CN101871248A - 一种反应型高分子防水卷材 - Google Patents
一种反应型高分子防水卷材 Download PDFInfo
- Publication number
- CN101871248A CN101871248A CN 201010191736 CN201010191736A CN101871248A CN 101871248 A CN101871248 A CN 101871248A CN 201010191736 CN201010191736 CN 201010191736 CN 201010191736 A CN201010191736 A CN 201010191736A CN 101871248 A CN101871248 A CN 101871248A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- reactive polymer
- waterproofing coiled
- polymer waterproofing
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种反应型高分子防水卷材，该防水卷材包括包括胎膜层、反应型复合胶层和防粘隔离膜层，反应型复合胶层覆设在胎膜层的表面上，而防粘隔离膜层覆设在反应型复合胶层的另一表面上；所述的反应型复合胶按重量百分比包括：SIS型热熔胶85.0％～92.0％、滑石粉3.0％～5.0％、复合矿粉2.0％～3.5％、气相二氧化硅1.0％～2.5％、硅烷偶联剂0.5％～2.0％、纳米碳酸钙0.5％～2.0％。本防水卷材在施工中能够与现浇的混凝土基体发生化学交联并一同固化，从根本上杜绝“窜水”现象，此外还具有高强度、高韧性、耐老化和使用寿命长等优点。
Description
技术领域
本发明涉及一种建筑用防水卷材，更具体地说，本发明涉及一种反应型高分子防水卷材。
背景技术
目前，在建筑行业中大量使用的防水卷材多为改性沥青防水卷材，这类防水卷材普遍存在强度较低，易破损渗漏；卷材与混凝土墙体之间存在缝隙，易发生“窜水”；以及耐候性较差，使用寿命短等问题，容易引起严重的建筑工程质量问题并且很难修复。此外，这类防水卷材不能有效地防止煤气、沼气等气体的泄漏，也不能防止由于屋面种植的植物根穿刺而引起的渗漏。再者，这类防水卷材在未做保护层之前，不能在其上放置骨架钢筋，否则会对防水卷材造成破坏而失去防水作用。为了克服上述的这些问题，人们开始对现有的防水卷材进行改进，以提高其防水性能。
发明内容
本发明的目的在于提供一种反应型高分子防水卷材，该反应型高分子防水卷材具有高强度、高韧性、耐老化等优点，并且能够与现浇的混凝土发生化学反应而一同固化，从而能够克服现有防水卷材的缺陷。
本发明的目的是通过以下技术方案实现的：
一种反应型高分子防水卷材，包括胎膜层、反应型复合胶层和防粘隔离膜层，所述的反应型复合胶层覆设在所述胎膜层的表面上，所述的防粘隔离膜层覆设在所述反应型复合胶层的另一表面上。
在本发明中，所述的胎膜选自高密度聚乙烯(HDPE)、低密度聚乙烯(LDPE)、三元乙丙橡胶(EPDM)、聚氯乙烯(PVC)、乙烯-醋酸乙烯共聚物(EVA)、乙烯共聚物改性沥青树脂(ECB)或者聚烯烃热塑性弹性体(TPO)等中的一种，所述胎膜层的厚度为0.75mm～1.00mm。
在本发明中，所述的防粘隔离膜层选自聚乙烯薄膜或者经硅油处理的牛皮纸。
在本发明中，所述的反应型复合胶按重量百分比包括以下组分：
SIS型热熔胶 85.0％～92.0％；
滑石粉 3.0％～5.0％；
复合矿粉 2.0％～3.5％；
气相二氧化硅 1.0％～2.5％；
硅烷偶联剂 0.5％～2.0％；
纳米碳酸钙 0.5％～2.0％。
所述的SIS型热熔胶为苯乙烯-异戊二烯嵌段聚合物；所述的复合矿粉是由硅酸二钙、铝酸三钙和铁铝酸四钙混合而成的；所述的硅烷偶联剂为氨丙基三乙氧基硅烷；而所述的滑石粉是粒度在400目以上的滑石粉。
在本发明所述的反应型复合胶中，所采用的SIS型热熔胶是一种与胎膜基材(如HDPE、LDPE、EPDM、PVC、EVA、ECB、TPO等)有极强粘结力的柔韧性热熔胶；所采用的硅烷偶联剂能够增强本反应型复合胶与胎膜基材和混凝土之间的粘结力；而所采用的复合矿粉、滑石粉、气相二氧化硅和纳米碳酸钙能够与现浇的混凝土发生水合反应，从而使防水卷材与混凝土结合成一体，其中复合矿粉是主要的反应物质。此外，所采用的滑石粉还能够改善覆膜过程中刮涂的平顺性和流畅性，所采用的气相二氧化硅还能够增强本反应型复合胶的硬度和内聚强度等物理指标；而所采用的纳米碳酸钙还能够改善本反应型复合胶的初粘性能。
本发明所述的反应型高分子防水卷材是一种能够与现浇的混凝土基体发生化学反应的新型防水卷材，亦称为CRC防水卷材(Chemistry Reaction Coiled-Material)。本反应型高分子防水卷材在施工中能够与现浇的混凝土基体发生化学交联并一同固化，从而与混凝土基体形成一体，能够完全防止水分渗入防水卷材与结构之间的间隙，从根本上杜绝“窜水”现象。本反应型高分子防水卷材采用了HDPE、LDPE、EPDM、PVC、EVA、ECB、TPO等作为胎膜基材，这些胎膜基材具有高强度、高韧性、耐老化等优点，能够有效地防止植物根穿刺以及回填土中的废玻璃、废铁屑、废瓷砖等锋利杂物对防水卷材划切造成破坏。此外，本反应型高分子防水卷材具有优异的耐候性，使用寿命长，还可以有效地防止煤气、沼气等易燃易爆气体泄漏，并且不受基底层位移的影响，不需要使用保护板，可在其上行走，也可以在垫上支撑或垫块后直接放置浇注骨架钢筋。
具体实施方式
实施例一：本发明所述的反应型复合胶的制备
SIS型热熔胶 85.0％～92.0％；滑石粉 3.0％～5.0％；
复合矿粉 2.0％～3.5％； 气相二氧化硅 1.0％～2.5％；
硅烷偶联剂 0.5％～2.0％； 纳米碳酸钙 0.5％～2.0％。
在500L反应釜中按配方量加入SIS型热熔胶，打开加热装置，升温至160℃～165℃；按配方量加入滑石粉、复合矿粉、气相二氧化硅和纳米碳酸钙，开动搅拌机，匀速搅拌1.5h～2h，直至粉料与热熔胶充分混合均匀；关闭加热装置，自然降温至120℃～130℃，按配方量加入硅烷偶联剂，再匀速搅拌0.5h；用覆盖有隔离纸的不锈钢盘接取出料，待接料盘中的胶料完全冷却至室温后，用硅油型隔离纸包好，备用。
实施例二：本发明所述的反应型高分子防水卷材的制备
将实施例一制得的反应型复合胶投入温度在130℃～135℃的溶胶缸中，通过供胶泵和涂布模头，将该反应型复合胶均匀涂布在高密度聚乙烯(HDPE)薄膜基材的一个表面上，其中，涂布模头的温度控制在110℃～115℃之间。随后采用聚乙烯薄膜进行覆膜处理，将聚乙烯薄膜覆设在反应型复合胶层的另一个表面上，冷却后即得到本发明所述的反应型高分子防水卷材。
Claims (9)
1.一种反应型高分子防水卷材，其特征在于：包括胎膜层、反应型复合胶层和防粘隔离膜层，所述的反应型复合胶层覆设在所述胎膜层的表面上，所述的防粘隔离膜层覆设在所述反应型复合胶层的另一表面上。
2.根据权利要求1所述的反应型高分子防水卷材，其特征在于，所述的反应型复合胶按重量百分比包括以下组分：
SIS型热熔胶 85.0％～92.0％；
滑石粉 3.0％～5.0％；
复合矿粉 2.0％～3.5％；
气相二氧化硅 1.0％～2.5％；
硅烷偶联剂 0.5％～2.0％；
纳米碳酸钙 0.5％～2.0％。
3.根据权利要求2所述的反应型高分子防水卷材，其特征在于：所述的SIS型热熔胶为苯乙烯-异戊二烯嵌段聚合物。
4.根据权利要求2所述的反应型高分子防水卷材，其特征在于：所述的复合矿粉由硅酸二钙、铝酸三钙和铁铝酸四钙混合而成。
5.根据权利要求2所述的反应型高分子防水卷材，其特征在于：所述的硅烷偶联剂为氨丙基三乙氧基硅烷。
6.根据权利要求2所述的反应型高分子防水卷材，其特征在于：所述的滑石粉是粒度在400目以上的滑石粉。
7.根据权利要求1所述的反应型高分子防水卷材，其特征在于：所述的胎膜选自高密度聚乙烯、低密度聚乙烯、三元乙丙橡胶、聚氯乙烯、乙烯-醋酸乙烯共聚物、乙烯共聚物改性沥青树脂或者聚烯烃热塑性弹性体中的一种。
8.根据权利要求1所述的反应型高分子防水卷材，其特征在于：所述的胎膜层的厚度为0.75mm～1.00mm。
9.根据权利要求1所述的反应型高分子防水卷材，其特征在于：所述的防粘隔离膜层选自聚乙烯薄膜或者经硅油处理的牛皮纸。