CN1468929A - 一种防水卷材及其生产方法 - Google Patents

一种防水卷材及其生产方法 Download PDF

Info

Publication number
CN1468929A
CN1468929A CNA021326258A CN02132625A CN1468929A CN 1468929 A CN1468929 A CN 1468929A CN A021326258 A CNA021326258 A CN A021326258A CN 02132625 A CN02132625 A CN 02132625A CN 1468929 A CN1468929 A CN 1468929A
Authority
CN
China
Prior art keywords
styrene
waterproof roll
butadiene
rubber
filler
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA021326258A
Other languages
English (en)
Other versions
CN1185321C (zh
Inventor
亓玉台
高佑海
王凤秀
宋若霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Petroleum and Chemical Corp
Liaoning Shihua University
Original Assignee
China Petroleum and Chemical Corp
Liaoning Shihua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Petroleum and Chemical Corp, Liaoning Shihua University filed Critical China Petroleum and Chemical Corp
Priority to CNB021326258A priority Critical patent/CN1185321C/zh
Publication of CN1468929A publication Critical patent/CN1468929A/zh
Application granted granted Critical
Publication of CN1185321C publication Critical patent/CN1185321C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明涉及一种制造复合改性聚合物防水卷材及生产方法。该复合改性聚合物防水卷材是由一定比例的丁苯橡胶、废丁基橡胶、苯乙烯－丁二烯－苯乙烯嵌段共聚物、石油建筑沥青、滑石粉、碳酸钙及一些化学助剂，经混炼、精炼、延压制成非硫化型无胎复合改性聚合物防水卷材。该技术工艺简单、操作简便易行、生产成本低，无环境污染问题。该产品具有延伸度高、强度大、耐低温和高温及防水性能好等特点。与高分子防水卷材胶粘剂配合，可在环境温度下冷施工，施工中无环境污染。

Description

一种防水卷材及其生产方法
1、技术领域
本发明涉及一种防水卷材及其生产方法，特别是涉及一种非硫化型无胎复合改性聚合物防水卷材及其生产方法。
2、技术领域
随着城市高档民用建筑和复杂工业建筑的不断增多，对防水材料质量的要求也越来越高。以往的沥青油毡因其高温流淌、低温脆裂、易老化、寿命短等致命弱点已完全不能满足这一要求。因此，各种新型防水卷材相继出现，例如，三元乙丙橡胶防水卷材、PVC卷材以及废丁基橡胶防水卷材等。其中三元乙丙橡胶及PVC等卷材因其生产工艺较为复杂，且部分原料价格偏高，导致产品成本高，缺乏市场竞争力。废丁基橡胶防水卷材由于原料质量参差不齐，配方较为单一，导致产品在耐低温、柔韧性及抗拉强度等方面存在一定问题，严重影响了产品的防水效果及使用寿命。CN87105084A提出采用再生胶、废丁基橡胶、废纤维、建筑石油沥青及助剂、填料等为原料生产防水卷材，但其耐高、低温性能较差，在温差较大的地区使用时，寿命较短，防水性能需进一步提高。
3、发明内容
针对现有技术的不足，本发明的目的在于提出一种延伸度高、强度大、耐低温和高温及防水性能好的复合改性聚合物防水卷材及生产方法。
本发明防水卷材原料包括丁苯橡胶(SBR)和/或苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、废丁基橡胶、石油建筑沥青和填料，同时还可以含有化学助剂等，以重量份计具体组成为如下：
丁苯橡胶和/或SBS    5-30份
废丁基橡胶    10-50份
建筑石油沥青  5-20份
填料          10-60份
还可以含有化学助剂2-10份，其中，建筑石油沥青通常采用10号建筑石油沥青，化学助剂为包括防老剂、增强剂和软化剂中的一种或几种，防老剂可以选用N-苯基-a-萘胺以及辛基化二苯胺等，增强剂可以选用通用炭黑以及高耐磨炭黑等，软化剂为硬脂酸等，填料包括轻质碳酸钙和/或滑石粉。防水卷材的厚度、幅宽长度可以根据需要确定，一般厚度为0.5～5mm。
本发明防水卷材的生产过程为：将各种原料按需要比例在炼胶机上混炼均匀，辊温为60～70℃，精炼温度为60～70℃，薄通(精炼)10次以上，通常为15～40次，然后在压延机上出型，压延机辊温为90～100℃。
本发明的防水卷材充分利用丁苯橡胶良好的耐低温性和柔韧性、SBS良好的热塑性和弹性以及丁基橡胶良好的耐挠曲性、抗撕裂性、耐老化性，并使用建筑石油沥青对橡胶良好的软化性和分散性，把上述聚合物的各个特性有机的结合起来，使得所生产的防水卷材具有耐高温和低温性能好、延伸性好、抗拉强度高、防水效果好、耐老化、使用寿命长等优点。本发明防水卷材的生产方法具有成本低、工艺简单、操作方便易行、无环境污染。另外，该防水卷材施工简单，与高分子防水卷材胶粘剂配合，可在环境温度下冷施工，无任何环境污染问题，符合环保要求。
4、具体实施方式
下面通过实施例进一步说明本发明实施方案和效果。
实施例1
将10份丁苯橡胶、5份苯乙烯-丁二烯-苯乙烯嵌段共聚物即SBS(岳阳化工厂YH-791)、40份废丁基橡胶、5份10号建筑石油沥青、25份碳酸钙、15份滑石粉先在炼胶机上混炼均匀，辊温为65℃，然后在65℃下薄通20次。再在压延机上出型，压延机辊温为95℃，出型厚度为1.5毫米，幅宽1米。
实施例2
将15份丁苯橡胶、5份SBS、20份废丁基橡胶、5份10号建筑石油沥青、3份化学助剂高耐磨炭黑、2份防老剂萘N-苯基-a-胺、25份碳酸钙、20份滑石粉先在炼胶机上混炼均匀，辊温为60℃，然后在60℃下薄通30次。再在压延机上出型，压延机辊温为100℃，出型厚度为1.2毫米，幅宽1米。
实施例3
将10份丁苯橡胶、35份废丁基橡胶、15份10号建筑石油沥青、3份化学助剂通用炭黑、2份防老剂辛基化二苯胺、25份碳酸钙、45份滑石粉先在炼胶机上混炼均匀，辊温为70℃，然后在70℃下薄通35次。再在压延机上出型，压延机辊温为90℃，出型厚度为1.8毫米，幅宽1米。
实施例4
将10份SBS、35份废丁基橡胶、5份10号建筑石油沥青、3份防老剂萘N-苯基-a-胺、10份碳酸钙、20份滑石粉先在炼胶机上混炼均匀，辊温为65℃，然后在65℃下薄通15次。再在压延机上出型，压延机辊温为95℃，出型厚度为1.5毫米，幅宽1米。
表一  各实施例产品性质
检测项目    实施例1    实施例2     实施例3    实施例4
抗拉强度/MPa    1.38    1.45     1.42    1.39
延伸率/％    253    260     265    257
低温柔性   -30℃ 2h对折无裂纹    -30℃ 2h对折无裂纹    -30℃ 2h对折无裂纹    -30℃ 2h对折无裂纹
耐热度   120℃，5h不起泡不发粘    120℃，5h不起泡不发粘    120℃，5h不起泡不发粘    120℃，5h不起泡不发粘
比较例：本发明防水卷材与同类产品丁基胶防水卷材性质对比分析结果。
  检测项目    同类丁基胶防水卷材    实施例2防水卷材
抗拉强度/MPa    1.0    1.45
延伸率/％    120    260
低温柔性    -20℃ 2h对折无裂纹    -30℃ 2h对折无裂纹
耐热度    100℃，5h不起泡不发粘    120℃，5h不起泡不发粘
从上述性质分析结果比较可以看出，本发明的复合改性聚合物防水卷材对温度的敏感性明显降低，也就是说本发明的复合改性聚合物防水卷材耐高温性能以及耐低温性能显著提高，且抗拉强度及延伸率性能指标远优于对比产品，表明本发明的复合改性聚合物防水卷材防水效果以及使用寿命优于对比产品。

Claims (9)

1、一种防水卷材，含有废丁基橡胶、建筑石油沥青以及填料，其特征在于还含有丁苯橡胶和/或苯乙烯-丁二烯-苯乙烯嵌段共聚物，以重量份计比例如下：
丁苯橡胶和/或苯乙烯-丁二烯-苯乙烯嵌段共聚物     5-30份
废丁基橡胶          10-50份
石油建筑沥青        5-20份
填料                10-60份。
2、按照权利要求1所述的防水卷材，其特征在于含有化学助剂2-10份。
3、按照权利要求1所述的防水卷材，其特征在于所述的填料为轻质碳酸一钙和/或滑石粉。
4、按照权利要求2所述的防水卷材，其特征在于所述的化学助剂为防老剂、增强剂和硬脂酸中的一种或几种。
5、按照权利要求1所述的防水卷材，其特征在于防水卷材的厚度为0.5～5mm。
6、按照权利要求4所述的防水卷材，其特征在于所述的防老剂为N-苯基-a-萘胺或辛基化二苯胺，增强剂为炭黑或高耐磨炭黑。
7、一种权利要求1所述防水卷材的生产方法，其特征在于将丁苯橡胶、废丁基橡胶、苯乙烯-丁二烯-苯乙烯嵌段共聚物、石油建筑沥青、以及填料和化学助剂进行混炼、精炼、压延成型，制得本发明防水卷材。
8、按照权利要求7所述的方法，其特征在于所述的混炼辊温为60～70℃，精炼辊温为60～70℃，压延辊温为90～100℃。
9、按照权利要求7或8所述的方法，其特征在于所述的精炼过程为薄通10次以上。
CNB021326258A 2002-07-17 2002-07-17 一种防水卷材及其生产方法 Expired - Lifetime CN1185321C (zh)