CN101892579B - Production method of single-side reticulated power-point adhesive lining cloth - Google Patents

Production method of single-side reticulated power-point adhesive lining cloth Download PDF

Info

Publication number
CN101892579B
CN101892579B CN2010102180759A CN201010218075A CN101892579B CN 101892579 B CN101892579 B CN 101892579B CN 2010102180759 A CN2010102180759 A CN 2010102180759A CN 201010218075 A CN201010218075 A CN 201010218075A CN 101892579 B CN101892579 B CN 101892579B
Authority
CN
China
Prior art keywords
agent
kiering
motor vehicle
speed
lining cloth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2010102180759A
Other languages
Chinese (zh)
Other versions
CN101892579A (en
Inventor
唐新东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yiyi New Material Co.,Ltd.
Original Assignee
NANTONG YIYI INTERLINING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG YIYI INTERLINING CO Ltd filed Critical NANTONG YIYI INTERLINING CO Ltd
Priority to CN2010102180759A priority Critical patent/CN101892579B/en
Publication of CN101892579A publication Critical patent/CN101892579A/en
Application granted granted Critical
Publication of CN101892579B publication Critical patent/CN101892579B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a production method of single-side reticulated power-point adhesive lining cloth, comprising the following steps of: selecting foundation cloth, preprocessing, resisting the shrinkage of resin, combining, pre-shrinking, and the like. The size of the adhesive lining cloth has high stability, the change of horizontal and vertical water-washing sizes and a dry-heat size is within 1 percent, the washing size of the lining cloth is changed into 4-5 levels after the lining cloth is adhered, and the free formaldehyde content is within 75mg/kg (JISL-1041). The single-side reticulated power-point adhesive lining cloth produced by using the production method has even production reticulated points, high ventilation property, no leak points, no leak coating and soft hand feeling and increases the clothes ventilation property and the wear comfort property.

Description

The production method of single-side reticulated power-point adhesive lining cloth
Technical field:
The present invention relates to a kind of production method of binding lining.
Background technology:
Existing binding lining exists crawling to spare, have leak source, holiday phenomenon, has defective in inventions such as content of formaldehyde, shrinkage, comfortablenesses.
Summary of the invention:
The object of the present invention is to provide the production method of the single-side reticulated power-point adhesive lining cloth that a kind of DIMENSIONAL STABILITY is good, comfortableness is good.
Technical solution of the present invention is:
A kind of production method of single-side reticulated power-point adhesive lining cloth is characterized in that: comprise the following steps: successively
(1) base fabric is selected: base fabric adopts cotton textiles, polyester-cotton blend, pure washing or woven fabric, knitted fabric or bondedfibre fabric that viscose is processed into;
(2) pre-treatment: with base fabric stitch, singe through the stand successively, cold dome destarch, kiering, the processing of scouringing and bleaching; The process conditions of wherein singing when handling are: vapourizing temperature is 75～80 ℃, and steam pressure is 0.26～0.28Mpa, and the speed of a motor vehicle is 110m/min, and burner quantity is 2 positive 2 anti-, the water fire extinguishing; Cotton textiles, polyester-cotton blend, the pure polyester fabric of yarn count more than 30S is without the processing of singing;
The process conditions that the cold dome destarch is handled are: caustic soda 15～35g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzymes, 6～12g/l, H 2O 27～18g/l, stabilizing agent 4～10g/l, the speed of a motor vehicle 30～50m/min banks up the time: sealing running 24 hours, 90～95 ℃ of hot water wash of 1～3 lattice;
The process conditions that kiering is handled are: padding liquid consists of: caustic soda 10～15g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzymes, 6～10g/l, H 2O 2The water of 5～8g/l, stabilizing agent 4～10g/l and surplus; Kiering liquid is formed and treatment conditions are: the water of caustic soda 15～16g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzyme 4～5g/l and surplus, the speed of a motor vehicle 30～50m/min, the time 120min that banks up, 90～95 ℃ of hot water wash of 1～4 lattice;
The process conditions of handling of scouringing and bleaching are: H 2O 28～10g/l, scouring agent 2～4g/l, chelating agent 3g/l, 188 kiering enzymes, 6～10g/l, stabilizing agent 4～10g/l, pH value are 10.5～11, the speed of a motor vehicle 30～50m/min, the time 60min that banks up, 100 ℃ of steam temperatures, 90～95 ℃ of hot water wash of 1～4 lattice;
For bondedfibre fabric, then without pre-treatment;
Described intercalating agent is triethanolamine or its condensation product;
The scouring agent molecule is:
Figure BSA00000170854600021
The stabilizing agent molecular formula is: C 18H 37(OCH 2CH 2) nOH;
(3) the shrinkproof processing of resin: through padding, tentering, baking typing and handle, the process conditions of wherein padding processing are: low formaldehyde resin 70～175g/l, PA-116 softener are 80～125g/l, MgCl successively 212.5～31.5g/l, JFC bleeding agent 1.25g/l, CY-100 formaldehyde catching agent 7～15g/l, pH value 5～5.5, the speed of a motor vehicle 35～60m/min, the mode of padding is 2 to soak 2 and roll, rolling point pressure is 0.3～0.32Mpa; The process conditions that bake processing are: the speed of a motor vehicle 35～60m/min, 148～152 ℃ of drying room temperature;
Described low formaldehyde resin is the DMDHEU resin; Described PA-116 softener molecular formula is:
Figure BSA00000170854600031
The molecular formula of described CY-100 formaldehyde catching agent is:
Figure BSA00000170854600032
Bondedfibre fabric is without the shrinkproof processing of resin;
(4) compound: adopt compounding machine through preliminary drying, compound, bake, cooling processing, the preliminary drying temperature is that 192 ℃, combined temp are that 220 ℃, baking temperature are 175 ℃ to roll point pressure be 0.1-0.15Mpa, the composite roll gap is 0.1-0.5mm.
Also handle through preshrunk after compound, preshrunk is handled and is adopted sanforizer, comprises into cloth, spraying dewing, three roller rubber blanket preshrunks, cropping step successively, the speed of a motor vehicle is 25～35m/min, rubber blanket distortion thickness is 5-10mm, and steam pressure is 0.1-0.4Mpa, and the bearing roller temperature is 90-95 ℃.
When scouringing and bleaching 90～95 ℃ of hot water wash of usefulness of handling, add the lemon acid for adjusting pH value in the water, control cloth cover pH value is between 5.0～7.5.
DIMENSIONAL STABILITY of the present invention is good, in length and breadth to washing change in size, xeothermic change in size all in 1%, bonding back washing size is changed to the 4-5 level, free formaldehyde content is in 75mg/kg (JISL-1041); The product site that the present invention produces is even, good permeability, and no leak source, holiday phenomenon are soft, has improved the gas permeability and the wearing comfortableness of ready-made clothes.
The invention will be further described below in conjunction with embodiment.
The specific embodiment:
A kind of production method of single-side reticulated power-point adhesive lining cloth comprises the following steps: successively
(1) base fabric is selected: base fabric adopts cotton textiles, polyester-cotton blend, pure washing or woven fabric, knitted fabric or bondedfibre fabric that viscose is processed into;
(2) pre-treatment: with base fabric stitch, singe through the stand successively, cold dome destarch, kiering, the processing of scouringing and bleaching; The process conditions of wherein singing when handling are: vapourizing temperature is 75～80 ℃, and steam pressure is 0.26～0.28Mpa, and the speed of a motor vehicle is 110m/min, and burner quantity is 2 positive 2 anti-, the water fire extinguishing; Cotton textiles, polyester-cotton blend, the pure polyester fabric of yarn count more than 30S is without the processing of singing;
The process conditions that the cold dome destarch is handled are: caustic soda 15～35g/l (routine 15g/l, 25g/l, 35g/l), scouring agent 4～8g/l (routine 4g/l, 6g/l, 8g/l), chelating agent 3g/l, 188 kiering enzymes, 6～12g/l (routine 6g/l, 9g/l, 12g/l), H 2O 27～18g/l (routine 7g/l, 12g/l, 18g/l), stabilizing agent 4～10g/l (routine 4g/l, 7g/l, 10g/l), the speed of a motor vehicle 30～50m/min (example 30 minutes, 40 minutes, 50 minutes) banks up the time: sealing running 24 hours, 90～95 ℃ of hot water wash of 1～3 lattice;
The process conditions that kiering is handled are: padding liquid consists of: caustic soda 10～15g/l (routine 10g/l, 12g/l, 15g/l), scouring agent 4～8g/l (routine 4g/l, 6g/l, 8g/l), chelating agent 3g/l, 188 kiering enzymes, 6～10g/l (routine 6g/l, 8g/l, 10g/l), H 2O 2The water of 5～8g/l (routine 5g/l, 7g/l, 8g/l), stabilizing agent 4～10g/l (routine 4g/l, 7g/l, 10g/l) and surplus; Kiering liquid is formed and treatment conditions are: the water of caustic soda 15～16g/l, scouring agent 4～8g/l (routine 4g/l, 6g/l, 8g/l), chelating agent 3g/l, 188 kiering enzyme 4～5g/l and surplus, the speed of a motor vehicle 30～50m/min (example 30 minutes, 40 minutes, 50 minutes), the time 120min that banks up, 90～95 ℃ of hot water wash of 1～4 lattice;
The process conditions of handling of scouringing and bleaching are: H 2O 28～10g/l (routine 8g/l, 9g/l, 10g/l), scouring agent 2～4g/l, chelating agent 3g/l, 188 kiering enzymes, 6～10g/ (routine 6g/l, 8g/l, 10g/l) l, stabilizing agent 4～10g/l, pH value are 10.5～11, the speed of a motor vehicle 30～50m/min (example 30 minutes, 40 minutes, 50 minutes), time 60min banks up, 100 ℃ of steam temperatures, 90～95 ℃ of hot water wash of 1～4 lattice, and in water, adding the lemon acid for adjusting pH value, control cloth cover pH value is between 5.0～7.5.
For bondedfibre fabric, then without pre-treatment;
Described intercalating agent is triethanolamine or its condensation product;
The scouring agent molecule is:
Figure BSA00000170854600051
The stabilizing agent molecular formula is: C 18H 37(OCH 2CH 2) nOH;
(3) the shrinkproof processing of resin: through padding, tentering, baking typing and handle, the process conditions of wherein padding processing are: low formaldehyde resin 70～175g/l (routine 70g/l, 130g/l, 175g/l), PA-116 softener are 80～125g/l (routine 80g/l, 100g/l, 125g/l), MgCl successively 212.5～31.5g/l (routine 13g/l, 23g/l, 31g/l), JFC bleeding agent 1.25g/l, CY-100 formaldehyde catching agent 7～15g/l (routine 7g/l, 12g/l, 15g/l), pH value 5～5.5, the speed of a motor vehicle 35～60m/min (example 35 minutes, 45 minutes, 60 minutes), the mode of padding is 2 to soak 2 and roll, and rolling point pressure is 0.3～0.32Mpa; The process conditions that bake processing are: the speed of a motor vehicle 35～60m/min (example 35 minutes, 45 minutes, 60 minutes), 148～152 ℃ of drying room temperature;
Described low formaldehyde resin is the DMDHEU resin; Described PA-116 softener molecular formula is:
Figure BSA00000170854600052
The molecular formula of described CY-100 formaldehyde catching agent is:
Figure BSA00000170854600061
Bondedfibre fabric is without the shrinkproof processing of resin;
(4) compound: adopt compounding machine through preliminary drying, compound, bake, cooling processing, the preliminary drying temperature is that 192 ℃, combined temp are that 220 ℃, baking temperature are 175 ℃ to roll point pressure be 0.1-0.15Mpa, the composite roll gap is 0.1-0.5mm.
Also handle through preshrunk after compound, preshrunk is handled and is adopted sanforizer, comprises into cloth, spraying dewing, three roller rubber blanket preshrunks, cropping step successively, the speed of a motor vehicle is 25～35m/min, rubber blanket distortion thickness is 5-10mm, and steam pressure is 0.1-0.4Mpa, and the bearing roller temperature is 90-95 ℃.

Claims (3)

1. the production method of a single-side reticulated power-point adhesive lining cloth is characterized in that: comprise the following steps: successively
(1) base fabric is selected: base fabric adopts cotton textiles, polyester-cotton blend, pure washing or woven fabric, knitted fabric or bondedfibre fabric that viscose is processed into;
(2) pre-treatment: with base fabric stitch, singe through the stand successively, cold dome destarch, kiering, the processing of scouringing and bleaching; The process conditions of wherein singing when handling are: vapourizing temperature is 75～80 ℃, and steam pressure is 0.26～0.28Mpa, and the speed of a motor vehicle is 110m/min, and burner quantity is 2 positive 2 anti-, the water fire extinguishing; Cotton textiles, polyester-cotton blend, the pure polyester fabric of yarn count more than 30S is without the processing of singing;
The process conditions that the cold dome destarch is handled are: caustic soda 15～35g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzymes, 6～12g/l, H 2O 27～18g/l, stabilizing agent 4～10g/l, the speed of a motor vehicle 30～50m/min banks up the time: sealing running 24 hours, 90～95 ℃ of hot water wash of 1～3 lattice;
The process conditions that kiering is handled are: padding liquid consists of: caustic soda 10～15g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzymes, 6～10g/l, H 2O 2The water of 5～8g/l, stabilizing agent 4～10g/l and surplus; Kiering liquid is formed and treatment conditions are: the water of caustic soda 15～16g/l, scouring agent 4～8g/l, chelating agent 3g/l, 188 kiering enzyme 4～5g/l and surplus, the speed of a motor vehicle 30～50m/min, the time 120min that banks up, 90～95 ℃ of hot water wash of 1～4 lattice;
The process conditions of handling of scouringing and bleaching are: H 2O 28～10g/l, scouring agent 2～4g/l, chelating agent 3g/l, 188 kiering enzymes, 6～10g/l, stabilizing agent 4～10g/l, pH value are 10.5～11, the speed of a motor vehicle 30～50m/min, the time 60min that banks up, 100 ℃ of steam temperatures, 90～95 ℃ of hot water wash of 1～4 lattice;
For bondedfibre fabric, then without pre-treatment;
Described intercalating agent is triethanolamine or its condensation product;
The scouring agent molecule is:
The stabilizing agent molecular formula is: C 18H 37(OCH 2CH 2) nOH;
(3) the shrinkproof processing of resin: through padding, tentering, baking typing and handle, the process conditions of wherein padding processing are: low formaldehyde resin 70～175g/l, PA-116 softener are 80～125g/l, MgCl successively 212.5～31.5g/l, JFC bleeding agent 1.25g/l, CY-100 formaldehyde catching agent 7～15g/l, pH value 5～5.5, the speed of a motor vehicle 35～60m/min, the mode of padding is 2 to soak 2 and roll, rolling point pressure is 0.3～0.32Mpa; The process conditions that bake processing are: the speed of a motor vehicle 35～60m/min, 148～152 ℃ of drying room temperature;
Described low formaldehyde resin is the DMDHEU resin; Described PA-116 softener molecular formula is:
Figure FDA0000085017510000022
The molecular formula of described CY-100 formaldehyde catching agent is:
Figure FDA0000085017510000023
Bondedfibre fabric is without the shrinkproof processing of resin;
(4) compound: adopt compounding machine through preliminary drying, compound, bake, cooling processing, the preliminary drying temperature is that 192 ℃, combined temp are that 220 ℃, baking temperature are 175 ℃, to roll point pressure be 0.1-0.15Mpa, the composite roll gap is 0.1-0.5mm.
2. the production method of single-side reticulated power-point adhesive lining cloth according to claim 1, it is characterized in that: also handle after compound through preshrunk, preshrunk is handled and is adopted sanforizer, comprise into cloth, spraying dewing, three roller rubber blanket preshrunks, cropping step successively, the speed of a motor vehicle is 25～35m/min, rubber blanket distortion thickness is 5-10mm, and steam pressure is 0.1-0.4Mpa, and the bearing roller temperature is 90-95 ℃.
3. the production method of single-side reticulated power-point adhesive lining cloth according to claim 1 and 2 is characterized in that: when scouringing and bleaching 90～95 ℃ of hot water wash of usefulness of handling, add the lemon acid for adjusting pH value in the water, control cloth cover pH value between 5.0～7.5.
CN2010102180759A 2010-06-29 2010-06-29 Production method of single-side reticulated power-point adhesive lining cloth Active CN101892579B (en)