粒状产品，置于上、下透气的不锈钢干燥筛中，放入干燥箱中烘干，得到的产品过筛，得到蛋氨酸铜产品。
2.根据权利要求1所述的蛋氨酸铜的制备方法，其特征在于：所述的引发剂为甲酸或乙酸。
3.根据权利要求1所述的蛋氨酸铜的制备方法，其特征在于：所述引发剂与蛋氨酸的摩尔比为0.02-0.05∶1。
4.根据权利要求1所述的蛋氨酸铜的制备方法，其特征在于：所述蛋氨酸、水、碱式碳酸铜的摩尔比为2∶30∶1-1.2。