CN102051054B - 一种高分子防水卷材的制备方法 - Google Patents
一种高分子防水卷材的制备方法 Download PDFInfo
- Publication number
- CN102051054B CN102051054B CN 200910066313 CN200910066313A CN102051054B CN 102051054 B CN102051054 B CN 102051054B CN 200910066313 CN200910066313 CN 200910066313 CN 200910066313 A CN200910066313 A CN 200910066313A CN 102051054 B CN102051054 B CN 102051054B
- Authority
- CN
- China
- Prior art keywords
- waterproof sheet
- high polymer
- rubber
- polymer waterproof
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种高分子防水卷材的制备方法，将沥青加热至160-170℃，然后加入橡胶在160-170℃下搅拌50-60分钟，再加入炭黑和防老剂搅拌混合均匀，最后成型处理得到防水卷材。本发明的制备方法过程简单，选择合适的温度和搅拌时间，使得沥青和橡胶的性能在高分子防水卷材中的匀质性和耐热性好，制备时加入炭黑作为补强剂，添加防老剂264能抑制或延缓橡胶的氧化降解从而延长高分子防水卷材的使用寿命，适合在产业上大规模使用。
Description
技术领域
本发明属于建筑防水卷材技术领域，具体涉及一种高分子防水卷材的制备方法。
背景技术
屋面渗漏是建筑工程的通病，要保证防水工程的质量，除了设计施工的因素外，还要选择合适的防水卷材。防水卷材主要应用于建筑屋面防水、地下防水、室内防潮等方面。目前大都是采用沥青作为防水卷材的基础材料，但是目前的防水卷材的制备方法还存在工艺较为复杂，制备过程温度和时间控制不够理想的缺点。
发明内容
本发明的目的在于提供一种工艺简单的高分子防水卷材的制备方法。
本发明采用以下技术方案：一种高分子防水卷材的制备方法，将沥青加热至160-170℃，然后加入橡胶在160-170℃下搅拌50-60分钟，再加入炭黑和防老剂搅拌混合均匀，最后成型处理得到防水卷材；所述沥青、橡胶、炭黑和防老剂的重量份数分别为：70-75份、20-25份、2-3份和1.6-2.5份。
所述防老剂为防老剂264。
本发明的制备方法过程简单，选择合适的温度和搅拌时间，使得沥青和橡胶的性能在高分子防水卷材中的匀质性和耐热性好，制备时加入炭黑作为补强剂，添加防老剂264能抑制或延缓橡胶的氧化降解从而延长高分子防水卷材的使用寿命，适合在产业上大规模使用。
具体实施方式
实施例1：将70份沥青加热至160℃，然后加入25份橡胶在160℃下搅拌60分钟，再加入2份炭黑和2.5份防老剂264搅拌混合均匀，最后送入成型机的原料进口经成型得到防水卷材。
实施例2：将75份沥青加热至165℃，然后加入20份橡胶在165℃下搅拌55分钟，再加入3份炭黑和1.6份防老剂264搅拌混合均匀，最后送入成型机的原料进口经成型得到防水卷材。
实施例3：将73份沥青加热至170℃，然后加入22份橡胶在170℃下搅拌50分钟，再加入2.5份炭黑和2份防老剂264搅拌混合均匀，最后送入成型机的原料进口经成型得到防水卷材。
以上实施例中的份数均为重量份数。
Claims (1)
1.一种高分子防水卷材的制备方法，其特征在于：将沥青加热至160-170℃，然后加入橡胶在160-170℃下搅拌50-60分钟，再加入炭黑和防老剂搅拌混合均匀，最后成型处理得到防水卷材；所述沥青、橡胶、炭黑和防老剂的重量份数分别为：70-75份、20-25份、2-3份和1.6-2.5份；所述防老剂为防老剂264。