CN101818341A - 用于对含镁铝合金进行涂镀的方法 - Google Patents
用于对含镁铝合金进行涂镀的方法 Download PDFInfo
- Publication number
- CN101818341A CN101818341A CN201010119775A CN201010119775A CN101818341A CN 101818341 A CN101818341 A CN 101818341A CN 201010119775 A CN201010119775 A CN 201010119775A CN 201010119775 A CN201010119775 A CN 201010119775A CN 101818341 A CN101818341 A CN 101818341A
- Authority
- CN
- China
- Prior art keywords
- coating
- aluminium alloy
- alloy containing
- containing magnesium
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于对含镁铝合金进行涂镀的方法。本发明的一个优选的应用领域是采用连续浇铸成型的涂镀方法。因此,本发明的任务是,在不含六价铬(Chrome(VI))的条件下对含镁铝合金进行钝化处理。本发明的任务这样实现的,即,在由含镁铝合金构成的金属基板上涂镀一层缓冲层,该缓冲层为三价铬(Chrome(III))钝化涂层,在涂镀之前进行约450℃-约620℃的加热处理。
Description
技术领域
本发明涉及一种用于对含镁铝合金进行涂镀的方法。本发明的一个优选的应用领域是采用连续浇铸成型的涂镀方法。
发明内容
因此,本发明的任务是,在不含六价铬(Chrome(VI))的条件下对含镁铝合金进行钝化处理。
本发明的任务由权利要求1实现,其中,在由含镁铝合金构成的金属基板上涂镀一层缓冲层,该缓冲层为三价铬(Chrome(III))钝化涂层,在涂镀之前进行约450℃-约620℃的加热处理。本发明具有优势的技术方案在从属权利要求中给出。本发明的第一个具有优势的技术方案在于,使钝化涂层在不通电的情况下进行涂镀。本发明的另一个具有优势的技术方案在于,在加热以后和涂镀之前将钝化涂层冷却到室温。这种铝合金的含镁量占至少大约0.5%,并且不多于3%。上述缓冲层的厚度约0.1-约10μm。
Claims (5)
1.一种用于对含镁铝合金进行涂镀的方法,其特征在于,在金属基板上涂镀一层缓冲层,所述缓冲层为三价铬钝化涂层,在涂镀之前进行约450℃-约620℃的加热处理。
2.根据权利要求1所述的方法,其特征在于,使钝化涂层在不通电的情况下进行涂镀。
3.根据权利要求1或2所述的方法,其特征在于,在加热以后和涂镀之前将钝化涂层冷却到室温。
4.根据权利要求1、2或3所述的方法,其特征在于,所述铝合金的含镁量占至少大约0.5%,并且不多于3%。
5.根据权利要求1、2、3或4所述的方法,其特征在于,所述缓冲层的厚度约0.1-约10μm。