CN101912876A - 镁合金板材的生产方法 - Google Patents

镁合金板材的生产方法 Download PDF

Info

Publication number
CN101912876A
CN101912876A CN 201010255819 CN201010255819A CN101912876A CN 101912876 A CN101912876 A CN 101912876A CN 201010255819 CN201010255819 CN 201010255819 CN 201010255819 A CN201010255819 A CN 201010255819A CN 101912876 A CN101912876 A CN 101912876A
Authority
CN
China
Prior art keywords
temperature
rolling
magnesium alloy
slab
rolled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010255819
Other languages
English (en)
Other versions
CN101912876B (zh
Inventor
陈琦
翁文凭
刘国金
吴维治
余铭皋
迟之东
赵奇特
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Nonferrous Metals Processing Technology Co Ltd
Original Assignee
Suzhou Nonferrous Metal Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Nonferrous Metal Research Institute Co Ltd filed Critical Suzhou Nonferrous Metal Research Institute Co Ltd
Priority to CN 201010255819 priority Critical patent/CN101912876B/zh
Publication of CN101912876A publication Critical patent/CN101912876A/zh
Application granted granted Critical
Publication of CN101912876B publication Critical patent/CN101912876B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及镁合金板材的生产方法，首先，通过合金熔炼获得镁合金熔体；将镁合金熔体铸轧出板坯，在230～400℃进行热卷取；然后对铸轧卷坯进行均匀化处理；继而进行轧制，即先将卷坯放入加热炉内加热至250～420℃，再送至轧机卷取机上，采用单机架双卷取的带式法热温轧制方式，通过卷取机上保温罩的加热使卷坯温度在200～420℃，用开卷机进行热开卷，控制轧机的轧辊温度为150～250℃，在板材厚度轧至1.5mm之前，控制卷坯温度在300～400℃，当板材厚度轧至1.5mm后，停止加热，带卷在轧制过程中自然冷却，并控制板材终轧温度为200～220℃，终轧道次加工率为10～15％；对成品进行卷取，卷取温度为200～300℃；最后对成品进行高温退火热处理，退火温度400℃，退火时间30min，而后出炉空冷。

Description

镁合金板材的生产方法
技术领域
本发明涉及一种镁合金板材的生产方法，属于有色金属加工制造技术领域。
背景技术
目前国内外变形镁合金板材大部分采用铸锭热轧开坯的方式来生产，其主要工艺流程为：半连铸铸造→均匀化热处理→锯切铣面→多次加热及多道次粗轧→剪切→多次加热多道次精轧→成品剪切→成品退火。此类镁板生产方式，尤其是镁合金薄板，工序繁多，成材率低，生产效率低，板材力学性能一般，因而无法有效的降低镁合金板材的加工成本，扩大镁合金应用市场。
发明内容
本发明的目的是克服现有技术存在的不足，提供一种镁合金板材的生产方法。
本发明的目的通过以下技术方案来实现：
镁合金板材的生产方法，特点是：首先，通过合金熔炼获得镁合金铸锭；将镁合金铸锭铸轧出铸轧板坯，在230～400℃进行热卷取；然后对铸轧卷坯进行均匀化处理；继而进行轧制，即先将卷坯放入加热炉内加热至250～420℃，再送至轧机卷取机(给轧机配套的卷取机，通常简称轧机卷取机)上，采用单机架双卷取的带式法热温轧制方式，通过卷取机上保温罩的加热使卷坯温度在200～420℃，用开卷机进行热开卷，控制轧机的轧辊温度为150～250℃，在板材厚度轧至1.5mm之前，控制卷坯温度在300～400℃，当板材厚度轧至1.5mm后，停止加热，带卷在轧制过程中自然冷却，并控制板材终轧温度为200～220℃，终轧道次加工率为10～15％；对成品进行卷取，卷取温度为200～300℃；最后对成品进行高温退火热处理，退火温度400℃，退火时间30min，而后出炉空冷。
进一步地，上述的镁合金板材的生产方法，其中，所述卷坯放入加热炉内加热至250～420℃，保温2～4h后再送至轧机卷取机。
本发明技术方案突出的实质性特点和显著的进步主要体现在：
本发明制备的变形镁合金薄板材，成品率高，板材的力学性能也良好，抗拉强度达260～280MPa，屈服强度200～220MPa，延伸率15～20％，平均晶粒尺寸10μm以下。其生产工艺大大减少原有的镁合金板材加工工序，如铣面、锯切和反复加热等，有效的降低了能耗及金属损耗。带式法取代了低效的块式法生产方式，减少了工人的工作强度，极大的提高了生产效率。卷取机配备的保温罩，轧机工作轧辊配置加热装置，根据工艺要求，在轧制过程中达到稳定控制轧制温度的目的。
具体实施方式
本发明通过采用镁合金铸轧供坯，通过单机架双卷取的带式法轧制方式来生产变形镁合金中厚板及薄板，可以极大地缩短板材加工流程，节能减排，提高成材率，降低生产成本。
本发明镁合金板材的生产方法，其工艺流程为：合金熔炼→连续铸轧→卷取→卷坯均匀化处理→卷坯加热→热开卷→带式法热温轧制→成品卷取→成品热处理。首先，通过合金熔炼获得镁合金铸锭；将镁合金铸锭铸轧出铸轧板坯，在230～400℃进行热卷取；然后对铸轧卷坯进行均匀化处(即将金属加热到一定温度然后保温的过程，420℃×2～4h)；继而进行轧制，即先将卷坯放入加热炉内加热至250～420℃，保温2～4h，再送至轧机卷取机(给轧机配套的卷取机，通常简称轧机卷取机)上，采用单机架双卷取的带式法热温轧制方式，通过卷取机上保温罩的加热使卷坯温度在200～420℃，用开卷机进行热开卷，控制轧机的轧辊温度为150～250℃，在板材厚度轧至1.5mm之前，控制卷坯温度在300～400℃，当板材厚度轧至1.5mm后，停止加热，带卷在轧制过程中自然冷却，并控制板材终轧温度为200～220℃，终轧道次加工率为10～15％；对成品进行卷取，卷取温度为200～300℃；最后对成品进行高温退火热处理，退火温度400℃，退火时间30min，而后出炉空冷。
实现带式法热温轧制，采用的单机架双卷取轧制方式，通过卷取机配套的保温罩和轧辊温度来控制实际的轧制温度，以保证带卷的温度保持在合适的加工范围内，通常为200～420℃；卷取机配有保温罩，其采用电加热方式，除了设有穿带口，其余为密闭结构，能够保持带卷在一定温度范围内。
铸轧-卷取供坯，后续单机架或多机架，利用轧机在两个卷取机间对镁合金板材进行往复轧制。卷取机配有一个保温罩，在保证穿带、卸卷等操作前提下，将卷筒及卷坯密闭在其内部，并保持卷坯的温度在所需范围内，并可根据需要调节温度。其铸轧-卷取、后续热温轧制-卷取工艺，要求卷取装置满足可替换要求，即卷筒结构、上/卸卷操作，以及卸卷小车均采用同一结构，带卷可以分别在铸轧卷取机和热温轧制卷取机上进行上卸卷操作。后续带式法热温轧制，可采用单机架双卷取热温轧制，或者多机架连轧。轧机工作辊配置加热装置，将轧辊预热温度控制在120～250℃范围。
实施例
以生产AZ31镁合金薄板，规格为1.0mm×400mm×50m带卷为例
首先铸轧出规格为6mm×400mm的AZ31铸轧板，约350℃直接进行热卷取。然后对铸轧卷坯进行均匀化处理。
进入轧制工序，先将卷坯放在加热炉内加热至420℃，保温2h；然后运送到轧机卷取机上，根据温降情况，适当用保温罩加热，以保证卷坯温度在400～420℃，而后用开卷机进行热开卷操作。轧机轧辊温度为180～200℃。在板材厚度轧至1.5mm以前，卷取机保温罩要保持卷坯温度在300～400℃，当厚度降到1.5mm后，保温罩停止加热，让带卷在轧制过程中自然冷却，并控制板材终轧温度(200～220℃)和终轧道次加工率(10～15％)。成品热处理采用高温退火，400℃×30min，而后出炉空冷。
本发明制备的变形镁合金薄板材，成品率高，板材的力学性能也良好，抗拉强度可到达260～280MPa，屈服强度200～220MPa，延伸率15～20％，平均晶粒尺寸10μm以下。其生产工艺可以大大减少原有的镁合金板材加工工序，如铣面、锯切和反复加热等，有效的降低了能耗及金属损耗。带式法取代了低效的块式法生产方式，减少了工人的工作强度，极大的提高了生产效率。卷取机配备的保温罩，轧机工作轧辊配置加热装置，可以根据工艺要求，在轧制过程中达到稳定控制轧制温度的目的。
需要理解到的是：以上所述仅是本发明的优选实施方式，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (2)

1.镁合金板材的生产方法，其特征在于：首先，通过合金熔炼获得镁合金熔体；将镁合金熔体铸轧出板坯，在230～400℃进行热卷取；然后对铸轧卷坯进行均匀化处理；继而进行轧制，即先将卷坯放入加热炉内加热至250～420℃，再送至轧机卷取机上，采用单机架双卷取的带式法热温轧制方式，通过卷取机上保温罩的加热使卷坯温度在200～420℃，用开卷机进行热开卷，控制轧机的轧辊温度为150～250℃，在板材厚度轧至1.5mm之前，控制卷坯温度在300～400℃，当板材厚度轧至1.5mm后，停止加热，带卷在轧制过程中自然冷却，并控制板材终轧温度为200～220℃，终轧道次加工率为10～15％；对成品进行卷取，卷取温度为200～300℃；最后对成品进行高温退火热处理，退火温度400℃，退火时间30min，而后出炉空冷。
2.根据权利要求1所述的镁合金板材的生产方法，其特征在于：所述卷坯放入加热炉内加热至250～420℃，保温2～4h后再送至轧机卷取机。
CN 201010255819 2010-08-17 2010-08-17 镁合金板材的生产方法 Active CN101912876B (zh)