CN101894624A - 一种铜扁线及其制作方法 - Google Patents
一种铜扁线及其制作方法 Download PDFInfo
- Publication number
- CN101894624A CN101894624A CN 201010231984 CN201010231984A CN101894624A CN 101894624 A CN101894624 A CN 101894624A CN 201010231984 CN201010231984 CN 201010231984 CN 201010231984 A CN201010231984 A CN 201010231984A CN 101894624 A CN101894624 A CN 101894624A
- Authority
- CN
- China
- Prior art keywords
- copper
- copper conductor
- glass fiber
- polyamides
- flat wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种铜扁线及其制作方法，该铜扁线的中心为铜导体，所述铜导体的外表面由内向外依次设有聚酰-酰亚胺复合漆涂层和涤纶玻璃丝烧结层，该铜扁线的制作方法包括如下步骤：将铜导体进行校直和抛光，然后在其表面涂覆聚酰-酰亚胺复合漆涂层，再在所述聚酰-酰亚胺复合漆涂层外面包绕涤纶丝与玻璃纤维纱的混纺体，然后进行烧结，烧结温度范围为290～310℃，所述涤纶丝发生熔融后与玻璃纤维纱形成涤纶玻璃丝烧结层，紧紧包覆在所述聚酰-酰亚胺复合漆涂层的外表面。本发明的铜扁线的外层不需涂绝缘漆，不需烘焙工序，节能环保；耐磨、耐刮性能好；耐温指数高、防潮性能好，可广泛应用于大型火力发电机组和核电机组的定子绕组。
Description
技术领域
本发明涉及一种电线，特别是一种主要用于大型火力发电机组(1000MW)和核电机组(1050MW)的定子绕组用的铜扁线。
背景技术
现有技术中的铜扁线有的将铜扁线先进行漆包之后，再在外层经过双玻璃丝烧结，这样的制作出的铜扁线的耐磨、耐刮性能都不高，若应用于大型火力发电机组和大型核电机组的定子绕组，易损伤漆包层，电性能降低。
发明内容
本发明的目的是提供一种耐磨、耐刮性能高的铜扁线。
为解决上述技术问题，本发明采用如下技术方案：
一种铜扁线，其中心为铜导体，其特征在于：所述的铜导体的外表面设置有聚酰-酰亚胺复合漆涂层，所述的聚酰-酰亚胺复合漆涂层外表面设置有涤纶玻璃丝烧结层，其中，所述的涤纶玻璃丝烧结层为涤纶丝与玻璃纤维纱的混纺体。
一种制作所述的铜扁线的方法，该方法包括步骤如下：
A、对待加工的所述的铜导体进行校直和抛光；
B、在所述的铜导体的外表面涂覆聚酰-酰亚胺复合漆；
C、在涂覆了聚酰-酰亚胺复合漆的所述的铜导体的外表面包绕涤纶丝与玻璃纤维纱的混纺体；
D、将包绕了涤纶丝与玻璃纤维纱的混纺体的所述的铜导体进行烧结，其中，烧结温度高于280℃。
优选地，所述的烧结温度范围为290～310℃。
其中，步骤D中的烧结过程中，所述的涤纶丝与玻璃纤维纱的混纺体中的涤纶丝发生熔融并与玻璃纤维纱形成一体，紧紧包覆在所述的聚酰-酰亚胺复合漆涂层外面。
本发明的有益效果是：
1.由于本发明的铜扁线的外层不需涂覆绝缘漆，不需烘焙，减小了能耗。
2.由于本发明的铜扁线的外层为涤纶丝与玻璃纤维纱的混纺体烧结层，比传统的外层为双玻璃丝烧结层的铜扁线耐磨、耐刮性能都要好。
3.本发明的耐温指数高、防潮性能好、使用寿命长。
附图说明
附图1为本发明的铜扁线的结构示意图。
附图中：1、涤纶玻璃丝烧结层；2、聚酰-酰亚胺复合漆涂层；3、铜导体。
具体实施方式
下面结合附图所示的实施例对本发明的技术方案作以下详细描述：
如附图1所示，本发明的铜扁线的中心为铜导体3，铜导体3的外表面涂有聚酰-酰亚胺复合漆涂层2，在聚酰-酰亚胺复合漆涂层2的外面又包绕有涤纶丝与玻璃纤维丝的混纺纱，再经数控高频烧结在外表面形成一层涤纶玻璃丝烧结层1，聚酰-酰亚胺复合漆涂层2与涤纶玻璃丝烧结层1均为绝缘层。
该铜扁线的制作步骤如下：将铜导体3进行校直和抛光之后，在其外表面涂覆聚酰-酰亚胺复合漆涂层2，再在聚酰-酰亚胺复合漆涂层2的外表面包绕涤纶丝与玻璃纤维丝的混纺纱，然后对其进行烧结，烧结过程中要将烧结温度稳定控制在290℃～310℃之间，在烧结的过程中，涤纶丝与玻璃纤维丝的混纺纱中的涤纶丝(涤纶丝的熔点为258～280℃)发生熔融后与玻璃纤维丝形成一体，紧紧包覆在覆聚酰-酰亚胺复合漆涂层2的外面，得到铜扁线。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (5)
1.一种铜扁线，其中心为铜导体，其特征在于：所述的铜导体的外表面设置有聚酰-酰亚胺复合漆涂层，所述的聚酰-酰亚胺复合漆涂层外表面设置有涤纶玻璃丝烧结层。
2.根据权利要求1所述的一种铜扁线，其特征在于：所述的涤纶玻璃丝烧结层为涤纶丝与玻璃纤维纱的混纺体的烧结形成层。
3.一种制作如权利要求1所述的铜扁线的方法，其特征在于：它包括如下步骤：
A、对待加工的所述的铜导体进行校直和抛光；
B、在所述的铜导体的外表面涂覆聚酰-酰亚胺复合漆；
C、在涂覆了聚酰-酰亚胺复合漆的所述的铜导体的外表面包绕涤纶丝与玻璃纤维纱的混纺体；
D、将包绕了涤纶丝与玻璃纤维纱的混纺体的所述的铜导体进行烧结，其中，烧结温度高于280℃。
4.根据权利要求3所述的一种制作铜扁线的方法，其特征在于：所述的烧结温度范围为290～310℃。
5.根据权利要求3所述的一种制作铜扁线的方法，其特征在于：步骤D中的烧结过程中，所述的涤纶丝与玻璃纤维纱的混纺体中的涤纶丝发生熔融并与玻璃纤维纱形成一体，紧紧包覆在所述的聚酰-酰亚胺复合漆涂层外面。